To improve the wettability of hypereutectic Al−60Si alloy and enhance the mechanical properties of the joints,Al−60Si alloy was joined by ultrasonic soldering with Sn-9Zn solder,and a sound joint with in-situ Si parti...To improve the wettability of hypereutectic Al−60Si alloy and enhance the mechanical properties of the joints,Al−60Si alloy was joined by ultrasonic soldering with Sn-9Zn solder,and a sound joint with in-situ Si particle reinforcement was obtained.The oxide film of Al−60Si alloy at the interface was identified by transmission electron microscopy(TEM)analysis as amorphous Al_(2)O_(3).The oxide of Si particles in the base metal was also alumina.The oxide film of Al−60Si alloy was observed to be removed by ultrasonic vibration instead of holding treatment.Si particle-reinforced joints(35.7 vol.%)were obtained by increasing the ultrasonication time.The maximum shear strength peaked at 99.5 MPa for soldering at 330℃with an ultrasonic vibration time of 50 s.A model of forming of Si particles reinforced joint under the ultrasound was proposed,and ultrasonic vibration was considered to promote the dissolution of Al and migration of Si particles.展开更多
The characterization of reinforcement in 15% SiC particles reinforced AI matrix composites processed by powder metallurgy route was studied by statistical method. During the analysis, a new approach for the estimation...The characterization of reinforcement in 15% SiC particles reinforced AI matrix composites processed by powder metallurgy route was studied by statistical method. During the analysis, a new approach for the estimation of the characterization of reinforcement was presented. The mathematic software MATLAB was used to calculate the area and perimeter of reinforcement, in which the image processing technique was applied. Based on the calculation, the fractal dimension, shape factor, reinforcement size distribution and reinforcement distribution were investigated. The results show that the reinforcement shape is similar to rectangle; the reinforcement size distribution is broad with the＇ range of 1-12 μm; the topography of reinforcement is smooth; and the reinforcement distribution is inhomogeneous. Furthermore, the cell model based on the statistical characterization was established and tested.展开更多
Different proportions of commercial 2024 aluminum alloy powder and FeNiCrCoA13 high entropy alloy （HEA） powder were ball-milled （BM） for different time. The powder was consolidated by hot extrusion method. The mic...Different proportions of commercial 2024 aluminum alloy powder and FeNiCrCoA13 high entropy alloy （HEA） powder were ball-milled （BM） for different time. The powder was consolidated by hot extrusion method. The microstructures of the milled powder and bulk alloy were examined by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. Mechanical properties of the extruded alloy were examined by mechanical testing machine. The results show that after BM, the particle size and microstructures of the mixed alloy powder change obviously. After 48 h BM, the average size of mixed powder is about 30 nm, and then after hot extrusion, the average size of grains reaches about 70 rim. The compressive strength of the extruded alloy reaches 710 MPa under certain conditions of milling time and composition. As a result of the identification of the nano-/micro-strueture-property relationship of the samples, such high strength is attributed mainly to the nanocrystalline grains of a（Al） and nanoscaled FeNiCrCoAl3 particles, and the fine secondary phase of Al2Cu and Fe-rich phases.展开更多
In order to solve the friction,wear and lubrication problems of titanium,a series of TaN/ployether−ether−ketone(PEEK)coatings were developed by electrophoretic deposition,and the effects of TaN nanoparticles on the mi...In order to solve the friction,wear and lubrication problems of titanium,a series of TaN/ployether−ether−ketone(PEEK)coatings were developed by electrophoretic deposition,and the effects of TaN nanoparticles on the microstructure,mechanical properties and tribological performance of coatings were explored.Results manifest that the introduction of TaN nanoparticles into PEEK coatings could improve the deposition efficiency,enhance the resistant deform capacity,increase the hardness,elastic modulus and adhesive bonding strength.Compared with the pure PEEK coating,the friction coefficient of P-TN-3 was greatly reduced by 31.25%.The wear resistance of P-TN-3 was also improved in huge boost,and its specific wear rate was decreased from 9.42×10^(−5) to 1.62×10^(−5) mm^(3)·N^(−1)·m^(−1).The homogeneous composite TaN/PEEK coatings prepared by electrophoretic deposition were well-adhered to the titanium alloy substrate,TaN nanoparticles could improve the strength of PEEK coating,and provide wear-resistance protection for titanium alloys.展开更多
In order to select a suitable material for the rolling mill guide application, the dry sliding friction and wear resistance of a tungsten carbide combining cobalt (WC-Co) particle reinforced chromium cast iron composi...In order to select a suitable material for the rolling mill guide application, the dry sliding friction and wear resistance of a tungsten carbide combining cobalt (WC-Co) particle reinforced chromium cast iron composite material were studied. In particular, the wear resistance was discussed in detail. The results showed that the composite material demonstrates 25 times the wear resistance of high Cr cast iron, and 9 times the wear resistance of heat resistant steel. However, the average friction factor in the stable friction stage showed a relationship of μComposites/45#steel>μHigh chromium cast iron/45#steel>μHeat resistant steel/45 # steel. The wear resistance mechanism of the composite material was associated with the reinforcing particles, which protruded from the worn surface to bear the friction load when the matrix material surface was worn, thereby reducing the abrasive and adhesive wear. In addition, the matrix material possessed suitable hardness and toughness, providing a support to the reinforcements.展开更多
