Praseodymium （Pr） was impregnated to CeO2-ZrO2 solid solution by an impregnation method. The as-obtained Pr modi- fied CeO2-ZrO2 was impregnated with 1 wt.% Pd to prepare the catalysts. The structure and reducibilit...Praseodymium （Pr） was impregnated to CeO2-ZrO2 solid solution by an impregnation method. The as-obtained Pr modi- fied CeO2-ZrO2 was impregnated with 1 wt.% Pd to prepare the catalysts. The structure and reducibility of the fresh and hydrother- really aged catalysts were characterized by X-ray diffraction （XRD）, Raman, X-ray photoelectron spectroscopy （XPS）, CO chemi- sorption and H2 temperature-programmed reduction （H2-TPR）. The oxygen storage capacity （OSC） was evaluated with CO serving as probe gas. Effects of impregnated Pr on the structure and oxygen storage capacity of catalysts were investigated. The results showed that the aged Pr-impregnated samples had much higher OSC and better reducibility than the unmodified ones. The scheme of structural evolutions of the catalysts with and without Pr was also established. Partial of the impregnated Pr diffused into the bulk of CeO2-ZrO2 during ageing, which inhibited the sintering, and increased the amount of oxygen vacancies in CeO2-ZrO2 support. Furthermore, those impregnated Pr species which covered on the surface of the support obstructed the strong metal-support interaction between Pd and Ce so as to reduce the encapsulation of Pd as well as the back spill-over of the oxygen during the catalytic process.展开更多
Hairong Wang, Yaoqiang Chen, Qiulin Zhang, Qingchao Zhu, Maochu Gong, Ming Zhao（ Key Laboratory of Green Chemistry ＆ Technology of Ministry Education, College of Chemistry, Sichuan University, Chengdu 610064, Sichua...Hairong Wang, Yaoqiang Chen, Qiulin Zhang, Qingchao Zhu, Maochu Gong, Ming Zhao（ Key Laboratory of Green Chemistry ＆ Technology of Ministry Education, College of Chemistry, Sichuan University, Chengdu 610064, Sichuan, China展开更多
The Pd-only catalysts for motorcycle were prepared by impregnating CeO2-ZrO2-Al2O3 and CeO2-ZrO2+Al2O3 with PdCl2 aqueous solution and characterized by X-ray diffraction (XRD), oxygen storage capacity (OSC) and H2-tem...The Pd-only catalysts for motorcycle were prepared by impregnating CeO2-ZrO2-Al2O3 and CeO2-ZrO2+Al2O3 with PdCl2 aqueous solution and characterized by X-ray diffraction (XRD), oxygen storage capacity (OSC) and H2-temperature-programmed reduction (H2-TPR) methods. The XRD result indicated that the CeO2-ZrO2-Al2O3 compound prepared by co-precipitation formed a single solid solution and had good thermal stability, and Pd phase was not observed in all catalysts. The TPR results showed that the reduction temperature of Pd/CeO2-ZrO2-Al2O3 catalyst was lower than that of Pd/CeO2-ZrO2+Al2O3 catalyst whether they were fresh or aged catalysts. The Pd/CeO2-ZrO2-Al2O3 exhibited high three-way catalytic activity at low temperature, high thermal stability, and wide working window, suggesting a great potential for applications.展开更多
Ce-Zr-Al-Nd2O3 （CZAN） support materials were prepared by co-precipitation and impregnation methods, respectively. They were characterized by X-ray diffTaction （XRD）, low temperature nitrogen adsorption-desorption,...Ce-Zr-Al-Nd2O3 （CZAN） support materials were prepared by co-precipitation and impregnation methods, respectively. They were characterized by X-ray diffTaction （XRD）, low temperature nitrogen adsorption-desorption, oxygen pulsing technique, H2-temperamre programmed reduction （H2-TPR） and X-ray photoelectron spectroscopy （XPS）. The Pd-only three-way catalysts （Pd-TWC） supported on these materials were prepared by incipient wetness method and studied by activity tests. The results demonstrated that the CZAN supports obtained by the two methods showed better structural, textural and redox properties than the CZA without Nd2O3, and the addition of Nd203 improved the catalytic activity of TWC. Especially, the CZAN-i support prepared by impregnation method had better thermal stability and redox property. Meanwhile, the Pd/CZAN-i catalyst exhibited the best catalytic performance. XPS measurements indicated that the Nd-modified samples possessed more Ce3＋ and oxygen vacancies on the surface of samples, which led to a better redox property. The excellent redox property of support materials helped to improve the catalytic activity of TWC.展开更多
CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that...CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that three CeO2-based oxygen storage materials are all forming homogeneous solid solution.Among the samples,CeO2-ZrO2-Al2O3(CZA)has the best textural properties and excellent thermal stability.The specific surface area and pore volume of aged CZA are 90 m2/g and 0.29 mL/g.We proposed a viewpoint:Al3+ might insert among the interspace of fluorite structure or highly dispersal in solid solutions.展开更多
