High-density polyethylene/carbon black foaming conductive composites were prepared from acetylene black（ACEY） and super conductive carbon black（HG-1P） as conductive filler, low-density polyethylene（LDPE） as the ...High-density polyethylene/carbon black foaming conductive composites were prepared from acetylene black（ACEY） and super conductive carbon black（HG-1P） as conductive filler, low-density polyethylene（LDPE） as the second component, ethylene-vinyl acetate（EVA） and ethylene propylene rubber（EPR） as the third component, azobisformamide（AC） as foamer, and dicumyl peroxide（DCP） as cross-linker. The structure and resistivity-temperature behavior of high-density polyethylene（HDPE）/CB foaming conductive composites were investigated. Influences of carbon black, LDPE, EVA, EPR, AC, and DCP on the foaming performance and resistivity-temperature behavior of HDPE/CB foaming conductive composites were also studied. The results reveal that HDPE/CB foaming conductive composite exhibits better switching characteristic; ACET-filled HDPE foaming conductive composite displays better positive temperature coefficient（PYC） effect; whereas super conductive carbon black（HG-1P）-filled HDPE foaming conductive composite shows better negative temperature coefficient（NTC） effect.展开更多
The DC electrical resistivity-temperature characteristic is an important property for insulating materials to operate at a high stress level.In order to improve the DC electrical resistivity at elevated temperature in...The DC electrical resistivity-temperature characteristic is an important property for insulating materials to operate at a high stress level.In order to improve the DC electrical resistivity at elevated temperature in a targeted way,a positive temperature coefficient(PTC)material(Ba Ti O3-based compound(BT60))was selected as the filler in this paper,whose electrical resistivity has a PTC effect when the temperature exceeds its Curie temperature.The BT60 was treated with hydrogen peroxide and(3-Aminopropyl)triethoxysilane.Epoxy composites with different loadings of BT60 fillers(0 wt%,0.5 wt%,and 2 wt%of epoxy)were prepared,denoted as EP-0,EP-0.5,and EP-2.It was shown that BT60 was able to maintain the DC breakdown strength when its loading was less than 2 wt%of epoxy.As the temperature exceeds 60°C,BT60 will compensate for the negative temperature coefficient effect of epoxy resin to some extent.The electrical resistivity of EP-2 was improved by 55%compared with that of neat epoxy at 90°C.It was found that the potential barrier at the grain boundary of BT60 and the deep traps in the interface between BT60 and the epoxy resin hinder the migration of carriers and thus increase the electrical resistivity of epoxy composite.展开更多
Vinylester （bismethacryloxy derivative with glass-carbon hybrid fibers （CF-GF） weight fraction of a bisphenol-A type EP resin, VE） composites of 50%, were prepared by the compress molding method. The distribution ...Vinylester （bismethacryloxy derivative with glass-carbon hybrid fibers （CF-GF） weight fraction of a bisphenol-A type EP resin, VE） composites of 50%, were prepared by the compress molding method. The distribution of carbon fiber in the hybrids was observed by stereomicroscope. The electrical resistance behavior of the composites filled with different carbon fiber （CF） weight contents （0.5% to 20%） was studied. The experimental results show that the electrical resistance behaviors of CF-GF/VE composites are different with those of CF/VE composites because carbon fibers＇ conducting networks are broken by the glass fibers in the CF-GF/VE composites. The carbon fibers distribute uniformly in the networks of glass fibers （GF） like single silk and form the semi-continuous conducting networks. Composite filled with GF-CF hybrid has a higher percolation threshold than that filled with pure CF. At that time, the resistivity of CF-GF/VE composites varies little with the temperature increasing. The temperature coefficient of resistivity in GF-CF/VE composite is less than 317 ppm and the variation of the resistivity after ten thermal cycles from 20℃ to 240 ℃is less than 1.96%.展开更多
文摘High-density polyethylene/carbon black foaming conductive composites were prepared from acetylene black（ACEY） and super conductive carbon black（HG-1P） as conductive filler, low-density polyethylene（LDPE） as the second component, ethylene-vinyl acetate（EVA） and ethylene propylene rubber（EPR） as the third component, azobisformamide（AC） as foamer, and dicumyl peroxide（DCP） as cross-linker. The structure and resistivity-temperature behavior of high-density polyethylene（HDPE）/CB foaming conductive composites were investigated. Influences of carbon black, LDPE, EVA, EPR, AC, and DCP on the foaming performance and resistivity-temperature behavior of HDPE/CB foaming conductive composites were also studied. The results reveal that HDPE/CB foaming conductive composite exhibits better switching characteristic; ACET-filled HDPE foaming conductive composite displays better positive temperature coefficient（PYC） effect; whereas super conductive carbon black（HG-1P）-filled HDPE foaming conductive composite shows better negative temperature coefficient（NTC） effect.
基金support from National Natural Science Foundation of China(No.51977186)the China Postdoctoral Science Foundation(No.2019M650029)+3 种基金the Young Elite Scientists Sponsorship Program by CAST(No.2018QNRC001)the National Key R&D Program of China(No.2017YFB0902704)the State Key Development Program of Basic Research of China(973 Program)(No.2014CB239501)the Science and Technology Project of the State Grid Corp.of China(No.52110418001Y).
文摘The DC electrical resistivity-temperature characteristic is an important property for insulating materials to operate at a high stress level.In order to improve the DC electrical resistivity at elevated temperature in a targeted way,a positive temperature coefficient(PTC)material(Ba Ti O3-based compound(BT60))was selected as the filler in this paper,whose electrical resistivity has a PTC effect when the temperature exceeds its Curie temperature.The BT60 was treated with hydrogen peroxide and(3-Aminopropyl)triethoxysilane.Epoxy composites with different loadings of BT60 fillers(0 wt%,0.5 wt%,and 2 wt%of epoxy)were prepared,denoted as EP-0,EP-0.5,and EP-2.It was shown that BT60 was able to maintain the DC breakdown strength when its loading was less than 2 wt%of epoxy.As the temperature exceeds 60°C,BT60 will compensate for the negative temperature coefficient effect of epoxy resin to some extent.The electrical resistivity of EP-2 was improved by 55%compared with that of neat epoxy at 90°C.It was found that the potential barrier at the grain boundary of BT60 and the deep traps in the interface between BT60 and the epoxy resin hinder the migration of carriers and thus increase the electrical resistivity of epoxy composite.
基金Funded by the Natural Science Foundation of Hubei Province (No.2007ABA028)
文摘Vinylester （bismethacryloxy derivative with glass-carbon hybrid fibers （CF-GF） weight fraction of a bisphenol-A type EP resin, VE） composites of 50%, were prepared by the compress molding method. The distribution of carbon fiber in the hybrids was observed by stereomicroscope. The electrical resistance behavior of the composites filled with different carbon fiber （CF） weight contents （0.5% to 20%） was studied. The experimental results show that the electrical resistance behaviors of CF-GF/VE composites are different with those of CF/VE composites because carbon fibers＇ conducting networks are broken by the glass fibers in the CF-GF/VE composites. The carbon fibers distribute uniformly in the networks of glass fibers （GF） like single silk and form the semi-continuous conducting networks. Composite filled with GF-CF hybrid has a higher percolation threshold than that filled with pure CF. At that time, the resistivity of CF-GF/VE composites varies little with the temperature increasing. The temperature coefficient of resistivity in GF-CF/VE composite is less than 317 ppm and the variation of the resistivity after ten thermal cycles from 20℃ to 240 ℃is less than 1.96%.