V-Pd/γ-Al2O3-TiO2 catalysts with different vanadium contents were prepared by a combined sol-gel and impregnation method. X-ray diffraction （XRD）, N2 adsorption-desorption （BET）, X-ray photoelectron spectroscopy ...V-Pd/γ-Al2O3-TiO2 catalysts with different vanadium contents were prepared by a combined sol-gel and impregnation method. X-ray diffraction （XRD）, N2 adsorption-desorption （BET）, X-ray photoelectron spectroscopy （XPS） and catalytic removal of ethanol, acetaldehyde and nitrogen oxides at low temperature （〈300 ？C） were used to assess the properties of the catalysts. The results showed that the sample with 1wt% vanadium exhibited an excellent catalytic performance for simultaneous removal of ethanol, acetaldehyde and nitrogen oxides. The conversions of ethanol, acetaldehyde and nitrogen oxides at 250 ？C were 100%, 74.4% and 98.7%, respectively. V-Pd/γ-Al2O3-TiO2 catalyst with 1 wt% vanadium showed the largest surface area and higher dispersion of vanadium oxide on the catalyst surface, and possessed a larger mole fraction of V4＋ species and unique PdO species on the surface, which can be attributed to the strong synergistic effect among palladium, vanadium and the carriers. The higher activity of V-Pd/γ-Al2O3-TiO2 catalyst is related to the V4＋ and Pd2＋ species on the surface, which might be favorable for the formation of active sites.展开更多
Nano-particle Pd/?-Al2O3 monometallic and Pd-Cu/?-Al2O3 bimetall ic catalysts were prepared by solvated metal atom impregnation (SMAI) method. Th e results of XRD measurement indicated that Pd- Cu alloy was formed in ...Nano-particle Pd/?-Al2O3 monometallic and Pd-Cu/?-Al2O3 bimetall ic catalysts were prepared by solvated metal atom impregnation (SMAI) method. Th e results of XRD measurement indicated that Pd- Cu alloy was formed in the bim etallic catalysts and the crystalline particle size of the alloy increased as Cu contents increased with average diameters < 6.0nm for all the samples. XPS and Auger spectra showed that Pd was in zero- valent state, Cu existed mainly in z ero- valent state and partially in monovalent state Cu+. The Pd/?-Al2O3 and Pd-Cu/?-Al2O3 catalysts exhibited higher activity for CO oxidation at low temperature. The activity of Pd-Cu/?-Al2O3 bimetallic catalyst was hig her than that of Pd/?-Al2O3 monometallic catalyst. The Pd-Cu/?-Al2O3 c atalyst with Pd/Cu atomic ratio of 1∶1 showed the highest activity.展开更多
基金supported by the National Natural Science Foundation of China (No. 21073131)the Shanxi Natural Science Foundation(No. 2009011011-3)
文摘V-Pd/γ-Al2O3-TiO2 catalysts with different vanadium contents were prepared by a combined sol-gel and impregnation method. X-ray diffraction （XRD）, N2 adsorption-desorption （BET）, X-ray photoelectron spectroscopy （XPS） and catalytic removal of ethanol, acetaldehyde and nitrogen oxides at low temperature （〈300 ？C） were used to assess the properties of the catalysts. The results showed that the sample with 1wt% vanadium exhibited an excellent catalytic performance for simultaneous removal of ethanol, acetaldehyde and nitrogen oxides. The conversions of ethanol, acetaldehyde and nitrogen oxides at 250 ？C were 100%, 74.4% and 98.7%, respectively. V-Pd/γ-Al2O3-TiO2 catalyst with 1 wt% vanadium showed the largest surface area and higher dispersion of vanadium oxide on the catalyst surface, and possessed a larger mole fraction of V4＋ species and unique PdO species on the surface, which can be attributed to the strong synergistic effect among palladium, vanadium and the carriers. The higher activity of V-Pd/γ-Al2O3-TiO2 catalyst is related to the V4＋ and Pd2＋ species on the surface, which might be favorable for the formation of active sites.
基金supported by the National Natural Science Foundation of China(21173153)National Hi-tech Research and Development Program of China(863)(2015AA034603)Opening Project of Key Laboratory of Green Chemistry of Sichuan Institutes of Higher Education,China(LYJ1407)~~
文摘Nano-particle Pd/?-Al2O3 monometallic and Pd-Cu/?-Al2O3 bimetall ic catalysts were prepared by solvated metal atom impregnation (SMAI) method. Th e results of XRD measurement indicated that Pd- Cu alloy was formed in the bim etallic catalysts and the crystalline particle size of the alloy increased as Cu contents increased with average diameters < 6.0nm for all the samples. XPS and Auger spectra showed that Pd was in zero- valent state, Cu existed mainly in z ero- valent state and partially in monovalent state Cu+. The Pd/?-Al2O3 and Pd-Cu/?-Al2O3 catalysts exhibited higher activity for CO oxidation at low temperature. The activity of Pd-Cu/?-Al2O3 bimetallic catalyst was hig her than that of Pd/?-Al2O3 monometallic catalyst. The Pd-Cu/?-Al2O3 c atalyst with Pd/Cu atomic ratio of 1∶1 showed the highest activity.