Polyurethane modified organic silicone was successfully prepared from hydroxyl-terminated polyether modified silicone,toluene-2,4-diisocyanate( TDI), and NaHSO3. The chemical structure of the polyurethane modified org...Polyurethane modified organic silicone was successfully prepared from hydroxyl-terminated polyether modified silicone,toluene-2,4-diisocyanate( TDI), and NaHSO3. The chemical structure of the polyurethane modified organic silicone was characterized by FT-IR and1H-NMR. The polymer film on the cotton surface was investigated by scanning electron microscopy( SEM) and the results showed that a thin polymer film was successfully formed. The FT-IR of treated cotton fabrics indicated that hydroxyl( OH) of cellulose fiber and isocyanate group( NCO)of the polyurethane modified organic silicone has formed covalent cross-linking. X-ray diffraction( XRD) analysis revealed that the crystalline region of treated cotton fabrics wasn't changed. The wet rubbing fastness of treated cotton fabrics was increased by approximately rating 1 on average. There was little change of DE values for the polyurethane modified organic silicone. The softness was improved significantly.展开更多
文摘Polyurethane modified organic silicone was successfully prepared from hydroxyl-terminated polyether modified silicone,toluene-2,4-diisocyanate( TDI), and NaHSO3. The chemical structure of the polyurethane modified organic silicone was characterized by FT-IR and1H-NMR. The polymer film on the cotton surface was investigated by scanning electron microscopy( SEM) and the results showed that a thin polymer film was successfully formed. The FT-IR of treated cotton fabrics indicated that hydroxyl( OH) of cellulose fiber and isocyanate group( NCO)of the polyurethane modified organic silicone has formed covalent cross-linking. X-ray diffraction( XRD) analysis revealed that the crystalline region of treated cotton fabrics wasn't changed. The wet rubbing fastness of treated cotton fabrics was increased by approximately rating 1 on average. There was little change of DE values for the polyurethane modified organic silicone. The softness was improved significantly.