This study provides a detailed report on the synthesis of spherical activated carbon with mesoporous structure using a soluble low molecular weight phenolic resol precursor through an ammonium alginate assisted sol–g...This study provides a detailed report on the synthesis of spherical activated carbon with mesoporous structure using a soluble low molecular weight phenolic resol precursor through an ammonium alginate assisted sol–gel method. The effects of calcinating temperature and the addition of CaCO_3 as a pore-enlarging agent on texture structure and catalytic performance in isobutane dehydrogenation to isobutene were investigated. Characterization of N_2 sorption,mechanical strength tests,and optical photographs confirmed that the obtained carbon materials had high mechanical strength,a good degree of sphericity,and a large surface area. Introducing CaCO_3 as a pore-enlarging agent during the preparation process promoted the formation of a mesoporous structure of carbon spheres and evidently increased the surface area and oxygen content,which can improve isobutane conversion and isobutene selectivity of these carbon spheres. The conversion of isobutane reached up to 28% for this spherical activated carbon,and the selectivity of isobutene reached up to 96%. Isobutane conversion increased with an increase in calcination temperature due to an increase in the oxygen content,whereas the selectivity of isobutene decreased due to the slight decrease in the specific surface area.展开更多
A highly ordered porous alumina template with pores of 45 nm in diameter was synthesized by a two-step electrochemical anodizing process. The influence of pore-enlargement treatment on the porous structure and tribolo...A highly ordered porous alumina template with pores of 45 nm in diameter was synthesized by a two-step electrochemical anodizing process. The influence of pore-enlargement treatment on the porous structure and tribological properties of the film was investigated, and ultrasonic impregnation technology was applied on it to form self-lubricating surface. The structure of the self-lubricating film and its tribological properties were investigated in detail. It can be concluded that the optimum time of pore-enlargement treatment is 20 min. The diameter of the pores and the surface porosity of the film are about 70 nm and 30%, respectively, while the film maintains the property of its high hardness. Under the same friction condition, the frictional coefficient of the self-lubricating film is 0. 18, much lower than that of the anodic aluminum oxide template, which is 0.52. In comparison with the lubricating surface of non-porous dense anodic aluminum oxide template, the lubricating surface fabricated by the ultrasonic impregnation method on the porous anodic aluminum oxide template keeps longer period with low friction coefficient. SEM examination shows that some C60 particles have been embedded in ultrasonic impregnation technology. the nanoholes of the anodic aluminum oxide template by the展开更多
基金supported by the Natural Science Foundation of Tianjin, China (no. 15JCYBJC20900)
文摘This study provides a detailed report on the synthesis of spherical activated carbon with mesoporous structure using a soluble low molecular weight phenolic resol precursor through an ammonium alginate assisted sol–gel method. The effects of calcinating temperature and the addition of CaCO_3 as a pore-enlarging agent on texture structure and catalytic performance in isobutane dehydrogenation to isobutene were investigated. Characterization of N_2 sorption,mechanical strength tests,and optical photographs confirmed that the obtained carbon materials had high mechanical strength,a good degree of sphericity,and a large surface area. Introducing CaCO_3 as a pore-enlarging agent during the preparation process promoted the formation of a mesoporous structure of carbon spheres and evidently increased the surface area and oxygen content,which can improve isobutane conversion and isobutene selectivity of these carbon spheres. The conversion of isobutane reached up to 28% for this spherical activated carbon,and the selectivity of isobutene reached up to 96%. Isobutane conversion increased with an increase in calcination temperature due to an increase in the oxygen content,whereas the selectivity of isobutene decreased due to the slight decrease in the specific surface area.
基金Project(2007CB607605) supported by the National Basic Research Program of China
文摘A highly ordered porous alumina template with pores of 45 nm in diameter was synthesized by a two-step electrochemical anodizing process. The influence of pore-enlargement treatment on the porous structure and tribological properties of the film was investigated, and ultrasonic impregnation technology was applied on it to form self-lubricating surface. The structure of the self-lubricating film and its tribological properties were investigated in detail. It can be concluded that the optimum time of pore-enlargement treatment is 20 min. The diameter of the pores and the surface porosity of the film are about 70 nm and 30%, respectively, while the film maintains the property of its high hardness. Under the same friction condition, the frictional coefficient of the self-lubricating film is 0. 18, much lower than that of the anodic aluminum oxide template, which is 0.52. In comparison with the lubricating surface of non-porous dense anodic aluminum oxide template, the lubricating surface fabricated by the ultrasonic impregnation method on the porous anodic aluminum oxide template keeps longer period with low friction coefficient. SEM examination shows that some C60 particles have been embedded in ultrasonic impregnation technology. the nanoholes of the anodic aluminum oxide template by the