Tungsten(W)particle-reinforced nickel(Ni)-based composites were fabricated via laser-direct energy de-position(L-DED).The influence of the W particle size on the microstructure and mechanical properties of the deposit...Tungsten(W)particle-reinforced nickel(Ni)-based composites were fabricated via laser-direct energy de-position(L-DED).The influence of the W particle size on the microstructure and mechanical properties of the deposited samples was systematically studied.The results indicate that refining the W particle size could refine theγ-Ni grains and subgrains,thin the(Ni,Cr)_(4)W interface layer,and increase the disloca-tion density of the intergranular matrix,thus improving the tensile strength and elongation of the L-DED samples.As W particle size decreased from 75 to 150μm to 6.5-12μm,the tensile strength and elonga-tion of the deposited samples increased by 150 MPa and 2.9 times to 1347.6±15.7 MPa and 17.5±0.4%,respectively.Based on the properties of the interface(Ni,Cr)_(4)W,a load-transfer efficiency factor suitable for this composite was proposed and the load-transfer strengthening formula was optimized.A quanti-tative analysis of the strengthening mechanisms was established considering load-transfer strengthening,Hall-Petch strengthening,thermal-mismatch strengthening,and solid-solution strengthening.The calcu-lated contribution of each strengthening mechanism to the yield strength and theoretical calculations were in good agreement with the experimental data.The article breaks the bottleneck of poor plasticity of W particle-reinforced Ni-based composites prepared by L-DED and provides a theoretical basis for the construction design of W particle-reinforced Ni-based composites with excellent mechanical properties.展开更多
Particulate reinforced metal matrix composite(PR-MMC) has excellent properties such as good wear resistance,corrosion resistance and high temperature properties.Laser cladding is usually used to form PR-MMC on metal s...Particulate reinforced metal matrix composite(PR-MMC) has excellent properties such as good wear resistance,corrosion resistance and high temperature properties.Laser cladding is usually used to form PR-MMC on metal surface with various volume fractions of ceramic particles.Recent literatures showed that laser melting of powder mixture containing carbon and carbide-forming elements,was favorable for the formation of in-situ synthesized carbide particles.In this paper,rare earth oxide(RE2O3) was added into t...展开更多
Higher-order multiscale structures are proposed to predict the effective elastic properties of 3-phase particle reinforced composites by considering the probabilistic spherical particles spatial distribution,the parti...Higher-order multiscale structures are proposed to predict the effective elastic properties of 3-phase particle reinforced composites by considering the probabilistic spherical particles spatial distribution,the particle interactions,and utilizing homogenization with ensemble volume average approach.The matrix material,spherical particles with radius a1,and spherical particles with radius a2,are denoted as the 0th phase,the 1st phase,and the 2nd phase,respectively.Particularly,the two inhomogeneity phases are different particle sizes and the same elastic material properties.Improved higher-order(in ratio of spherical particle sizes to the distance between the centers of spherical particles)bounds on effective elastic properties of 3-phase particle reinforced proposed Formulation II and Formulation I derive composites.As a special case,i.e.,particle size of the 1st phase is the same as that of the 2nd phase,the proposed formulations reduce to 2-phase formulas.Our theoretical predictions demonstrate excellent agreement with selected experimental data.In addition,several numerical examples are presented to demonstrate the competence of the proposed frameworks.展开更多
This article mainly discussed bulk material lHvl^ared by powder metallurgy, and the commercial 2024 aluminum alloy powder and FeNiCrCoA13 high entropy alloy powder （both produced by argon gas atomization process） we...This article mainly discussed bulk material lHvl^ared by powder metallurgy, and the commercial 2024 aluminum alloy powder and FeNiCrCoA13 high entropy alloy powder （both produced by argon gas atomization process） were ball-milled for different hours. The prepared powder was consolidated by hot extrusion method. The microstruetures of the milled powder and bulk alloy were examined by X - Ray Diffraction （XRD）, Scanning Electron Microscopy （SEM） and Transmission Electron Microscopy （TEM）. The thermal stability was tested by differential scanning calorimetry （DSC）. Mechanical properties of the extruded alloy were examined by Vickers hardness tester and mechanical testing machine. The results show that after milling, the mixed particle sizes and microstructures of the alloy powder change obviously. The compressive strength of the extruded alloy has reached 580 MPa under certain conditions of milling time and composition.展开更多
This paper provides a comprehensive review of research progress in particle-reinforced Mg matrix composites prepared via powder metallurgy.The article discusses different strategies,such as micro-sized,nano-sized part...This paper provides a comprehensive review of research progress in particle-reinforced Mg matrix composites prepared via powder metallurgy.The article discusses different strategies,such as micro-sized,nano-sized particles,and multi-particle hybridization,which has been employed to enhance the performance of the composites.In addition,a range of preparation techniques that optimize the dispersion of the reinforcing particles are summarized.The paper also highlights how the different configurations between the reinforcements and matrix alloy impact the composites’performance.Finally,the article outlines the prospects of particles reinforced Mg matrix composites fabricated via powder metallurgy and recommends modification methods that could be explored to further develop these materials for various applications.展开更多
