Surface of TiO2 nanoparticles was modified with the in situ chemical oxidative polymerization of aniline. Polyaniline modified TiO2 nanoparticles （PANI-TiO2） were characterized with the FT-IR, XRD, SEM and TEM techn...Surface of TiO2 nanoparticles was modified with the in situ chemical oxidative polymerization of aniline. Polyaniline modified TiO2 nanoparticles （PANI-TiO2） were characterized with the FT-IR, XRD, SEM and TEM techniques. Results confirmed that PANI was grafted successfully on the surface of TiO2 nanoparticles, therefore agglomeration of nanoparticles decreased dramatically. Polyvinyl chloride nanocomposites filled with 1 wt%-5 wt% of PANI-TiO2 and TiO2 nanoparticles were prepared via the solution blending method. PVC nanocomposites were analyzed with FT-IR, XRD, SEM, TG/DTA, DSC and tensile test techniques. Effect of PANI as surface modifier of nanoparticles was discussed according to the final properties of PVC nanocomposites. Results demonstrated that deposition of PANI on the surface of TiO2 nanoparticles improved the interfacial adhesion between the constituents of nanocomposites, which resulted in better dispersion of nanoparticles in the PVC matrix. Also PVC/PANI-TiO2 nanocomposites showed higher thennal resistance, tensile strength and Young＇s modulus compared to those of unfilled PVC and PVC/TiO2 nanocomposites.展开更多
Polyaniline （PAn） sensitized nanocrystalline TiO2 composites （TiO2/PAn） were successfully prepared and used as an efficient photocatalyst for the degradation of dye methylene blue （MB）. The results showed that P...Polyaniline （PAn） sensitized nanocrystalline TiO2 composites （TiO2/PAn） were successfully prepared and used as an efficient photocatalyst for the degradation of dye methylene blue （MB）. The results showed that PAn was able to sensitize TiO2 efficiently and the composite photocatalyst could be activated by absorbing both the ultraviolet and visible light （λ： 190 ～ 800 nm）, whereas pure TiO2 absorbed ultraviolet light only （λ 〈 380 nm）. Under the irradiation of natural light, MB could be degraded more efficiently on the TiO2/PAn composites than on the TiO2 Furthermore, it could be easily separated from the solution by simple sedimentation.展开更多
The p-NiO/n-TiO2/polyaniline composites were synthesized via in situ polymerization of aniline. The structure and morphology of the composites were characterized by means of X-ray diffraction（XRD）, scanning electron...The p-NiO/n-TiO2/polyaniline composites were synthesized via in situ polymerization of aniline. The structure and morphology of the composites were characterized by means of X-ray diffraction（XRD）, scanning electron microscopy（SEM）, Fourier transform infrared spectroscopy（FTIR） and UV-Vis absorption spectroscopy. It was found that the p-n junction p-NiO/n-TiO2 particles were trapped in the polyaniline molecular matrix and the polyaniline was deposited on the surface of the particles to form a kind of flower cluster morphologies. The electrochemical behavior of the polyaniline composites was investigated. The electrochemical reactivity of the polyaniline was influenced by the p-NiO/n-TiO2 particles due to the effect of electron-hole pairs in these p-n junction particles. The reversibility of redox process and current intensity of the polyaniline composites with the changing of potential scan rate were also discussed.展开更多
Polyaniline （PANI） composite nanotubes （90-130 nm in diameter） containing titanium dioxide （TiO2） nanoparticles （about 10 nm in diameter） were synthesized through a self-assembly process in the presence of a-n...Polyaniline （PANI） composite nanotubes （90-130 nm in diameter） containing titanium dioxide （TiO2） nanoparticles （about 10 nm in diameter） were synthesized through a self-assembly process in the presence of a-naphthalenesulfonic acid （a-NSA） as the dopant. It was found that PANI-TiO2 composites and PANI nanotubes both behaved with significant photocatalytic activities towards AZO dyes, during 2 h photocatalytic processes under natural light, the degradation ratio was 94.2% and 97.2% respectively （methyl orange and orange II）. The morphology of such products was characterized by SEM. The specific surface area of such composite nanotubes was 14.7 m2/g compared to normal polyaniline which was 0.27 m2/g. IR and X-ray diffraction characterizations showed that the chemical chain of the composite nanotubes was identical to that of the doped PANI. It may provide a new way for photodegradation of organic contaminants by using conjugated polymer with dimensional structure.展开更多
TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to es...TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to estimate activity of catalysts and determine the kinetics. And the effects of parameters including the initial concentration of AY, light intensity and TiO2 content in catalysts were examined. The results indicate that TAs has a higher efficiency in decomposition of AY than P25, pure TiO2 particles as well as the mixture of TiO2 powder and active carbon. The photocatalytic degradation rate is found to follow the pseudo-first order kinetics with respect to the AY concentration. The new kinetic model fairly resembles the classic Langmuir-Hinshelwood equation, and the rate constant is proportional to the square root of the light intensity in a wide range. However, its absorption performance depends on the surface areas of catalysts. The model fits quite well with the experimental data and elucidates phenomena about the effects of the TiO2 content in TAs on the degradation rate.展开更多
