The mixed-valent Pb3Rh7O15 undergoes a Verwey-type transition at Tv≈180K, below which the development of Rh3＋3＋/Rh4＋4＋ charge order induces an abrupt conductor-to-insulator transition in resistivity. Here we inve...The mixed-valent Pb3Rh7O15 undergoes a Verwey-type transition at Tv≈180K, below which the development of Rh3＋3＋/Rh4＋4＋ charge order induces an abrupt conductor-to-insulator transition in resistivity. Here we investigate the effect of pressure on the Verwey-type transition of Pb3Rh7O15 by measuring its electrical resistivity under hydrostatic pressures up to 8GPa with a cubic anvil cell apparatus. We find that the application of high pressure can suppress the Verwey-type transition around 3GPa, above which a metallic state is realized at temperatures below ～70K, suggesting the melting of charge order by pressure. Interestingly, the low-temperature metallic region shrinks gradually upon further increasing pressure and disappears completely at P〉7GPa, which indicates that the charge carriers in Pb3Rh7O15 undergo a reentrant localization under higher pressures. We have constructed a temperature-pressure phase diagram for Pb3Rh7O15 and compared to that of Fe3O4, showing an archetype Verwey transition.展开更多
基金Supported by the"Shi-Pei Ji Hua",the National Science Foundation of China under Grant Nos 51402019 and 11574377the Beijing Natural Science Foundation under Grant No 2152011+5 种基金the National Basic Research Program of China under Grants No2014CB921500the Strategic Priority Research ProgramKey Research Program of Frontier Sciences of the Chinese Academy of Sciences under Grant Nos XDB07020100 and QYZDB-SSW-SLH013the U.S.Department of Energy,Office of Science,Basic Energy Sciences,Materials Sciences and Engineering Divisionthe CEMNSF MRSEC under Grant No DMR-1420451
文摘The mixed-valent Pb3Rh7O15 undergoes a Verwey-type transition at Tv≈180K, below which the development of Rh3＋3＋/Rh4＋4＋ charge order induces an abrupt conductor-to-insulator transition in resistivity. Here we investigate the effect of pressure on the Verwey-type transition of Pb3Rh7O15 by measuring its electrical resistivity under hydrostatic pressures up to 8GPa with a cubic anvil cell apparatus. We find that the application of high pressure can suppress the Verwey-type transition around 3GPa, above which a metallic state is realized at temperatures below ～70K, suggesting the melting of charge order by pressure. Interestingly, the low-temperature metallic region shrinks gradually upon further increasing pressure and disappears completely at P〉7GPa, which indicates that the charge carriers in Pb3Rh7O15 undergo a reentrant localization under higher pressures. We have constructed a temperature-pressure phase diagram for Pb3Rh7O15 and compared to that of Fe3O4, showing an archetype Verwey transition.