Effects of diffusion welding process parameters on strength of welded joint based on particle reinforced aluminium matrix composite Al 2O 3p /6061Al have been studied through comparing with aluminium matrix allo...Effects of diffusion welding process parameters on strength of welded joint based on particle reinforced aluminium matrix composite Al 2O 3p /6061Al have been studied through comparing with aluminium matrix alloy. The mechanism for loss of joint strength has been analyzed. It should be pointed out that key processing parameters affecting the strength of joint was welding temperature. The high quality joint can be successfully obtained with appropriate diffusion welding parameters.展开更多
The mechanisms of interfacial debonding of particle reinforcedrheological materials are studied. Based on an energy criterion, asimple formula of local critical stress for interfacial debonding isderived and expressed...The mechanisms of interfacial debonding of particle reinforcedrheological materials are studied. Based on an energy criterion, asimple formula of local critical stress for interfacial debonding isderived and expressed in terms of the interfacial energy. Theparticle size effect on interface debond- ing can then be analyzedeasily owing to the fact that critical stress is inverselyproportional to the square root of particle radius. By takingPP/CaCO_3 system as an example, the present energy criterion iscompared with the mechanical debonding criterion, and it is foundthat under the condition that bond strength is equal to matrixstrength and particle radius not over 0.2μm, the mechanicaldebonding cri- terion can be automatically satisfied if the energycirterion is satisfied.展开更多
To obtain the Ti_(p)with different aspect ratios,the Ti_(p)/Mg-5Zn-0.3Ca composite prepared by semi-solid stir casting was subjected to extrusion at 220℃,180℃,and 140℃,respectively.Then,the effect of the Ti_(p)’s ...To obtain the Ti_(p)with different aspect ratios,the Ti_(p)/Mg-5Zn-0.3Ca composite prepared by semi-solid stir casting was subjected to extrusion at 220℃,180℃,and 140℃,respectively.Then,the effect of the Ti_(p)’s aspect ratio on the microstructure,mechanical properties,work hardening and softening behaviors of Ti_(p)/Mg-5Zn-0.3Ca composites was investigated.The results indicated that the Ti_(p)could be elongated obviously after low-temperature extrusion,and the aspect ratio of which would reach to 13.7:1 as the extrusion temperature deceased to 140℃.Then the“Ti/Mg”layer-like structure was formed in the Ti_(p)/Mg-5Zn-0.3Ca composite.Accompanied with the elongation of Ti_(p),the dynamic recrystallized grains and dynamic precipitates were both refined significantly,however,the dynamic recrystallization rate changed a little.The elongated Ti_(p)endowed the Ti_(p)/Mg-5Zn-0.3Ca composites with better matching of strength and toughness without the sacrifice of elongation and bending strain.Both the work hardening rate and softening rate of Ti_(p)/Mg-5Zn-0.3Ca composites increased with the increasing aspect ratio of Ti_(p).The formation of“Ti/Mg”layer-like structure contributed to the redistribution of strain from large aggregations to a network-like distribution,which effectively suppresses the initiation and propagation of micro-cracks,thus enhancing the plasticity of the Ti_(p)/Mg-5Zn-0.3Ca composites.展开更多
A mixture of NiCrSiB alloy powder and tantalum （Ta） powder was used as laser clad material to improve abrasive wear resistance of the Ni-based coating. The microstructure and wear resistance of the coating were inve...A mixture of NiCrSiB alloy powder and tantalum （Ta） powder was used as laser clad material to improve abrasive wear resistance of the Ni-based coating. The microstructure and wear resistance of the coating were investigated. Addition of Ta element works to suppress the growth of coarse M7C3 carbide in the coating, resulting in a decrease in aspect ratio of coarse carbide. In the abrasive wear test, in situ synthesized TaC particles well bond with Ni-based matrix, and are hardly pull out from wear surface. Grooves on the worn surface of NiCrSiB coating are much deeper and sharper than those in the NiCrSiB＋Ta composite coating. Also, a weight loss of the composite coating is much lower than that of the NiCrSiB coating. The wear resistance of the laser clad Ni-based coating is enhanced to a much greater extent through the addition of Ta. This is attributed to the in situ synthesized hard TaC particles of nearly equiaxed shape, the Ni-based matrix strengthened by Ta and the decrease in aspect ratio of the coarse brittle carbides.展开更多
Resin matrix carbon brush composites(RMCBCs)are critical materials for high-powered electric tools.However,effectively improving their wear resistance and heat dissipation remains a challenge.RMCBCs prepared with flak...Resin matrix carbon brush composites(RMCBCs)are critical materials for high-powered electric tools.However,effectively improving their wear resistance and heat dissipation remains a challenge.RMCBCs prepared with flake graphite powders that were evenly loaded with tungsten copper composite powder(RMCBCs-W@Cu)exhibited a low wear rate of 1.63 mm^(3)/h,exhibiting 48.6%reduction in the wear rate relative to RCMBCs without additives(RMCBCs-0).In addition,RMCBCs-W@Cu achieved a low friction coefficient of 0.243 and low electric spark grade.These findings indicate that tungsten copper composite powders provide particle reinforcement and generate a gradation effect for the epoxy resin(i.e.,connecting phase)in RMCBCs,which weakens the wear of RMCBCs caused by fatigue under a cyclic current-carrying wear.展开更多