We report the construction of a graphene/tourmaline/TiO2(G/T/TiO2)composite system with enhanced charge‐carrier separation,and therefore enhanced photocatalytic properties,based on tailoring the surface‐charged stat...We report the construction of a graphene/tourmaline/TiO2(G/T/TiO2)composite system with enhanced charge‐carrier separation,and therefore enhanced photocatalytic properties,based on tailoring the surface‐charged state of graphene and/or by introducing an external electric field arising from tourmaline.A simple two‐step hydrothermal method was used to synthesize G/T/TiO2composites and poly(diallyldimethylammonium chloride)‐G/T/TiO2composites.In the photocatalytic degradation of2‐propanol(IPA),the catalytic activity of the composite containing negatively charged graphene was higher than of the composite containing positively charged graphene.The highest acetone evolution rate(223?mol/h)was achieved using the ternary composite with the optimum composition,i.e.,G0.5/T5/TiO2(0.5wt%graphene and5wt%tourmaline).The involvement of tourmaline and graphene in the composite is believed to facilitate the separation and transportation of electrons and holes photogenerated in TiO2.This synergetic effect could account for the enhanced photocatalytic activity of the G/T/TiO2composite.A mechanistic study indicated that O2??radicals and holes were the main reactive oxygen species in photocatalytic degradation of IPA.展开更多
Modern communication technologies put forward higher requirements for electromagnetic wave(EMW)absorption materials.Metal-organic framework(MOF)derivatives have been widely concerned with its diverse advantages.To bre...Modern communication technologies put forward higher requirements for electromagnetic wave(EMW)absorption materials.Metal-organic framework(MOF)derivatives have been widely concerned with its diverse advantages.To break the mindset of magneticderivative design,and make up the shortage of monometallic non-magnetic derivatives,we first try non-magnetic bimetallic MOFs derivatives to achieve efficient EMW absorption.The porous carbon-wrapped TiO2/ZrTiO4 composites derived from PCN-415(TiZr-MOFs)are qualified with a minimum reflection loss of−67.8 dB(2.16 mm,13.0 GHz),and a maximum effective absorption bandwidth of 5.9 GHz(2.70 mm).Through in-depth discussions,the synergy of enhanced interfacial polarization and other attenuation mechanisms in the composites is revealed.Therefore,this work confirms the huge potentials of nonmagnetic bimetallic MOFs derivatives in EMW absorption applications.展开更多
A nanoheterojunction composite photocatalyst Bi2O3/TiO2 working under visible-light （λ≥ 420 nm） was prepared by combining two semiconductors Bi2O3 and TiO2 varying the Bi2O3/TiO2 molar ratio. Maleic acid was emplo...A nanoheterojunction composite photocatalyst Bi2O3/TiO2 working under visible-light （λ≥ 420 nm） was prepared by combining two semiconductors Bi2O3 and TiO2 varying the Bi2O3/TiO2 molar ratio. Maleic acid was employed as an organic binder to unite Bi2O3 and TiO2 nanoparticles. The SEM, TEM, XRD and diffuse reflectance spectra were utilized to characterize the prepared Bi2O3/TiO2 nanoheterojunction. The nanocomposite exhibited unusual high photocatalytic activity in decomposing 2-propanol in gas phase and phenol in aqueous phase and, evolution of CO2 under visible light irradiation while the end members exhibited low photocatalytic activity. The composite was optimized to 5 mol% Bi2O3/TiO2. The remarkable high photocatalytic efficiency originates from the unique relative energy band position of Bi2O3 and TiO2 as well as the absorption of visible light by Bi2O3.展开更多
TiO2 filled polytetrafluoroethylene (PTFE) composite were fabricated for microwave circuit applications. PTFE/TiO2 composites were prepared by cold pressing and hot treating. The particle size of TiO2 varied from 5 μ...TiO2 filled polytetrafluoroethylene (PTFE) composite were fabricated for microwave circuit applications. PTFE/TiO2 composites were prepared by cold pressing and hot treating. The particle size of TiO2 varied from 5 μm to 11 μm.TiO2 powders with different sizes were prepared by the solid state ceramic route. The effects of TiO2 particle size on the microstructure, density, moisture absorption, thermal conductivity and microwave dielectric properties of PTFE/TiO2 composites were investigated. The density showed an increasing trend as the TiO2 particle size increased, while the dielectric loss (tanδ) and moisture absorption decreased with the increase of TiO2 particle size. The dielectric constant (εr) and thermal conductivity (λ) decreased up to D50 = 6.5 μm and then sharply increased. Good properties with values of εr = 6.8, tanδ = 0.0012 and λ = 0.533 W?m?1?K?1 were obtained in PTFE/TiO2 composites when the particle size of TiO2 was 11 μm.展开更多