基金supported by the National Natural Science Foundation of China(21173153)National Hi-tech Research and Development Program of China(863)(2015AA034603)Opening Project of Key Laboratory of Green Chemistry of Sichuan Institutes of Higher Education,China(LYJ1407)~~
基金supported by National Natural Science Foundation of China(51202116)Ministry of Science and Technology,China(2010CB732304,2013AA065302)
文摘Praseodymium （Pr） was impregnated to CeO2-ZrO2 solid solution by an impregnation method. The as-obtained Pr modi- fied CeO2-ZrO2 was impregnated with 1 wt.% Pd to prepare the catalysts. The structure and reducibility of the fresh and hydrother- really aged catalysts were characterized by X-ray diffraction （XRD）, Raman, X-ray photoelectron spectroscopy （XPS）, CO chemi- sorption and H2 temperature-programmed reduction （H2-TPR）. The oxygen storage capacity （OSC） was evaluated with CO serving as probe gas. Effects of impregnated Pr on the structure and oxygen storage capacity of catalysts were investigated. The results showed that the aged Pr-impregnated samples had much higher OSC and better reducibility than the unmodified ones. The scheme of structural evolutions of the catalysts with and without Pr was also established. Partial of the impregnated Pr diffused into the bulk of CeO2-ZrO2 during ageing, which inhibited the sintering, and increased the amount of oxygen vacancies in CeO2-ZrO2 support. Furthermore, those impregnated Pr species which covered on the surface of the support obstructed the strong metal-support interaction between Pd and Ce so as to reduce the encapsulation of Pd as well as the back spill-over of the oxygen during the catalytic process.
基金the National Natural Science Foundation of China (20773090)the Specialized Research Fund for the Doctoral Program of Higher Education of China (20070610026, 200806100009)
文摘Hairong Wang, Yaoqiang Chen, Qiulin Zhang, Qingchao Zhu, Maochu Gong, Ming Zhao（ Key Laboratory of Green Chemistry ＆ Technology of Ministry Education, College of Chemistry, Sichuan University, Chengdu 610064, Sichuan, China
基金Project supported by the National High Technology Research and Development Program of China (863 Program,2006AA06Z347)the Specialized Research Fund for the Doctoral Program of Higher Education (20070610026)
文摘The Pd-only catalysts for motorcycle were prepared by impregnating CeO2-ZrO2-Al2O3 and CeO2-ZrO2+Al2O3 with PdCl2 aqueous solution and characterized by X-ray diffraction (XRD), oxygen storage capacity (OSC) and H2-temperature-programmed reduction (H2-TPR) methods. The XRD result indicated that the CeO2-ZrO2-Al2O3 compound prepared by co-precipitation formed a single solid solution and had good thermal stability, and Pd phase was not observed in all catalysts. The TPR results showed that the reduction temperature of Pd/CeO2-ZrO2-Al2O3 catalyst was lower than that of Pd/CeO2-ZrO2+Al2O3 catalyst whether they were fresh or aged catalysts. The Pd/CeO2-ZrO2-Al2O3 exhibited high three-way catalytic activity at low temperature, high thermal stability, and wide working window, suggesting a great potential for applications.
基金Project supported by National Natural Science Foundation of China (20773090, 20803049)the Specialized Research Fund for the Doctoral Program of Higher Education (20070610026, 200806100009)
文摘Ce-Zr-Al-Nd2O3 （CZAN） support materials were prepared by co-precipitation and impregnation methods, respectively. They were characterized by X-ray diffTaction （XRD）, low temperature nitrogen adsorption-desorption, oxygen pulsing technique, H2-temperamre programmed reduction （H2-TPR） and X-ray photoelectron spectroscopy （XPS）. The Pd-only three-way catalysts （Pd-TWC） supported on these materials were prepared by incipient wetness method and studied by activity tests. The results demonstrated that the CZAN supports obtained by the two methods showed better structural, textural and redox properties than the CZA without Nd2O3, and the addition of Nd203 improved the catalytic activity of TWC. Especially, the CZAN-i support prepared by impregnation method had better thermal stability and redox property. Meanwhile, the Pd/CZAN-i catalyst exhibited the best catalytic performance. XPS measurements indicated that the Nd-modified samples possessed more Ce3＋ and oxygen vacancies on the surface of samples, which led to a better redox property. The excellent redox property of support materials helped to improve the catalytic activity of TWC.
文摘CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that three CeO2-based oxygen storage materials are all forming homogeneous solid solution.Among the samples,CeO2-ZrO2-Al2O3(CZA)has the best textural properties and excellent thermal stability.The specific surface area and pore volume of aged CZA are 90 m2/g and 0.29 mL/g.We proposed a viewpoint:Al3+ might insert among the interspace of fluorite structure or highly dispersal in solid solutions.