Single crystals of RSeTe2 （R =La, Ce, Pr, Nd） are synthesized using LiC1/RbCI flux. Transport and magnetic properties in the directions parallel and perpendicular to the a-c plane are investigated. We find that the ...Single crystals of RSeTe2 （R =La, Ce, Pr, Nd） are synthesized using LiC1/RbCI flux. Transport and magnetic properties in the directions parallel and perpendicular to the a-c plane are investigated. We find that the resistivity anisotropy P⊥/P∥ lies in the range 486-615 for different compounds at 2K, indicating the highly two-dimensional character. In both the orientations, the charge-density-wave transitions start near Tcow = 284（3）K, 316（3）K, 359（3）K for NdSeTe2, PrSeTe2, CeSeTe2, respectively, with a considerable increase in dc resistivity. While for LaSeTe2, no obvious resistivity anomaly is observed up to 380K. The value of TCDW increases monotonically with the increasing lattice parameters. Below TCDW, slight anomalies can be observed in NdSeTe2, PrSeTe2 and CeSeTe2 with onset temperature at 193（3）K, 161（3）K, 108（3）K, respectively, decreasing as lattice parameters increase. Magnetic susceptibility measurements show that the valence state of rare earth ions are trivalenee in these compounds. Antiferromagnetie-type magnetic order is formed in CeSeTe2 at 2.1 K, while no magnetic transition is observed in PrSeTe2 and NdSeTe2 down to 1.8 K.展开更多
基金Supported by the National Basic Research Program of China under Grant No 2015CB921303the Strategic Priority Research Program(B) of Chinese Academy of Sciences under Grant No XDB07020100
文摘Single crystals of RSeTe2 （R =La, Ce, Pr, Nd） are synthesized using LiC1/RbCI flux. Transport and magnetic properties in the directions parallel and perpendicular to the a-c plane are investigated. We find that the resistivity anisotropy P⊥/P∥ lies in the range 486-615 for different compounds at 2K, indicating the highly two-dimensional character. In both the orientations, the charge-density-wave transitions start near Tcow = 284（3）K, 316（3）K, 359（3）K for NdSeTe2, PrSeTe2, CeSeTe2, respectively, with a considerable increase in dc resistivity. While for LaSeTe2, no obvious resistivity anomaly is observed up to 380K. The value of TCDW increases monotonically with the increasing lattice parameters. Below TCDW, slight anomalies can be observed in NdSeTe2, PrSeTe2 and CeSeTe2 with onset temperature at 193（3）K, 161（3）K, 108（3）K, respectively, decreasing as lattice parameters increase. Magnetic susceptibility measurements show that the valence state of rare earth ions are trivalenee in these compounds. Antiferromagnetie-type magnetic order is formed in CeSeTe2 at 2.1 K, while no magnetic transition is observed in PrSeTe2 and NdSeTe2 down to 1.8 K.