In the present work, composites of poly (methyl methacrylate)/titanium oxide nanoparticles (100/0, 97.5/2.5, 95/5, 92.5/7.5, 90/10 and 0/100 wt/wt%)were prepared to be used as bioequivalent materials according to thei...In the present work, composites of poly (methyl methacrylate)/titanium oxide nanoparticles (100/0, 97.5/2.5, 95/5, 92.5/7.5, 90/10 and 0/100 wt/wt%)were prepared to be used as bioequivalent materials according to their importance broad practical and medical applications. Thermal properties as well as X-ray diffraction analyses were employed to characterize the structure properties of such composite. The obtained results showed variations in the glass transition temperature (Tg), the melting temperature (Tm), shape and area of thermal peaks which were attributed to the different degrees of crystallinity and the existence of interactions between PMMA and TiO2 nanoparticle molecules. The XRD patterns showed sharpening of peaks at different concentrations of nano-TiO2 powder with PMMA. This indicated changes in the crystallinity/amorphosity ratio, and also suggested that the miscibility between the amorphous components of homo- polymers PMMA and nano-TiO2 powder is possible.The results showed that nano-TiO2 powder mix with PMMA can improve the thermal stability of the homo-polymer under investigation, lead- ing to interesting technological applications.展开更多
We report a facile method for the fabrication of TiO2 nanofiber-nanoparticle composite （FP） via. simulta- neous electrospraying and electrospinning for dye-sensitized solar cell （DSC） applications. The loading of ...We report a facile method for the fabrication of TiO2 nanofiber-nanoparticle composite （FP） via. simulta- neous electrospraying and electrospinning for dye-sensitized solar cell （DSC） applications. The loading of nanoparticles on the fibers is controlled by varying their feed rates during electrospinning. The FP composites having three different particle loading are prepared by the methodology and the FP with the highest particle loading （denoted as FP-3 in the manuscript） showed the best overall efficiency of 9.15% in comparison to the other compositions of the FP （FP-2, 8.15% and FP-1, Z51%, respectively） and nanofibers （F） and nanoparticles （P） separately （7.21 and 7.81, respectively）. All the material systems are characterized by spec- troscopy, microscopy, surface area measurements and the devices are characterized by current-voltage （I-V）, incident photon-to-current conversion efficiency （IPCE）, electrochemical impedance measurements, etc. I-V, dye-loading and reflectance measurements throw light on the overall performance of the DSC devices.展开更多
Silica( SiO_2) based aerogel/xerogel materials have been received ever-growing attentions for versatile applications. However,the widespread applications are narrowed by the inert properties,fragile and brittle nature...Silica( SiO_2) based aerogel/xerogel materials have been received ever-growing attentions for versatile applications. However,the widespread applications are narrowed by the inert properties,fragile and brittle natureof silica materials and cumbersome preparation processes. In this paper,titania( TiO_2) was introduced into SiO_2 matrix to form photocatalytic hybrid gels. The TiO_2/SiO_2 composites were then reinforced by the impregnation of various fibrillary reinforcements,such as glass,mullite mineral and ceramic fibers. The properties of the composites were studied systematically in terms of fiberstability,microstructure,chemical interaction and thermal conductivity. The final xerogel composites displayed improved monolithic geometry,satisfied thermal conductivity(0. 09-0. 25 W·m^(-1)·K^(-1)) and optimized photocatalytic performance(85% removal of model pollutant of methyl orange( Mo)),which could be expected to be a feasible route to multi-functional building facades in the future.展开更多
In this paper, a detailed study was carried out on the PTFE reinforced with TiO2 and CaTiO3. The filler content of ceramic powder was a fixed value of 61 wt% and the content of CaTiO3 in PTFE matrix varied from 0 wt% ...In this paper, a detailed study was carried out on the PTFE reinforced with TiO2 and CaTiO3. The filler content of ceramic powder was a fixed value of 61 wt% and the content of CaTiO3 in PTFE matrix varied from 0 wt% to 16 wt% with a step size of 4 wt%. The effects of CaTiO3 loading on the density, moisture absorption, thermal expansion, microstructure and microwave dielectric properties were investigated. As CaTiO3 loading content increased from 0 wt% to 16 wt%, the thermal expansion initially displayed a sharp increase, and showed a slight enhancement when the content of CaTiO3 exceeded 12 wt%. The density experienced a continuous decrease with the addition of CaTiO3. The moisture absorption displayed a steady increase with the increasing CaTiO3 loading amount. The changing of dielectric constant (εr) and loss tangent (tanδ) were similar to that of the moisture absorption in a manner. Good dielectric properties with values of εr = 11.60, tanδ = 0.002 were obtained in the PTFE matrix with 16 wt% CaTiO3 and 45 wt% TiO2.展开更多
