The compound ingots of Pr0.15TbxDy0.85-xFe2 (x=0 to 0.85) were prepared by arc melting in a water Cu boat using arc furnace under a purified Ar atmosphere. Appropriate annealing (850℃, 100 h) can obtain single Laves ...The compound ingots of Pr0.15TbxDy0.85-xFe2 (x=0 to 0.85) were prepared by arc melting in a water Cu boat using arc furnace under a purified Ar atmosphere. Appropriate annealing (850℃, 100 h) can obtain single Laves phase compound. The magnetostriction for these systems will rise obviously when partially substituted Tb or Dy by Pr.展开更多
Effect of Li and Ti additions on Lα(AI)+Mg2Si pseudobinary eutectic reaction in ternary Al-Mg-Si system has been investigated by thermoanalysis, directional solidification and metallographic techniques in this study....Effect of Li and Ti additions on Lα(AI)+Mg2Si pseudobinary eutectic reaction in ternary Al-Mg-Si system has been investigated by thermoanalysis, directional solidification and metallographic techniques in this study. It has been found that Li addition causes decreasing of the volume fraction of Mg2Si, while a little amount of Ti causes to increasing, which is of a great importance to the adjustment of phase constitution and alloy properties. Doping components have little influence on the eutectic temperature.展开更多
基金the Natural Science Foundation of Hebei Province 596028 and the National NaturalScience Foundation of China No.59871062.
文摘The compound ingots of Pr0.15TbxDy0.85-xFe2 (x=0 to 0.85) were prepared by arc melting in a water Cu boat using arc furnace under a purified Ar atmosphere. Appropriate annealing (850℃, 100 h) can obtain single Laves phase compound. The magnetostriction for these systems will rise obviously when partially substituted Tb or Dy by Pr.
文摘Effect of Li and Ti additions on Lα(AI)+Mg2Si pseudobinary eutectic reaction in ternary Al-Mg-Si system has been investigated by thermoanalysis, directional solidification and metallographic techniques in this study. It has been found that Li addition causes decreasing of the volume fraction of Mg2Si, while a little amount of Ti causes to increasing, which is of a great importance to the adjustment of phase constitution and alloy properties. Doping components have little influence on the eutectic temperature.