The fcc structural CoCr2 FeNiTi(0.5) high-entropy alloy(HEA) composite coating with TiN particles reinforced was acquired by laser cladding on the commercial904 L stainless steels.The results show that phase structure...The fcc structural CoCr2 FeNiTi(0.5) high-entropy alloy(HEA) composite coating with TiN particles reinforced was acquired by laser cladding on the commercial904 L stainless steels.The results show that phase structure is mainly composed of fcc solid solution and TiN phases.The coating exhibits excellent structural stability below850℃.The microstructure consists of irregular dendrite and TiN particles.Transmission electron microscopy(TEM) results reveal that the close-packed plane of fcc phase is(111) with interplanar spacing of ~ 0.208 nm.The interface between TiN and fcc matrix is semi-coherent.And the angle of boundary between dendrite and matrix is ~ 65°.The hardness and corrosion resistance of coating have much improvement compared with those of substrate.展开更多
Pure Cu composites reinforced with diamond particles were fabricated by a high pressure and high temperature （HPHT） infiltration technique. Their microstructural evolution and thermal conductivity were presented as ...Pure Cu composites reinforced with diamond particles were fabricated by a high pressure and high temperature （HPHT） infiltration technique. Their microstructural evolution and thermal conductivity were presented as a function of sintering parameters （temperature, pressure, and time）. The improvement in interfacial bonding strength and the maximum thermM conductivity of 750 W/（m.K） were achieved at the optimal sintering parameters of 1200℃, 6 GPa and 10 min. It is found that the thermal conductivity of the composites depends strongly on sintering pressure. When the sintering pressure is above 6 GPa, the diamond skeleton is detected, which greatly contributes to the excellent thermal conductivity.展开更多
Particulate reinforced metallic matrix composites have attracted considerable attention due to their lightweight, high strength, high specific modulus, and good wear resistance. A1/B4C composite strips were produced i...Particulate reinforced metallic matrix composites have attracted considerable attention due to their lightweight, high strength, high specific modulus, and good wear resistance. A1/B4C composite strips were produced in this work by a modified accumulative roll bonding process where the strips were rotated 90° around the normal direction between successive passes. Transmission electron microscopy and X-ray diffraction analyses reveal the development of nanostructures in the Al matrix after seven passes. It is found that the B4C reinforcement distribution in the matrix is improved by progression of the process. Additionally, the tensile yield strength and elongation of the processed materials are increased with the increase of passes.展开更多
The 6351 wrought aluminum alloy and K2TiF6-CaF2-LiCl components were selected as raw materials to fabricate in situ Al3Ti particulate reinforced aluminum alloy at 720℃via direct melt reaction method with electromagne...The 6351 wrought aluminum alloy and K2TiF6-CaF2-LiCl components were selected as raw materials to fabricate in situ Al3Ti particulate reinforced aluminum alloy at 720℃via direct melt reaction method with electromagnetic stirring(EMS).CaF2 and LiCl acted as fluxes to lower the reaction temperature of the system.It is shown that the electromagnetic stirring and fluxes accelerate the emulsion process of K2TiF6.Optical microscopy,scanning electron microscopy,transmission electron microscopy and energy dispersive spectrum were utilized to analyze the microstructure and components of composites.Compared to composites fabricated without EMS and fluxes,the sizes of endogenetic Al3Ti are refined from 10-15μm to 2-4μm,which are often accompanied with silicon element.The morphology of Al3Ti or Al3TiSi0.22 exhibits triangle,quadrilateral and other clumpy patterns. Because of the Ca elements from CaF2,the sizes of Mg2Si decrease from 8-10μm to 1-2μm due to the formation of Ca2Si.展开更多
The key factor in semi-solid metal processing is the solid fraction at the forming temperature because it affects the microstructure and mechanical properties of the thixoformed components. Though an enormous amount o...The key factor in semi-solid metal processing is the solid fraction at the forming temperature because it affects the microstructure and mechanical properties of the thixoformed components. Though an enormous amount of data exists on the solid fraction-temperature re- lationship in A356 alloy, information regarding the solid fraction evolution characteristics of A356-TiB2 composites is scarce. The present article establishes the temperature-solid fraction correlation in A356 alloy and A356-xTiB2 （x = 2.5wt% and 5wt%） composites using dif- ferential thermal analysis （DTA）. The DTA results indicate that the solidification characteristics of the composites exhibited a variation of 2℃ and 3℃ in liquidus temperatures and a variation of 3℃ and 5℃ in solidus temperatures with respect to the base alloy. Moreover, the eutectic growth temperature and the solid fraction（fs） vs. temperature characteristics of the composites were found to be higher than those of the base alloy. The investigation revealed that in-situ formed TiB2 particles in the molten metal introduced more nucleation sites and reduced undercooling.展开更多
基金financial support from the National Natural Science Foundation of China(Nos.52275385,U2167216)Sichuan Province Science and Technology Support Program,China(No.2022YFG0086).