Particulate composites based on isotactic polypropylene(iPP) and titanium dioxide(TiO 2) have been prepared and their morphology and thermal behavior investigated by scanning electron microscopy(SEM), differential sca...Particulate composites based on isotactic polypropylene(iPP) and titanium dioxide(TiO 2) have been prepared and their morphology and thermal behavior investigated by scanning electron microscopy(SEM), differential scanning calorimetry(DSC) and thermogravimetric analysis(TGA). Tensile tests were performed to assess the influence of TiO 2 on the mechanical properties of the iPP.展开更多
Nanocrystalline titanium dioxide (TiO2) thin films were prepared by using sol-gel through spin- coating method. An assembly of indium tin oxide (ITO)/TiO2/polyaniline (PANI)/Ag was made in a sandwich panel structure. ...Nanocrystalline titanium dioxide (TiO2) thin films were prepared by using sol-gel through spin- coating method. An assembly of indium tin oxide (ITO)/TiO2/polyaniline (PANI)/Ag was made in a sandwich panel structure. The obtained junction shows rectifying behavior. Additionally, the I/V characteristic indicates that a P-N junction at nanocrystalline PANI/TiO2 interface has been created. In this experimental study, we depended only on the ratio between titanium and PANI in the process of preparing sol-gel (PANi/TiO2 at 20% wt). The largest open circuit voltage of 656 mV and short current density of 0.00315 mΑ/cm2 produce 0.0004% power conversion solar cell (η) under simulated solar radiation (50 mW/cm2). The thin films of PANI and titanium oxide (TiO2)/ PANI composites were synthesized by sol-gel technique. Pure TiO2 powder with nanoparticle size of less than 25 nm and PANI were synthesized through chemical oxidative polymerization of aniline monomers. The composite films were characterized by high resolution X-ray diffraction, Fourier transform infrared spectroscopy, field effect scanning electron microscopy, and UV-vis spectroscopy. The results were compared with the corresponding data on pure PANI films. The intensity of diffraction peaks for PANI/TiO2 composites is lower than that for TiO2. The characteristic of the FTIR peaks of pure PANI shifts to a higher wave number in TiO2/PANI composite, which is attributed to the interaction of TiO2 nanoparticles with PANI molecular chains.展开更多
ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （...ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.展开更多
Solid state NMR was successfully used to determine the proton spin-lattice relaxation time in the rotating frame (T1ρH) for systems based on polypropylene (PP) and PP with titanium dioxide (TiO<sub>2</sub>...Solid state NMR was successfully used to determine the proton spin-lattice relaxation time in the rotating frame (T1ρH) for systems based on polypropylene (PP) and PP with titanium dioxide (TiO<sub>2</sub>) organically modified or unmodified incorporated, in order to understand the molecular behavior of these systems. These techniques were employed in the samples organically modified and unmodified TiO<sub>2</sub> to investigate the effect of organic modification on the dispersion and distribution of the particles in the PP matrix. The results were analyzed in terms of the effect of the particles organic modified or not according to the intermolecular interaction in the composites. According to the T1ρH values, all composites showed at least two domains: the short values were related to the rigid part, which included the crystalline and amorphous phase constricted in it, while the longer times were attributed to the amorphous region, which had higher molecular mobility compared to the rigid region of the materials. The increase in the relaxation time parameter in the composites compared to the pure PP was associated to the strong interaction between titanium dioxide particles and the polymer chains. This effect was more pronounced for the systems containing organically modified TiO<sub>2</sub>. According to the results, it could be inferred that intermolecular interaction occurred in the CH<sub>2</sub> and CH groups, being more intense with CH<sub>2</sub> groups. Finally, the solid state NMR techniques were able to evaluate the molecular dynamics of those systems.展开更多
Mg-based Mg-TiO2 composite powder was prepared by arc plasma evaporation of the Mg＋5%TiO2 mixture followed by passivation in air. ICP, XRD and SEM techniques were used to characterize the composition, phase component...Mg-based Mg-TiO2 composite powder was prepared by arc plasma evaporation of the Mg＋5%TiO2 mixture followed by passivation in air. ICP, XRD and SEM techniques were used to characterize the composition, phase components and microstructure of the composite powder. The hydrogen sorption properties of the composite powder were investigated by DSC and PCT techniques. According to the data from PCT measurements, the hydrogenation enthalpy and entropy changes of the composite powder are calculated to be-71.5 kJ/mol and-130.1 J/（K·mol）, respectively. Besides, the hydrogenation activation energy is determined to be 77.2 kJ/ mol. The results indicate that TiO2 added into Mg by arc plasma method can act as a catalyst to improve the hydrogen sorption kinetic properties of Mg.展开更多
