Lightweight aggregates are increasingly used in concrete construction. They reduce concrete selfweight furnishing a structural advantage. In contrast, the mechanical properties and durability of lightweight concrete c...Lightweight aggregates are increasingly used in concrete construction. They reduce concrete selfweight furnishing a structural advantage. In contrast, the mechanical properties and durability of lightweight concrete can become the governing factor on lightweight aggregate replacement ratios. Alkali-Silica Reactison (ASR) and compressive strength of mortar samples with expanded slate, expanded glass or perlite, covering the spectrum of internal porosity and weight of lightweight aggregates, were evaluated. Scanning electron microscopy was utilized to evaluate the contribution of the aggregates’ porosity and chemical composition in inhibiting ASR. Perlite, owing to its highly porous microstructure and lower matter excelled in ASR expansion while chemical composition and denser microstructure of the heavier expanded slate resulted in more signified late ASR expansion and higher compressive strength. An attempt in visual inspection of ASR attack of alkali metal ions on silica-rich expanded glass using an ultra-accelerated exposure to sodium hydroxide solution was made</span></span><span style="font-family:Verdana;">.展开更多
文摘Lightweight aggregates are increasingly used in concrete construction. They reduce concrete selfweight furnishing a structural advantage. In contrast, the mechanical properties and durability of lightweight concrete can become the governing factor on lightweight aggregate replacement ratios. Alkali-Silica Reactison (ASR) and compressive strength of mortar samples with expanded slate, expanded glass or perlite, covering the spectrum of internal porosity and weight of lightweight aggregates, were evaluated. Scanning electron microscopy was utilized to evaluate the contribution of the aggregates’ porosity and chemical composition in inhibiting ASR. Perlite, owing to its highly porous microstructure and lower matter excelled in ASR expansion while chemical composition and denser microstructure of the heavier expanded slate resulted in more signified late ASR expansion and higher compressive strength. An attempt in visual inspection of ASR attack of alkali metal ions on silica-rich expanded glass using an ultra-accelerated exposure to sodium hydroxide solution was made</span></span><span style="font-family:Verdana;">.