文摘To improve the wettability of hypereutectic Al−60Si alloy and enhance the mechanical properties of the joints,Al−60Si alloy was joined by ultrasonic soldering with Sn-9Zn solder,and a sound joint with in-situ Si particle reinforcement was obtained.The oxide film of Al−60Si alloy at the interface was identified by transmission electron microscopy(TEM)analysis as amorphous Al_(2)O_(3).The oxide of Si particles in the base metal was also alumina.The oxide film of Al−60Si alloy was observed to be removed by ultrasonic vibration instead of holding treatment.Si particle-reinforced joints(35.7 vol.%)were obtained by increasing the ultrasonication time.The maximum shear strength peaked at 99.5 MPa for soldering at 330℃with an ultrasonic vibration time of 50 s.A model of forming of Si particles reinforced joint under the ultrasound was proposed,and ultrasonic vibration was considered to promote the dissolution of Al and migration of Si particles.
文摘The characterization of reinforcement in 15% SiC particles reinforced AI matrix composites processed by powder metallurgy route was studied by statistical method. During the analysis, a new approach for the estimation of the characterization of reinforcement was presented. The mathematic software MATLAB was used to calculate the area and perimeter of reinforcement, in which the image processing technique was applied. Based on the calculation, the fractal dimension, shape factor, reinforcement size distribution and reinforcement distribution were investigated. The results show that the reinforcement shape is similar to rectangle; the reinforcement size distribution is broad with the＇ range of 1-12 μm; the topography of reinforcement is smooth; and the reinforcement distribution is inhomogeneous. Furthermore, the cell model based on the statistical characterization was established and tested.
基金Project(2012CB619503)supported by the Nation Basic Research Program of ChinaProject(2013AA031001)supported by the National High Technology Research and Development Program of ChinaProject(2012DFA50630)supported by the International Science&Technology Cooperation Program of China
文摘Different proportions of commercial 2024 aluminum alloy powder and FeNiCrCoA13 high entropy alloy （HEA） powder were ball-milled （BM） for different time. The powder was consolidated by hot extrusion method. The microstructures of the milled powder and bulk alloy were examined by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. Mechanical properties of the extruded alloy were examined by mechanical testing machine. The results show that after BM, the particle size and microstructures of the mixed alloy powder change obviously. After 48 h BM, the average size of mixed powder is about 30 nm, and then after hot extrusion, the average size of grains reaches about 70 rim. The compressive strength of the extruded alloy reaches 710 MPa under certain conditions of milling time and composition. As a result of the identification of the nano-/micro-strueture-property relationship of the samples, such high strength is attributed mainly to the nanocrystalline grains of a（Al） and nanoscaled FeNiCrCoAl3 particles, and the fine secondary phase of Al2Cu and Fe-rich phases.
基金supported by the National Key Research and Development Program of China (No. 2018YFB2002000)the Guangdong Basic and Applied Basic Research Foundation,China (Nos. 2021A515012271, 2019A1515011220, 2020B1515120027)
文摘In order to solve the friction,wear and lubrication problems of titanium,a series of TaN/ployether−ether−ketone(PEEK)coatings were developed by electrophoretic deposition,and the effects of TaN nanoparticles on the microstructure,mechanical properties and tribological performance of coatings were explored.Results manifest that the introduction of TaN nanoparticles into PEEK coatings could improve the deposition efficiency,enhance the resistant deform capacity,increase the hardness,elastic modulus and adhesive bonding strength.Compared with the pure PEEK coating,the friction coefficient of P-TN-3 was greatly reduced by 31.25%.The wear resistance of P-TN-3 was also improved in huge boost,and its specific wear rate was decreased from 9.42×10^(−5) to 1.62×10^(−5) mm^(3)·N^(−1)·m^(−1).The homogeneous composite TaN/PEEK coatings prepared by electrophoretic deposition were well-adhered to the titanium alloy substrate,TaN nanoparticles could improve the strength of PEEK coating,and provide wear-resistance protection for titanium alloys.
基金supported by the Special Important Technology of Guangdong Province,China(2009A080304010,2011A080802003)the Core Technology Research and Strategic Emerging Industries of Guangdong Province,China(2012A090100018)
文摘In order to select a suitable material for the rolling mill guide application, the dry sliding friction and wear resistance of a tungsten carbide combining cobalt (WC-Co) particle reinforced chromium cast iron composite material were studied. In particular, the wear resistance was discussed in detail. The results showed that the composite material demonstrates 25 times the wear resistance of high Cr cast iron, and 9 times the wear resistance of heat resistant steel. However, the average friction factor in the stable friction stage showed a relationship of μComposites/45#steel>μHigh chromium cast iron/45#steel>μHeat resistant steel/45 # steel. The wear resistance mechanism of the composite material was associated with the reinforcing particles, which protruded from the worn surface to bear the friction load when the matrix material surface was worn, thereby reducing the abrasive and adhesive wear. In addition, the matrix material possessed suitable hardness and toughness, providing a support to the reinforcements.