The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The c...The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.展开更多
The uniform transparent TiO2/SiO2 photocatalytic composite thin films are prepared by sol-gel method on the soda lime glass substrates, and characterized by UV-visible spectroscopy, X-ray diffraction (XRD), transmissi...The uniform transparent TiO2/SiO2 photocatalytic composite thin films are prepared by sol-gel method on the soda lime glass substrates, and characterized by UV-visible spectroscopy, X-ray diffraction (XRD), transmission electron microscopy (TEM), BET surface area, FTIR spectroscopy and X-ray photoelectron spectroscopy (XPS). It was found that the addition of SiO2 to TiO2 thin films can suppress the grain growth of TiO2 crystal, increase the hydroxyl content on the surface of TiO2 films, lower the contact angle for water on TiO, films and enhance the hydrophilic property of TiO2 films. The super-hydrophilic TiO2/SiO2 photocatalytic composite thin films with the contact angle of 0((o) under bar) are obtained by the addition of 10%-20% SiO2 in mole fraction.展开更多
基金financially supported by the University of Tabriz
文摘Surface of TiO2 nanoparticles was modified with the in situ chemical oxidative polymerization of aniline. Polyaniline modified TiO2 nanoparticles （PANI-TiO2） were characterized with the FT-IR, XRD, SEM and TEM techniques. Results confirmed that PANI was grafted successfully on the surface of TiO2 nanoparticles, therefore agglomeration of nanoparticles decreased dramatically. Polyvinyl chloride nanocomposites filled with 1 wt%-5 wt% of PANI-TiO2 and TiO2 nanoparticles were prepared via the solution blending method. PVC nanocomposites were analyzed with FT-IR, XRD, SEM, TG/DTA, DSC and tensile test techniques. Effect of PANI as surface modifier of nanoparticles was discussed according to the final properties of PVC nanocomposites. Results demonstrated that deposition of PANI on the surface of TiO2 nanoparticles improved the interfacial adhesion between the constituents of nanocomposites, which resulted in better dispersion of nanoparticles in the PVC matrix. Also PVC/PANI-TiO2 nanocomposites showed higher thennal resistance, tensile strength and Young＇s modulus compared to those of unfilled PVC and PVC/TiO2 nanocomposites.
文摘Polyaniline （PAn） sensitized nanocrystalline TiO2 composites （TiO2/PAn） were successfully prepared and used as an efficient photocatalyst for the degradation of dye methylene blue （MB）. The results showed that PAn was able to sensitize TiO2 efficiently and the composite photocatalyst could be activated by absorbing both the ultraviolet and visible light （λ： 190 ～ 800 nm）, whereas pure TiO2 absorbed ultraviolet light only （λ 〈 380 nm）. Under the irradiation of natural light, MB could be degraded more efficiently on the TiO2/PAn composites than on the TiO2 Furthermore, it could be easily separated from the solution by simple sedimentation.
基金Supported by the National Natural Science Foundation of China(No.51073064)the Science Foundation of Anhui Province, China(No.090414192)
文摘The p-NiO/n-TiO2/polyaniline composites were synthesized via in situ polymerization of aniline. The structure and morphology of the composites were characterized by means of X-ray diffraction（XRD）, scanning electron microscopy（SEM）, Fourier transform infrared spectroscopy（FTIR） and UV-Vis absorption spectroscopy. It was found that the p-n junction p-NiO/n-TiO2 particles were trapped in the polyaniline molecular matrix and the polyaniline was deposited on the surface of the particles to form a kind of flower cluster morphologies. The electrochemical behavior of the polyaniline composites was investigated. The electrochemical reactivity of the polyaniline was influenced by the p-NiO/n-TiO2 particles due to the effect of electron-hole pairs in these p-n junction particles. The reversibility of redox process and current intensity of the polyaniline composites with the changing of potential scan rate were also discussed.
基金Funded in Part by the Research Fund of Hubei Provincial Department of Education,China(No.Q20121102)
文摘Polyaniline （PANI） composite nanotubes （90-130 nm in diameter） containing titanium dioxide （TiO2） nanoparticles （about 10 nm in diameter） were synthesized through a self-assembly process in the presence of a-naphthalenesulfonic acid （a-NSA） as the dopant. It was found that PANI-TiO2 composites and PANI nanotubes both behaved with significant photocatalytic activities towards AZO dyes, during 2 h photocatalytic processes under natural light, the degradation ratio was 94.2% and 97.2% respectively （methyl orange and orange II）. The morphology of such products was characterized by SEM. The specific surface area of such composite nanotubes was 14.7 m2/g compared to normal polyaniline which was 0.27 m2/g. IR and X-ray diffraction characterizations showed that the chemical chain of the composite nanotubes was identical to that of the doped PANI. It may provide a new way for photodegradation of organic contaminants by using conjugated polymer with dimensional structure.
