The effects of Zn content on the microstxucture and the mechanical and corrosion properties of as-cast low-alloyed Mg-xZn~.2Ca alloys （x = 0.6wt%, 2.0wt%, 2.5wt%, hereafter denoted as 0.6Zn, 2.0Zn, and 2.5Zn alloys, ...The effects of Zn content on the microstxucture and the mechanical and corrosion properties of as-cast low-alloyed Mg-xZn~.2Ca alloys （x = 0.6wt%, 2.0wt%, 2.5wt%, hereafter denoted as 0.6Zn, 2.0Zn, and 2.5Zn alloys, respectively） axe investigated. The results show that the Zn content not only influences grain refinement but also induces different phase precipitation behaviors. The as-cast microstxucture of the 0.6Zn alloy is composed of ct-Mg, Mg2Ca, and Ca2Mg6Zn3 phases, whereas 2.0Zn and 2.5Zn alloys only contain ct-Mg and Ca2Mg6Zn3 phases, as revealed by X-ray diffraction （XRD） and txonsmission electron microscopy （TEM） analyses. Moreover, with in- creasing Zn content, both the ultimate tensile strength （UTS） and the elongation to fracture first increase and then decrease. Among the three investigated alloys, the largest UTS （178 MPa） and the highest elongation to fracture （6.5%） are obtained for the 2.0Zn alloy. In addition, the corrosion rate increases with increasing Zn content. This paper provides on updated investigation of the alloy composi- tion-microstxucture-property relationships of different Zn-containing Mg-Zn-Ca alloys.展开更多
文摘薄膜 Cu2S-CdS 太阳电池的电性能参数与 P 型 Cu2S 层接触的栅极关系极大,电池的稳定性在某种程度上也取决于收集栅极的材料。Delaware 和 Stuttgart 大学[1,2]为了改善电池的稳定性,曾在 Cu2S 层蒸镀0.1nm 数量级的 Au,然后再粘网状 Cu 栅极,使电池性能有了改进。目前多采用 Cu 栅或者 Au 栅。
基金supported by the National Natural Science Foundation of China(No.51671017)Fundamental Research Funds for the Central Universities(No.FRF-GF-17-B3)+1 种基金Beijing Laboratory of Metallic Materials and Processing for Modern Transportation,the Opening Research Fund of State Key Laboratory for Advanced Metals and Materials(Nos.2016Z-11,2017Z-08)State's Key Project of Research and Development Plan(No.2016YFB0300801)
文摘The effects of Zn content on the microstxucture and the mechanical and corrosion properties of as-cast low-alloyed Mg-xZn~.2Ca alloys （x = 0.6wt%, 2.0wt%, 2.5wt%, hereafter denoted as 0.6Zn, 2.0Zn, and 2.5Zn alloys, respectively） axe investigated. The results show that the Zn content not only influences grain refinement but also induces different phase precipitation behaviors. The as-cast microstxucture of the 0.6Zn alloy is composed of ct-Mg, Mg2Ca, and Ca2Mg6Zn3 phases, whereas 2.0Zn and 2.5Zn alloys only contain ct-Mg and Ca2Mg6Zn3 phases, as revealed by X-ray diffraction （XRD） and txonsmission electron microscopy （TEM） analyses. Moreover, with in- creasing Zn content, both the ultimate tensile strength （UTS） and the elongation to fracture first increase and then decrease. Among the three investigated alloys, the largest UTS （178 MPa） and the highest elongation to fracture （6.5%） are obtained for the 2.0Zn alloy. In addition, the corrosion rate increases with increasing Zn content. This paper provides on updated investigation of the alloy composi- tion-microstxucture-property relationships of different Zn-containing Mg-Zn-Ca alloys.