基金supported by the Key Projects of the National Natural Science Foundation of China(Nos.92066201 and 92266101)the Jiangxi Provincial Key R&D Programme Projects(No.20212BBE51011).
文摘Tungsten(W)particle-reinforced nickel(Ni)-based composites were fabricated via laser-direct energy de-position(L-DED).The influence of the W particle size on the microstructure and mechanical properties of the deposited samples was systematically studied.The results indicate that refining the W particle size could refine theγ-Ni grains and subgrains,thin the(Ni,Cr)_(4)W interface layer,and increase the disloca-tion density of the intergranular matrix,thus improving the tensile strength and elongation of the L-DED samples.As W particle size decreased from 75 to 150μm to 6.5-12μm,the tensile strength and elonga-tion of the deposited samples increased by 150 MPa and 2.9 times to 1347.6±15.7 MPa and 17.5±0.4%,respectively.Based on the properties of the interface(Ni,Cr)_(4)W,a load-transfer efficiency factor suitable for this composite was proposed and the load-transfer strengthening formula was optimized.A quanti-tative analysis of the strengthening mechanisms was established considering load-transfer strengthening,Hall-Petch strengthening,thermal-mismatch strengthening,and solid-solution strengthening.The calcu-lated contribution of each strengthening mechanism to the yield strength and theoretical calculations were in good agreement with the experimental data.The article breaks the bottleneck of poor plasticity of W particle-reinforced Ni-based composites prepared by L-DED and provides a theoretical basis for the construction design of W particle-reinforced Ni-based composites with excellent mechanical properties.
文摘Particulate reinforced metal matrix composite(PR-MMC) has excellent properties such as good wear resistance,corrosion resistance and high temperature properties.Laser cladding is usually used to form PR-MMC on metal surface with various volume fractions of ceramic particles.Recent literatures showed that laser melting of powder mixture containing carbon and carbide-forming elements,was favorable for the formation of in-situ synthesized carbide particles.In this paper,rare earth oxide(RE2O3) was added into t...
基金This work was in part sponsored by the 2015-2016 California State University Long Beach Research,Scholarship and Creative Activity(RSCA)Award。
文摘Higher-order multiscale structures are proposed to predict the effective elastic properties of 3-phase particle reinforced composites by considering the probabilistic spherical particles spatial distribution,the particle interactions,and utilizing homogenization with ensemble volume average approach.The matrix material,spherical particles with radius a1,and spherical particles with radius a2,are denoted as the 0th phase,the 1st phase,and the 2nd phase,respectively.Particularly,the two inhomogeneity phases are different particle sizes and the same elastic material properties.Improved higher-order(in ratio of spherical particle sizes to the distance between the centers of spherical particles)bounds on effective elastic properties of 3-phase particle reinforced proposed Formulation II and Formulation I derive composites.As a special case,i.e.,particle size of the 1st phase is the same as that of the 2nd phase,the proposed formulations reduce to 2-phase formulas.Our theoretical predictions demonstrate excellent agreement with selected experimental data.In addition,several numerical examples are presented to demonstrate the competence of the proposed frameworks.
文摘This article mainly discussed bulk material lHvl^ared by powder metallurgy, and the commercial 2024 aluminum alloy powder and FeNiCrCoA13 high entropy alloy powder （both produced by argon gas atomization process） were ball-milled for different hours. The prepared powder was consolidated by hot extrusion method. The microstruetures of the milled powder and bulk alloy were examined by X - Ray Diffraction （XRD）, Scanning Electron Microscopy （SEM） and Transmission Electron Microscopy （TEM）. The thermal stability was tested by differential scanning calorimetry （DSC）. Mechanical properties of the extruded alloy were examined by Vickers hardness tester and mechanical testing machine. The results show that after milling, the mixed particle sizes and microstructures of the alloy powder change obviously. The compressive strength of the extruded alloy has reached 580 MPa under certain conditions of milling time and composition.
基金supports of the National Natural Science Foundation of China (Nos.U2241231 and 51631006).
文摘This paper provides a comprehensive review of research progress in particle-reinforced Mg matrix composites prepared via powder metallurgy.The article discusses different strategies,such as micro-sized,nano-sized particles,and multi-particle hybridization,which has been employed to enhance the performance of the composites.In addition,a range of preparation techniques that optimize the dispersion of the reinforcing particles are summarized.The paper also highlights how the different configurations between the reinforcements and matrix alloy impact the composites’performance.Finally,the article outlines the prospects of particles reinforced Mg matrix composites fabricated via powder metallurgy and recommends modification methods that could be explored to further develop these materials for various applications.
