In this work,a sponge-like polysulfonamide(PSA)/SiO_2 composite membrane is unprecedentedly prepared by the phase inversion method,and successfully demonstrated as a novel separator of lithium-ion batteries(LIBs).Comp...In this work,a sponge-like polysulfonamide(PSA)/SiO_2 composite membrane is unprecedentedly prepared by the phase inversion method,and successfully demonstrated as a novel separator of lithium-ion batteries(LIBs).Compared to the commercial polypropylene(PP) separator,the sponge-like PSA/SiO_2 composite possesses better physical and electrochemical properties,such as higher porosity,ionic conductivity,thermal stability and flame retarding ability.The LiCoO_2/Li half-cells using the sponge-like composite separator demonstrate superior rate capability and cyclability over those using the commercial PP separator.Moreover,the sponge-like composite separator can ensure the normal operation of LiCoO_2/Li half-cell at an extremely high temperature of 90 °C,while the commercial PP separator cannot.All these encouraging results suggest that this phase inversion based sponge-like PSA/SiO_2 composite separator is really a promising separator for high performance LIBs.展开更多
Polysulfonamide(PSA)was synthesized at room temperature,the polymerization based on terephthaloyl chloride and 3,3’-diaminodiphenylsulfone in the common solvent N,N-Dimethyl-acetamide(DMAc).Polysulfonamide/titanium o...Polysulfonamide(PSA)was synthesized at room temperature,the polymerization based on terephthaloyl chloride and 3,3’-diaminodiphenylsulfone in the common solvent N,N-Dimethyl-acetamide(DMAc).Polysulfonamide/titanium oxide nanocomposites were prepared by sol-gel method.Tetrabutyl titanate(TBT)was added into the polysulfonamide solution,at the same time,some water was mixed to make the TBT hydrolyze.In the process,hydrochloric acid was used to catalyze the reaction.The polysulfonamide chemistry structure was characterized by FT-IR spectrum.Atomic force microscopy(AFM)was employed to observe the microstructure of the composite film.The thermal property was investigated by TGA.The results show that we have succeeded to synthesize the polysulfonamide,TiO2 particles were well distributed in the composite film and average size was about 20 nm on average,the heat-resistance of nanocomposite was batter than the pure polysulfonamide.展开更多
基金Supported by the funding from "135" Projects Fund of CAS-QIBEBT Director Innovation FoundationThink-Tank Mutual Fund of Qingdao Energy Storage Industry Scientific Research+3 种基金Qingdao Key Lab of Solar Energy Utilization and Energy Storage Technologythe Strategic Priority Research Program of the Chinese Academy of Sciences(XDA09010105)National Natural Science Foundation of China(51502319)Shandong Provincial Natural Science Foundation(ZR2016BQ18)
文摘In this work,a sponge-like polysulfonamide(PSA)/SiO_2 composite membrane is unprecedentedly prepared by the phase inversion method,and successfully demonstrated as a novel separator of lithium-ion batteries(LIBs).Compared to the commercial polypropylene(PP) separator,the sponge-like PSA/SiO_2 composite possesses better physical and electrochemical properties,such as higher porosity,ionic conductivity,thermal stability and flame retarding ability.The LiCoO_2/Li half-cells using the sponge-like composite separator demonstrate superior rate capability and cyclability over those using the commercial PP separator.Moreover,the sponge-like composite separator can ensure the normal operation of LiCoO_2/Li half-cell at an extremely high temperature of 90 °C,while the commercial PP separator cannot.All these encouraging results suggest that this phase inversion based sponge-like PSA/SiO_2 composite separator is really a promising separator for high performance LIBs.
文摘Polysulfonamide(PSA)was synthesized at room temperature,the polymerization based on terephthaloyl chloride and 3,3’-diaminodiphenylsulfone in the common solvent N,N-Dimethyl-acetamide(DMAc).Polysulfonamide/titanium oxide nanocomposites were prepared by sol-gel method.Tetrabutyl titanate(TBT)was added into the polysulfonamide solution,at the same time,some water was mixed to make the TBT hydrolyze.In the process,hydrochloric acid was used to catalyze the reaction.The polysulfonamide chemistry structure was characterized by FT-IR spectrum.Atomic force microscopy(AFM)was employed to observe the microstructure of the composite film.The thermal property was investigated by TGA.The results show that we have succeeded to synthesize the polysulfonamide,TiO2 particles were well distributed in the composite film and average size was about 20 nm on average,the heat-resistance of nanocomposite was batter than the pure polysulfonamide.