基金Project(50802034) supported by the National Natural Science Foundation of ChinaProject(11A093) supported by the Key Project Foundation by the Education Department of Hunan Province,China
文摘TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to estimate activity of catalysts and determine the kinetics. And the effects of parameters including the initial concentration of AY, light intensity and TiO2 content in catalysts were examined. The results indicate that TAs has a higher efficiency in decomposition of AY than P25, pure TiO2 particles as well as the mixture of TiO2 powder and active carbon. The photocatalytic degradation rate is found to follow the pseudo-first order kinetics with respect to the AY concentration. The new kinetic model fairly resembles the classic Langmuir-Hinshelwood equation, and the rate constant is proportional to the square root of the light intensity in a wide range. However, its absorption performance depends on the surface areas of catalysts. The model fits quite well with the experimental data and elucidates phenomena about the effects of the TiO2 content in TAs on the degradation rate.
基金supported by the National Basic Research Program of China (973 Program,2014CB239300)the National Natural Science Foundation of China (51572191)the Natural Science Foundation of Tianjin (13JCYBJC16600)~~
文摘We report the construction of a graphene/tourmaline/TiO2(G/T/TiO2)composite system with enhanced charge‐carrier separation,and therefore enhanced photocatalytic properties,based on tailoring the surface‐charged state of graphene and/or by introducing an external electric field arising from tourmaline.A simple two‐step hydrothermal method was used to synthesize G/T/TiO2composites and poly(diallyldimethylammonium chloride)‐G/T/TiO2composites.In the photocatalytic degradation of2‐propanol(IPA),the catalytic activity of the composite containing negatively charged graphene was higher than of the composite containing positively charged graphene.The highest acetone evolution rate(223?mol/h)was achieved using the ternary composite with the optimum composition,i.e.,G0.5/T5/TiO2(0.5wt%graphene and5wt%tourmaline).The involvement of tourmaline and graphene in the composite is believed to facilitate the separation and transportation of electrons and holes photogenerated in TiO2.This synergetic effect could account for the enhanced photocatalytic activity of the G/T/TiO2composite.A mechanistic study indicated that O2??radicals and holes were the main reactive oxygen species in photocatalytic degradation of IPA.
基金The authors acknowledge funding from the National Natural Science Foundation of China(Nos.51572157,21902085,and 51702188)Natural Science Foundation of Shandong Province(No.ZR2019QF012)+1 种基金Fundamental Research Funds for the Central Universities(No.2018JC036 and No.2018JC046)Young Scholars Program of Shandong University(No.2018WLJH25).
文摘Modern communication technologies put forward higher requirements for electromagnetic wave(EMW)absorption materials.Metal-organic framework(MOF)derivatives have been widely concerned with its diverse advantages.To break the mindset of magneticderivative design,and make up the shortage of monometallic non-magnetic derivatives,we first try non-magnetic bimetallic MOFs derivatives to achieve efficient EMW absorption.The porous carbon-wrapped TiO2/ZrTiO4 composites derived from PCN-415(TiZr-MOFs)are qualified with a minimum reflection loss of−67.8 dB(2.16 mm,13.0 GHz),and a maximum effective absorption bandwidth of 5.9 GHz(2.70 mm).Through in-depth discussions,the synergy of enhanced interfacial polarization and other attenuation mechanisms in the composites is revealed.Therefore,this work confirms the huge potentials of nonmagnetic bimetallic MOFs derivatives in EMW absorption applications.
文摘A nanoheterojunction composite photocatalyst Bi2O3/TiO2 working under visible-light （λ≥ 420 nm） was prepared by combining two semiconductors Bi2O3 and TiO2 varying the Bi2O3/TiO2 molar ratio. Maleic acid was employed as an organic binder to unite Bi2O3 and TiO2 nanoparticles. The SEM, TEM, XRD and diffuse reflectance spectra were utilized to characterize the prepared Bi2O3/TiO2 nanoheterojunction. The nanocomposite exhibited unusual high photocatalytic activity in decomposing 2-propanol in gas phase and phenol in aqueous phase and, evolution of CO2 under visible light irradiation while the end members exhibited low photocatalytic activity. The composite was optimized to 5 mol% Bi2O3/TiO2. The remarkable high photocatalytic efficiency originates from the unique relative energy band position of Bi2O3 and TiO2 as well as the absorption of visible light by Bi2O3.
文摘TiO2 filled polytetrafluoroethylene (PTFE) composite were fabricated for microwave circuit applications. PTFE/TiO2 composites were prepared by cold pressing and hot treating. The particle size of TiO2 varied from 5 μm to 11 μm.TiO2 powders with different sizes were prepared by the solid state ceramic route. The effects of TiO2 particle size on the microstructure, density, moisture absorption, thermal conductivity and microwave dielectric properties of PTFE/TiO2 composites were investigated. The density showed an increasing trend as the TiO2 particle size increased, while the dielectric loss (tanδ) and moisture absorption decreased with the increase of TiO2 particle size. The dielectric constant (εr) and thermal conductivity (λ) decreased up to D50 = 6.5 μm and then sharply increased. Good properties with values of εr = 6.8, tanδ = 0.0012 and λ = 0.533 W?m?1?K?1 were obtained in PTFE/TiO2 composites when the particle size of TiO2 was 11 μm.