文摘Effects of diffusion welding process parameters on strength of welded joint based on particle reinforced aluminium matrix composite Al 2O 3p /6061Al have been studied through comparing with aluminium matrix alloy. The mechanism for loss of joint strength has been analyzed. It should be pointed out that key processing parameters affecting the strength of joint was welding temperature. The high quality joint can be successfully obtained with appropriate diffusion welding parameters.
基金the Nationai Natural Science Foundation of China(19632030 and 19872007)Natural Science Foundation of Jiangsu Province
文摘The mechanisms of interfacial debonding of particle reinforcedrheological materials are studied. Based on an energy criterion, asimple formula of local critical stress for interfacial debonding isderived and expressed in terms of the interfacial energy. Theparticle size effect on interface debond- ing can then be analyzedeasily owing to the fact that critical stress is inverselyproportional to the square root of particle radius. By takingPP/CaCO_3 system as an example, the present energy criterion iscompared with the mechanical debonding criterion, and it is foundthat under the condition that bond strength is equal to matrixstrength and particle radius not over 0.2μm, the mechanicaldebonding cri- terion can be automatically satisfied if the energycirterion is satisfied.
基金supported by the“National Natural Science Foundation of China”(Grants.52271109 and 52001223)Support from the“National Key Research and Development Program for Young Scientists”(Grant.2021YFB3703300)+1 种基金the Major Special Plan for Science and Technology in Shanxi Province(202201050201012)the Special Fund Project for Guiding Local Science and Technology Development by the Central Government(Grant.YDZJSX2021B019)。
文摘To obtain the Ti_(p)with different aspect ratios,the Ti_(p)/Mg-5Zn-0.3Ca composite prepared by semi-solid stir casting was subjected to extrusion at 220℃,180℃,and 140℃,respectively.Then,the effect of the Ti_(p)’s aspect ratio on the microstructure,mechanical properties,work hardening and softening behaviors of Ti_(p)/Mg-5Zn-0.3Ca composites was investigated.The results indicated that the Ti_(p)could be elongated obviously after low-temperature extrusion,and the aspect ratio of which would reach to 13.7:1 as the extrusion temperature deceased to 140℃.Then the“Ti/Mg”layer-like structure was formed in the Ti_(p)/Mg-5Zn-0.3Ca composite.Accompanied with the elongation of Ti_(p),the dynamic recrystallized grains and dynamic precipitates were both refined significantly,however,the dynamic recrystallization rate changed a little.The elongated Ti_(p)endowed the Ti_(p)/Mg-5Zn-0.3Ca composites with better matching of strength and toughness without the sacrifice of elongation and bending strain.Both the work hardening rate and softening rate of Ti_(p)/Mg-5Zn-0.3Ca composites increased with the increasing aspect ratio of Ti_(p).The formation of“Ti/Mg”layer-like structure contributed to the redistribution of strain from large aggregations to a network-like distribution,which effectively suppresses the initiation and propagation of micro-cracks,thus enhancing the plasticity of the Ti_(p)/Mg-5Zn-0.3Ca composites.
基金Funded by the National Natural Science Foundation of China(Nos. 50675136 and 50375096)the Scholastic Foundation of Nanchang University (Nos. Z02887 and 06300971)
文摘A mixture of NiCrSiB alloy powder and tantalum （Ta） powder was used as laser clad material to improve abrasive wear resistance of the Ni-based coating. The microstructure and wear resistance of the coating were investigated. Addition of Ta element works to suppress the growth of coarse M7C3 carbide in the coating, resulting in a decrease in aspect ratio of coarse carbide. In the abrasive wear test, in situ synthesized TaC particles well bond with Ni-based matrix, and are hardly pull out from wear surface. Grooves on the worn surface of NiCrSiB coating are much deeper and sharper than those in the NiCrSiB＋Ta composite coating. Also, a weight loss of the composite coating is much lower than that of the NiCrSiB coating. The wear resistance of the laser clad Ni-based coating is enhanced to a much greater extent through the addition of Ta. This is attributed to the in situ synthesized hard TaC particles of nearly equiaxed shape, the Ni-based matrix strengthened by Ta and the decrease in aspect ratio of the coarse brittle carbides.
基金Projects(51772081,51837009,51971091)supported by the National Natural Science Foundation of ChinaProject(HFZL2018CXY003-4)supported by the Industry-University-Research Cooperation of AECC,ChinaProject(kq1902046)supported by the Major Science and Technology Projects of Changsha City,China。
文摘Resin matrix carbon brush composites(RMCBCs)are critical materials for high-powered electric tools.However,effectively improving their wear resistance and heat dissipation remains a challenge.RMCBCs prepared with flake graphite powders that were evenly loaded with tungsten copper composite powder(RMCBCs-W@Cu)exhibited a low wear rate of 1.63 mm^(3)/h,exhibiting 48.6%reduction in the wear rate relative to RCMBCs without additives(RMCBCs-0).In addition,RMCBCs-W@Cu achieved a low friction coefficient of 0.243 and low electric spark grade.These findings indicate that tungsten copper composite powders provide particle reinforcement and generate a gradation effect for the epoxy resin(i.e.,connecting phase)in RMCBCs,which weakens the wear of RMCBCs caused by fatigue under a cyclic current-carrying wear.
