The extrusion ratio is one of the key parameters for manufacturing the lead-glass fiber(Pb-GF)composite wire by coating extrusion.The effect of extrusion ratio on coating extrusion of Pb-GF composite wire was studied ...The extrusion ratio is one of the key parameters for manufacturing the lead-glass fiber(Pb-GF)composite wire by coating extrusion.The effect of extrusion ratio on coating extrusion of Pb-GF composite wire was studied by finite element numerical simulation with the use of the DEFOEM simulation software.The simulation result shows that the higher the extrusion ratio,the higher the effective stress that the glass fiber bears during extrusion.It is also observed that the extrusion force increases with the increase of the extrusion ratio.The extrusion experiment of Pb-GF composite wire reveals that extrusion ratio is changed by changing the quantity of glass fiber and composite diameter.The rule that increasing the extrusion ratio enhances the coating speed limit suggests that the load on the glass fiber increases with increasing extrusion ratio.Both the simulation and the extrusion experiments show that the extrusion force increases with increasing extrusion ratio.展开更多
GF/Pb compositeswerefabricated by the method of powder metallurgy, and the density, microstructure and tensile propertywerecharacterized considering the size and content ofglass fibre （GF）. The results show that rel...GF/Pb compositeswerefabricated by the method of powder metallurgy, and the density, microstructure and tensile propertywerecharacterized considering the size and content ofglass fibre （GF）. The results show that relative densities decrease with increasing GF fraction, and the 50μm-GF reinforced specimens exhibit a better densification than the 300μm-GF reinforced ones. The GF particles distribute quite uniformly inPb matrix, and the composites fabricated at low sintering temperature （〈200℃） possess fine-grain microstructure. The addition of GF significantly improves the strength of the Pb composites, and the ultimate tensile strength of the Pb composite reinforcedwith the addition of 50μm-0.5% GF（mass fraction）is about 30MPa higher than that of GF-free sample. For all composites groups, increasing the reinforcement content from 0.5%to 2%（mass fraction）results in a decrease in both tensile strength and ductility.展开更多
文摘The extrusion ratio is one of the key parameters for manufacturing the lead-glass fiber(Pb-GF)composite wire by coating extrusion.The effect of extrusion ratio on coating extrusion of Pb-GF composite wire was studied by finite element numerical simulation with the use of the DEFOEM simulation software.The simulation result shows that the higher the extrusion ratio,the higher the effective stress that the glass fiber bears during extrusion.It is also observed that the extrusion force increases with the increase of the extrusion ratio.The extrusion experiment of Pb-GF composite wire reveals that extrusion ratio is changed by changing the quantity of glass fiber and composite diameter.The rule that increasing the extrusion ratio enhances the coating speed limit suggests that the load on the glass fiber increases with increasing extrusion ratio.Both the simulation and the extrusion experiments show that the extrusion force increases with increasing extrusion ratio.
文摘GF/Pb compositeswerefabricated by the method of powder metallurgy, and the density, microstructure and tensile propertywerecharacterized considering the size and content ofglass fibre （GF）. The results show that relative densities decrease with increasing GF fraction, and the 50μm-GF reinforced specimens exhibit a better densification than the 300μm-GF reinforced ones. The GF particles distribute quite uniformly inPb matrix, and the composites fabricated at low sintering temperature （〈200℃） possess fine-grain microstructure. The addition of GF significantly improves the strength of the Pb composites, and the ultimate tensile strength of the Pb composite reinforcedwith the addition of 50μm-0.5% GF（mass fraction）is about 30MPa higher than that of GF-free sample. For all composites groups, increasing the reinforcement content from 0.5%to 2%（mass fraction）results in a decrease in both tensile strength and ductility.