Polyvinylidene fluoride/lead zirconate titanate(PVDF/PZT)composite films have been prepared by direct ink writing and the effect of PZT content on crystallization behavior and electrical properties of film were system...Polyvinylidene fluoride/lead zirconate titanate(PVDF/PZT)composite films have been prepared by direct ink writing and the effect of PZT content on crystallization behavior and electrical properties of film were systematically investigated.The composite films were characterized by scanning electron microscope(SEM),X-ray diffractometer(XRD),Flourier transform infrared spectroscope(FTIR)and differential scanning calorimeter(DSC).The results show that,surface modified PZT powder(PZT@PDA)is successfully coated by polydopamine(PDA),resulting in a large number of polar groups that interact with the-CF_(2)-groups in PVDF,inducing the generation of polarβphase due to hydrogen bonding formed in the interaction.Theβphase content in composite film increases with increasing PZT@PDA content,up to 28.09%as with 5 wt.%PZT@PDA.PZT@PDA plays a role of nucleating agent to promote the generation of polar phases in the film and also acts as an impurity hindering the growth of nuclei to reduce crystallinity.Moreover,the presence of PZT@PDA in interfaces provides more sites for the occurrence of interfacial polarization and thus improving the electrical properties of films.The composite film with 5 wt.%PZT@PDA possesses the highest dielectric constant(8.61)and residual polarization value(0.6803μC/cm^(2)).展开更多
Polyvinylidene fluoride(PVDF)/garnet composite polymer electrolytes(CPEs) have shown great potential in the development of solid-state lithium metal batteries(SSLMBs) due to their excellent flexibility, high ionic con...Polyvinylidene fluoride(PVDF)/garnet composite polymer electrolytes(CPEs) have shown great potential in the development of solid-state lithium metal batteries(SSLMBs) due to their excellent flexibility, high ionic conductivity and superior mechanical strength.However, uneven dispersion of garnet fillers in CPEs would lead to deterioration of lithium metal batteries(LMBs) performance and severely limit their widespread application. Considering the rapidly growing research of addressing above-mentioned issue, herein, recent progress in the design and fabrication of uniformly dispersed fillers in PVDF/garnet CPEs for high-performance SSLMBs is summarized. We firstly analyze the mechanism for the aggregation of inorganic fillers, and provide a detailed introduction to the strategies for solving the uneven dispersion of nanoparticles in solid electrolytes. Moreover, we also comprehensively summarize their applications in PVDF/garnet electrolytes and their impact on the electrochemical performance of SSLMBs. Finally, the application challenges and future prospects of PVDF/garnet CPEs in SSLMBs were also proposed to promote their further development. It is anticipated that this review could inspire ongoing research interest in rational designing and fabricating novel CPEs for high-performance SSLMBs.展开更多
A new three-phase PZT C/PVC composite comprising PZT（50 vol%）,nanocrystalline PVC （50 vol%） and a small volume fraction f of black（C0was prepared by the hot-pressing technique.The dielectric property of the comp...A new three-phase PZT C/PVC composite comprising PZT（50 vol%）,nanocrystalline PVC （50 vol%） and a small volume fraction f of black（C0was prepared by the hot-pressing technique.The dielectric property of the composite as α function of the frequency and the dielectric and piezoelectric properties as α function of the volume fraction f of C were studied.The measured dielectric property demonstrates that α percolation transition occurs in the three-phase composites as in normal two-phase metal-insulator continuum media.The dielectric constant varies slightly with f at f〈0.1 and increases rapidly when f is close to the percolation threshold at 1kHz.The optimum properties were obtained for f=0.5 before the percolation threshold in the PZT/C/PVC（50/f/（50-f）vol%）composite with its d33（20pC/N） being 50% higher than that of the PZT/PVC（50/50vol%）,and its g33（47.23×10^-3Vm/N）and Kp（0.25） much higher than the earlier reported values,XRD patterns and P-E hysteresis loops were used to interpret the experimental results.展开更多
To get a dielectric material with a high dielectric permittivity and suppressed dielectric loss,nano-Ag with a particle size of 20 nm and Ag@TiO_(2)core-shell particles with diameters of approximately 70-120 nm were e...To get a dielectric material with a high dielectric permittivity and suppressed dielectric loss,nano-Ag with a particle size of 20 nm and Ag@TiO_(2)core-shell particles with diameters of approximately 70-120 nm were embedded in polyvinylidene fluoride(PVDF)to fabricate nano-Ag/Ag@TiO_(2)/PVDF composites.After being modified by nano-Ag with 3 vol%optimal amount,the relative permittivity(ε_r)at 100 Hz of 50 vol%Ag@TiO_(2)/PVDF composites was 61,and the dielectric loss can be suppressed to 0.04,almost 96.4%lower than that of unmodified composites,and a higher frequency stability of bothε_r and loss has also been found.The underlying mechanism of the reduced loss was attributed to Maxwell-Wagner polarization and the Coulomb blockade effect caused by the introduction of a small amount of nano-Ag,which will block the movement of electrons between metal nanoparticles and composites.The space charge polarization and conductance loss are weakened at lower and higher Ag@TiO_(2)filling ratios,respectively,thus leading to a very low loss of the composites.展开更多
基金Project(22020JJ4729)supported by the Natural Science Foundation of Hunan Province,China。
文摘Polyvinylidene fluoride/lead zirconate titanate(PVDF/PZT)composite films have been prepared by direct ink writing and the effect of PZT content on crystallization behavior and electrical properties of film were systematically investigated.The composite films were characterized by scanning electron microscope(SEM),X-ray diffractometer(XRD),Flourier transform infrared spectroscope(FTIR)and differential scanning calorimeter(DSC).The results show that,surface modified PZT powder(PZT@PDA)is successfully coated by polydopamine(PDA),resulting in a large number of polar groups that interact with the-CF_(2)-groups in PVDF,inducing the generation of polarβphase due to hydrogen bonding formed in the interaction.Theβphase content in composite film increases with increasing PZT@PDA content,up to 28.09%as with 5 wt.%PZT@PDA.PZT@PDA plays a role of nucleating agent to promote the generation of polar phases in the film and also acts as an impurity hindering the growth of nuclei to reduce crystallinity.Moreover,the presence of PZT@PDA in interfaces provides more sites for the occurrence of interfacial polarization and thus improving the electrical properties of films.The composite film with 5 wt.%PZT@PDA possesses the highest dielectric constant(8.61)and residual polarization value(0.6803μC/cm^(2)).