基金financially supported by the National Natural Science Foundation of China(No.51671061)the High-Level Innovative Talents Plan of Guizhou Province(No.(2015)4009)the Industrial Research Project of Guizhou Provincial Science and Technology Department(No.(2015)3022)。
文摘The fcc structural CoCr2 FeNiTi(0.5) high-entropy alloy(HEA) composite coating with TiN particles reinforced was acquired by laser cladding on the commercial904 L stainless steels.The results show that phase structure is mainly composed of fcc solid solution and TiN phases.The coating exhibits excellent structural stability below850℃.The microstructure consists of irregular dendrite and TiN particles.Transmission electron microscopy(TEM) results reveal that the close-packed plane of fcc phase is(111) with interplanar spacing of ~ 0.208 nm.The interface between TiN and fcc matrix is semi-coherent.And the angle of boundary between dendrite and matrix is ~ 65°.The hardness and corrosion resistance of coating have much improvement compared with those of substrate.
基金supported by the National Natural Science Foundation of China (No. 50971020)the National High-Tech Research and Development Program of China (No. 2008AA03Z505)
文摘Pure Cu composites reinforced with diamond particles were fabricated by a high pressure and high temperature （HPHT） infiltration technique. Their microstructural evolution and thermal conductivity were presented as a function of sintering parameters （temperature, pressure, and time）. The improvement in interfacial bonding strength and the maximum thermM conductivity of 750 W/（m.K） were achieved at the optimal sintering parameters of 1200℃, 6 GPa and 10 min. It is found that the thermal conductivity of the composites depends strongly on sintering pressure. When the sintering pressure is above 6 GPa, the diamond skeleton is detected, which greatly contributes to the excellent thermal conductivity.
文摘Particulate reinforced metallic matrix composites have attracted considerable attention due to their lightweight, high strength, high specific modulus, and good wear resistance. A1/B4C composite strips were produced in this work by a modified accumulative roll bonding process where the strips were rotated 90° around the normal direction between successive passes. Transmission electron microscopy and X-ray diffraction analyses reveal the development of nanostructures in the Al matrix after seven passes. It is found that the B4C reinforcement distribution in the matrix is improved by progression of the process. Additionally, the tensile yield strength and elongation of the processed materials are increased with the increase of passes.
基金Project(2007AA03Z548)supported by the National High-Tech Research and Development Program of ChinaProject(207038)supported by the Key Program of Ministry of Education of China+3 种基金Project(06-D-021)supported by the Talents Peak in Six Key Fields of Jiangsu Province in ChinaProject(07JDG084)supported by the Technical Enablement Foundation for the Super Special Talents of Jiangsu UniversityProject(20071108)supported by the Technical Enablement Foundation of Ministry of Education for the Returned ScholarsProject(20060299006)supported by the PhD Programs Foundation of Ministry of Education of China
文摘The 6351 wrought aluminum alloy and K2TiF6-CaF2-LiCl components were selected as raw materials to fabricate in situ Al3Ti particulate reinforced aluminum alloy at 720℃via direct melt reaction method with electromagnetic stirring(EMS).CaF2 and LiCl acted as fluxes to lower the reaction temperature of the system.It is shown that the electromagnetic stirring and fluxes accelerate the emulsion process of K2TiF6.Optical microscopy,scanning electron microscopy,transmission electron microscopy and energy dispersive spectrum were utilized to analyze the microstructure and components of composites.Compared to composites fabricated without EMS and fluxes,the sizes of endogenetic Al3Ti are refined from 10-15μm to 2-4μm,which are often accompanied with silicon element.The morphology of Al3Ti or Al3TiSi0.22 exhibits triangle,quadrilateral and other clumpy patterns. Because of the Ca elements from CaF2,the sizes of Mg2Si decrease from 8-10μm to 1-2μm due to the formation of Ca2Si.
基金financial support from the Indian Institute of Technology Bhubaneswar under the SEED project grant for fabricating the "cooling slope casting" experimental setupthe support extended by Central Research Facility (CRF), Indian Institute of Technology Kharagpur, toward the facility for conducting DTA experiments
文摘The key factor in semi-solid metal processing is the solid fraction at the forming temperature because it affects the microstructure and mechanical properties of the thixoformed components. Though an enormous amount of data exists on the solid fraction-temperature re- lationship in A356 alloy, information regarding the solid fraction evolution characteristics of A356-TiB2 composites is scarce. The present article establishes the temperature-solid fraction correlation in A356 alloy and A356-xTiB2 （x = 2.5wt% and 5wt%） composites using dif- ferential thermal analysis （DTA）. The DTA results indicate that the solidification characteristics of the composites exhibited a variation of 2℃ and 3℃ in liquidus temperatures and a variation of 3℃ and 5℃ in solidus temperatures with respect to the base alloy. Moreover, the eutectic growth temperature and the solid fraction（fs） vs. temperature characteristics of the composites were found to be higher than those of the base alloy. The investigation revealed that in-situ formed TiB2 particles in the molten metal introduced more nucleation sites and reduced undercooling.