文摘In the present work, composites of poly (methyl methacrylate)/titanium oxide nanoparticles (100/0, 97.5/2.5, 95/5, 92.5/7.5, 90/10 and 0/100 wt/wt%)were prepared to be used as bioequivalent materials according to their importance broad practical and medical applications. Thermal properties as well as X-ray diffraction analyses were employed to characterize the structure properties of such composite. The obtained results showed variations in the glass transition temperature (Tg), the melting temperature (Tm), shape and area of thermal peaks which were attributed to the different degrees of crystallinity and the existence of interactions between PMMA and TiO2 nanoparticle molecules. The XRD patterns showed sharpening of peaks at different concentrations of nano-TiO2 powder with PMMA. This indicated changes in the crystallinity/amorphosity ratio, and also suggested that the miscibility between the amorphous components of homo- polymers PMMA and nano-TiO2 powder is possible.The results showed that nano-TiO2 powder mix with PMMA can improve the thermal stability of the homo-polymer under investigation, lead- ing to interesting technological applications.
基金supported by Ministry of New and Renewable Energy(MNRE)the Solar Energy Research Initiative(SERI),respectively.of Govt.of India
文摘We report a facile method for the fabrication of TiO2 nanofiber-nanoparticle composite （FP） via. simulta- neous electrospraying and electrospinning for dye-sensitized solar cell （DSC） applications. The loading of nanoparticles on the fibers is controlled by varying their feed rates during electrospinning. The FP composites having three different particle loading are prepared by the methodology and the FP with the highest particle loading （denoted as FP-3 in the manuscript） showed the best overall efficiency of 9.15% in comparison to the other compositions of the FP （FP-2, 8.15% and FP-1, Z51%, respectively） and nanofibers （F） and nanoparticles （P） separately （7.21 and 7.81, respectively）. All the material systems are characterized by spec- troscopy, microscopy, surface area measurements and the devices are characterized by current-voltage （I-V）, incident photon-to-current conversion efficiency （IPCE）, electrochemical impedance measurements, etc. I-V, dye-loading and reflectance measurements throw light on the overall performance of the DSC devices.
基金National Natural Science Foundations of China(Nos.51308079,51408073,51678080,51678081)
文摘Silica( SiO_2) based aerogel/xerogel materials have been received ever-growing attentions for versatile applications. However,the widespread applications are narrowed by the inert properties,fragile and brittle natureof silica materials and cumbersome preparation processes. In this paper,titania( TiO_2) was introduced into SiO_2 matrix to form photocatalytic hybrid gels. The TiO_2/SiO_2 composites were then reinforced by the impregnation of various fibrillary reinforcements,such as glass,mullite mineral and ceramic fibers. The properties of the composites were studied systematically in terms of fiberstability,microstructure,chemical interaction and thermal conductivity. The final xerogel composites displayed improved monolithic geometry,satisfied thermal conductivity(0. 09-0. 25 W·m^(-1)·K^(-1)) and optimized photocatalytic performance(85% removal of model pollutant of methyl orange( Mo)),which could be expected to be a feasible route to multi-functional building facades in the future.
文摘In this paper, a detailed study was carried out on the PTFE reinforced with TiO2 and CaTiO3. The filler content of ceramic powder was a fixed value of 61 wt% and the content of CaTiO3 in PTFE matrix varied from 0 wt% to 16 wt% with a step size of 4 wt%. The effects of CaTiO3 loading on the density, moisture absorption, thermal expansion, microstructure and microwave dielectric properties were investigated. As CaTiO3 loading content increased from 0 wt% to 16 wt%, the thermal expansion initially displayed a sharp increase, and showed a slight enhancement when the content of CaTiO3 exceeded 12 wt%. The density experienced a continuous decrease with the addition of CaTiO3. The moisture absorption displayed a steady increase with the increasing CaTiO3 loading amount. The changing of dielectric constant (εr) and loss tangent (tanδ) were similar to that of the moisture absorption in a manner. Good dielectric properties with values of εr = 11.60, tanδ = 0.002 were obtained in the PTFE matrix with 16 wt% CaTiO3 and 45 wt% TiO2.
文摘Particulate composites based on isotactic polypropylene(iPP) and titanium dioxide(TiO 2) have been prepared and their morphology and thermal behavior investigated by scanning electron microscopy(SEM), differential scanning calorimetry(DSC) and thermogravimetric analysis(TGA). Tensile tests were performed to assess the influence of TiO 2 on the mechanical properties of the iPP.
