The effects of ceria and zirconium oxides additions to alumina-supported palladium catalysts on methane combustion behavior were investigated. The structure and TPR/TPO properties were studied by XRD, TPR, TPO techniq...The effects of ceria and zirconium oxides additions to alumina-supported palladium catalysts on methane combustion behavior were investigated. The structure and TPR/TPO properties were studied by XRD, TPR, TPO techniques. The results show that the addition of Ce-Zr oxides improves the thermal stability of alumina and PdO. The Pd/Ce0.2Zr0.8/Al2O3 exhibits the highest activity and thermal stability for methane combustion.展开更多
The transition metals （Cu, Co, and Fe） were applied to modify Ni/Ce0.2Zr0.1Al0.7Oδ catalyst. The effects of transition metals on the catalytic properties of Ni/Ce0.2Zr0.1Al0.7Oδ autothermal reforming of methane we...The transition metals （Cu, Co, and Fe） were applied to modify Ni/Ce0.2Zr0.1Al0.7Oδ catalyst. The effects of transition metals on the catalytic properties of Ni/Ce0.2Zr0.1Al0.7Oδ autothermal reforming of methane were investigated. The Ni-supported catalysts were characterized by XRD, TPR and XPS. Tests in autothermal reforming of methane to hydrogen showed that the addition of transition metals （Cu and Co） significantly increased the activity of catalyst under the conditions of lower reaction temperature, and Ni/Cu0.05Ce0.2Zr0.1Al0.65Oδ was found to have the highest conversion of CH4 among all catalysts in the operation temperatures ranging from 923 K to 1023 K. TPR, XRD and XPS measurements indicated that the cubic phases of CexZr1-xO2 solid solution were formed in the preparation process of catalysts. Strong interaction was found to exist between NiO and CexZr1-xO2 solid solution. The addition of Cu improved the dispersion of NiO, inhibited the formation of NiAl2O4, and thus significantly promoted the activity of the catalyst Ni/Cu0.05Ce0.2Zr0.1Al0.65Oδ展开更多
CexZr1-xO2 complex oxides doped by transition metal(Fe, Mn, Cu) were prepared by precipitation method. Thermal stability of samples was characterized by XRD, surface areas were measured by BET method and reductive pro...CexZr1-xO2 complex oxides doped by transition metal(Fe, Mn, Cu) were prepared by precipitation method. Thermal stability of samples was characterized by XRD, surface areas were measured by BET method and reductive property was characterized by TPR. The results show that MnO2 can be dispersed in solid solution after calcined at 1273 K, when the loading is 12%, while Fe and Cu is easy to separate from samples at this temperature. Samples doped simultaneously by Fe, Mn or Fe, Cu demonstrated high reactive property at low temperature. The starting reduction temperature are 413 and 373 K, respectively. TPR results also show a broad range of reductive temperature exists in these bi-metal doped samples.展开更多
文摘The effects of ceria and zirconium oxides additions to alumina-supported palladium catalysts on methane combustion behavior were investigated. The structure and TPR/TPO properties were studied by XRD, TPR, TPO techniques. The results show that the addition of Ce-Zr oxides improves the thermal stability of alumina and PdO. The Pd/Ce0.2Zr0.8/Al2O3 exhibits the highest activity and thermal stability for methane combustion.
基金This work was supported by Guangdong Natural Science Foundation of China (030514)Science and Technology Programs of Guangdong Province of China (2004B33401006)
文摘The transition metals （Cu, Co, and Fe） were applied to modify Ni/Ce0.2Zr0.1Al0.7Oδ catalyst. The effects of transition metals on the catalytic properties of Ni/Ce0.2Zr0.1Al0.7Oδ autothermal reforming of methane were investigated. The Ni-supported catalysts were characterized by XRD, TPR and XPS. Tests in autothermal reforming of methane to hydrogen showed that the addition of transition metals （Cu and Co） significantly increased the activity of catalyst under the conditions of lower reaction temperature, and Ni/Cu0.05Ce0.2Zr0.1Al0.65Oδ was found to have the highest conversion of CH4 among all catalysts in the operation temperatures ranging from 923 K to 1023 K. TPR, XRD and XPS measurements indicated that the cubic phases of CexZr1-xO2 solid solution were formed in the preparation process of catalysts. Strong interaction was found to exist between NiO and CexZr1-xO2 solid solution. The addition of Cu improved the dispersion of NiO, inhibited the formation of NiAl2O4, and thus significantly promoted the activity of the catalyst Ni/Cu0.05Ce0.2Zr0.1Al0.65Oδ
文摘CexZr1-xO2 complex oxides doped by transition metal(Fe, Mn, Cu) were prepared by precipitation method. Thermal stability of samples was characterized by XRD, surface areas were measured by BET method and reductive property was characterized by TPR. The results show that MnO2 can be dispersed in solid solution after calcined at 1273 K, when the loading is 12%, while Fe and Cu is easy to separate from samples at this temperature. Samples doped simultaneously by Fe, Mn or Fe, Cu demonstrated high reactive property at low temperature. The starting reduction temperature are 413 and 373 K, respectively. TPR results also show a broad range of reductive temperature exists in these bi-metal doped samples.