基金financially supported by the National Key Research and Development Program of China(No.2020YFB1713500)the Natural Science Foundation of Henan Province(No.242300420021)Open Fund of State Key Laboratory of Advanced Refractories(No.SKLAR202210)
文摘Polyvinylidene fluoride(PVDF)/garnet composite polymer electrolytes(CPEs) have shown great potential in the development of solid-state lithium metal batteries(SSLMBs) due to their excellent flexibility, high ionic conductivity and superior mechanical strength.However, uneven dispersion of garnet fillers in CPEs would lead to deterioration of lithium metal batteries(LMBs) performance and severely limit their widespread application. Considering the rapidly growing research of addressing above-mentioned issue, herein, recent progress in the design and fabrication of uniformly dispersed fillers in PVDF/garnet CPEs for high-performance SSLMBs is summarized. We firstly analyze the mechanism for the aggregation of inorganic fillers, and provide a detailed introduction to the strategies for solving the uneven dispersion of nanoparticles in solid electrolytes. Moreover, we also comprehensively summarize their applications in PVDF/garnet electrolytes and their impact on the electrochemical performance of SSLMBs. Finally, the application challenges and future prospects of PVDF/garnet CPEs in SSLMBs were also proposed to promote their further development. It is anticipated that this review could inspire ongoing research interest in rational designing and fabricating novel CPEs for high-performance SSLMBs.
文摘A new three-phase PZT C/PVC composite comprising PZT（50 vol%）,nanocrystalline PVC （50 vol%） and a small volume fraction f of black（C0was prepared by the hot-pressing technique.The dielectric property of the composite as α function of the frequency and the dielectric and piezoelectric properties as α function of the volume fraction f of C were studied.The measured dielectric property demonstrates that α percolation transition occurs in the three-phase composites as in normal two-phase metal-insulator continuum media.The dielectric constant varies slightly with f at f〈0.1 and increases rapidly when f is close to the percolation threshold at 1kHz.The optimum properties were obtained for f=0.5 before the percolation threshold in the PZT/C/PVC（50/f/（50-f）vol%）composite with its d33（20pC/N） being 50% higher than that of the PZT/PVC（50/50vol%）,and its g33（47.23×10^-3Vm/N）and Kp（0.25） much higher than the earlier reported values,XRD patterns and P-E hysteresis loops were used to interpret the experimental results.
基金Funded by the National Natural Science Foundation of China(No.51772107)the Fundamental Research Funds for the Central Universities(No.2017KFYXJJ022)。
文摘To get a dielectric material with a high dielectric permittivity and suppressed dielectric loss,nano-Ag with a particle size of 20 nm and Ag@TiO_(2)core-shell particles with diameters of approximately 70-120 nm were embedded in polyvinylidene fluoride(PVDF)to fabricate nano-Ag/Ag@TiO_(2)/PVDF composites.After being modified by nano-Ag with 3 vol%optimal amount,the relative permittivity(ε_r)at 100 Hz of 50 vol%Ag@TiO_(2)/PVDF composites was 61,and the dielectric loss can be suppressed to 0.04,almost 96.4%lower than that of unmodified composites,and a higher frequency stability of bothε_r and loss has also been found.The underlying mechanism of the reduced loss was attributed to Maxwell-Wagner polarization and the Coulomb blockade effect caused by the introduction of a small amount of nano-Ag,which will block the movement of electrons between metal nanoparticles and composites.The space charge polarization and conductance loss are weakened at lower and higher Ag@TiO_(2)filling ratios,respectively,thus leading to a very low loss of the composites.