文摘Nanocrystalline titanium dioxide (TiO2) thin films were prepared by using sol-gel through spin- coating method. An assembly of indium tin oxide (ITO)/TiO2/polyaniline (PANI)/Ag was made in a sandwich panel structure. The obtained junction shows rectifying behavior. Additionally, the I/V characteristic indicates that a P-N junction at nanocrystalline PANI/TiO2 interface has been created. In this experimental study, we depended only on the ratio between titanium and PANI in the process of preparing sol-gel (PANi/TiO2 at 20% wt). The largest open circuit voltage of 656 mV and short current density of 0.00315 mΑ/cm2 produce 0.0004% power conversion solar cell (η) under simulated solar radiation (50 mW/cm2). The thin films of PANI and titanium oxide (TiO2)/ PANI composites were synthesized by sol-gel technique. Pure TiO2 powder with nanoparticle size of less than 25 nm and PANI were synthesized through chemical oxidative polymerization of aniline monomers. The composite films were characterized by high resolution X-ray diffraction, Fourier transform infrared spectroscopy, field effect scanning electron microscopy, and UV-vis spectroscopy. The results were compared with the corresponding data on pure PANI films. The intensity of diffraction peaks for PANI/TiO2 composites is lower than that for TiO2. The characteristic of the FTIR peaks of pure PANI shifts to a higher wave number in TiO2/PANI composite, which is attributed to the interaction of TiO2 nanoparticles with PANI molecular chains.
基金Project(gf200901002)supported by the Open Research Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang Hangkong University,China
文摘ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.
文摘Solid state NMR was successfully used to determine the proton spin-lattice relaxation time in the rotating frame (T1ρH) for systems based on polypropylene (PP) and PP with titanium dioxide (TiO<sub>2</sub>) organically modified or unmodified incorporated, in order to understand the molecular behavior of these systems. These techniques were employed in the samples organically modified and unmodified TiO<sub>2</sub> to investigate the effect of organic modification on the dispersion and distribution of the particles in the PP matrix. The results were analyzed in terms of the effect of the particles organic modified or not according to the intermolecular interaction in the composites. According to the T1ρH values, all composites showed at least two domains: the short values were related to the rigid part, which included the crystalline and amorphous phase constricted in it, while the longer times were attributed to the amorphous region, which had higher molecular mobility compared to the rigid region of the materials. The increase in the relaxation time parameter in the composites compared to the pure PP was associated to the strong interaction between titanium dioxide particles and the polymer chains. This effect was more pronounced for the systems containing organically modified TiO<sub>2</sub>. According to the results, it could be inferred that intermolecular interaction occurred in the CH<sub>2</sub> and CH groups, being more intense with CH<sub>2</sub> groups. Finally, the solid state NMR techniques were able to evaluate the molecular dynamics of those systems.
基金Project(11ZR1417600)supported by Shanghai Natural Science Foundation from Science and Technology Committee of Shanghai,ChinaProject(11PJ1406000)supported by‘Pujiang’Project from the Science and Technology Committee of Shanghai+1 种基金Project(12ZZ017)supported by Shanghai Education Commission,ChinaProject(20100073120007)supported by China Education Commission
文摘Mg-based Mg-TiO2 composite powder was prepared by arc plasma evaporation of the Mg＋5%TiO2 mixture followed by passivation in air. ICP, XRD and SEM techniques were used to characterize the composition, phase components and microstructure of the composite powder. The hydrogen sorption properties of the composite powder were investigated by DSC and PCT techniques. According to the data from PCT measurements, the hydrogenation enthalpy and entropy changes of the composite powder are calculated to be-71.5 kJ/mol and-130.1 J/（K·mol）, respectively. Besides, the hydrogenation activation energy is determined to be 77.2 kJ/ mol. The results indicate that TiO2 added into Mg by arc plasma method can act as a catalyst to improve the hydrogen sorption kinetic properties of Mg.
基金Sponsored by Hi-Tech Research and Development Program of China (2003AA305120)
文摘The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.
基金This work was financially supported by the Foundation for University Key Teachers by the Ministry of Education, theKey Resear
文摘The uniform transparent TiO2/SiO2 photocatalytic composite thin films are prepared by sol-gel method on the soda lime glass substrates, and characterized by UV-visible spectroscopy, X-ray diffraction (XRD), transmission electron microscopy (TEM), BET surface area, FTIR spectroscopy and X-ray photoelectron spectroscopy (XPS). It was found that the addition of SiO2 to TiO2 thin films can suppress the grain growth of TiO2 crystal, increase the hydroxyl content on the surface of TiO2 films, lower the contact angle for water on TiO, films and enhance the hydrophilic property of TiO2 films. The super-hydrophilic TiO2/SiO2 photocatalytic composite thin films with the contact angle of 0((o) under bar) are obtained by the addition of 10%-20% SiO2 in mole fraction.