高性能复合镀层具有优良的耐磨、耐蚀性能,能满足工业生产对材料性能的要求。研究了脉冲电沉积RE Ni W B PTFE Al2O3 复合镀层的成分、形貌及性能。结果表明:脉冲电流及Al2O3 固体颗粒能明显提高RE Ni W B PTFE Al2O3 复合镀层中W和B的...高性能复合镀层具有优良的耐磨、耐蚀性能,能满足工业生产对材料性能的要求。研究了脉冲电沉积RE Ni W B PTFE Al2O3 复合镀层的成分、形貌及性能。结果表明:脉冲电流及Al2O3 固体颗粒能明显提高RE Ni W B PTFE Al2O3 复合镀层中W和B的含量;与直流电沉积相比,脉冲电沉积RE Ni W B复合镀层的表面裂纹已明显减小,但裂纹仍存在,当Al2O3 耐磨颗粒及PTFE减摩微粒嵌入RE Ni W B复合镀层中以后,在SEM 400倍下观察,RE Ni W B PTFE Al2O3镀层已不存在裂纹, 而且镀液中Al2O3 颗粒含量越多,晶粒就越细;此外,研究表明,镀液中Al2O3 颗粒含量增加, RE Ni W B PTFE Al2O3 复合镀层镀态硬度增加,磨损率降低。展开更多
A ternary system of PTFE/Al/Bi_(2)O_(3)is constructed by incorporating PTFE-based reactive material and thermite for enhancing the energy release of the PTFE-based reactive material.The effects of Bi_(2)O_(3)in the PT...A ternary system of PTFE/Al/Bi_(2)O_(3)is constructed by incorporating PTFE-based reactive material and thermite for enhancing the energy release of the PTFE-based reactive material.The effects of Bi_(2)O_(3)in the PTFE/Al/Bi_(2)O_(3)on both mechanical properties and the energy release were investigated through various tests such as thermogravimetry-differential scanning calorimetry,adiabatic oxygen bomb test and split Hopkinson pressure bar test.The microstructure observed through scanning electron microscope and Xray diffraction results are used to analyze the ignition and reaction mechanism of PTFE/Al/Bi_(2)O_(3).The results indicate that the PTFE/Al/Bi_(2)O_(3)are capable of triggering the exothermic reaction of molten PTFE/Bi_(2)O_(3)and Al/Bi_(2)O_(3)over the PTFE/Al reactive materials,thereby promoting reactions.The excessive aluminum in the ternary system is beneficial for increasing energy release.The ignition of shock-induced chemical reactions in PTFE/Al/Bi_(2)O_(3)is closely related to the material fracture.The dominant mechanism for hot-spot generation under Split Hopkinson Pressure Bar test is the frictional temperature rise at the microcrack after failure.展开更多
文摘高性能复合镀层具有优良的耐磨、耐蚀性能,能满足工业生产对材料性能的要求。研究了脉冲电沉积RE Ni W B PTFE Al2O3 复合镀层的成分、形貌及性能。结果表明:脉冲电流及Al2O3 固体颗粒能明显提高RE Ni W B PTFE Al2O3 复合镀层中W和B的含量;与直流电沉积相比,脉冲电沉积RE Ni W B复合镀层的表面裂纹已明显减小,但裂纹仍存在,当Al2O3 耐磨颗粒及PTFE减摩微粒嵌入RE Ni W B复合镀层中以后,在SEM 400倍下观察,RE Ni W B PTFE Al2O3镀层已不存在裂纹, 而且镀液中Al2O3 颗粒含量越多,晶粒就越细;此外,研究表明,镀液中Al2O3 颗粒含量增加, RE Ni W B PTFE Al2O3 复合镀层镀态硬度增加,磨损率降低。
基金the National Natural Science Foundation of China (Grant No.12002045)State Key Laboratory of Explosion Science and Technology,Beijing Institute of Technology (Grant No.QNKT22-09)。
文摘A ternary system of PTFE/Al/Bi_(2)O_(3)is constructed by incorporating PTFE-based reactive material and thermite for enhancing the energy release of the PTFE-based reactive material.The effects of Bi_(2)O_(3)in the PTFE/Al/Bi_(2)O_(3)on both mechanical properties and the energy release were investigated through various tests such as thermogravimetry-differential scanning calorimetry,adiabatic oxygen bomb test and split Hopkinson pressure bar test.The microstructure observed through scanning electron microscope and Xray diffraction results are used to analyze the ignition and reaction mechanism of PTFE/Al/Bi_(2)O_(3).The results indicate that the PTFE/Al/Bi_(2)O_(3)are capable of triggering the exothermic reaction of molten PTFE/Bi_(2)O_(3)and Al/Bi_(2)O_(3)over the PTFE/Al reactive materials,thereby promoting reactions.The excessive aluminum in the ternary system is beneficial for increasing energy release.The ignition of shock-induced chemical reactions in PTFE/Al/Bi_(2)O_(3)is closely related to the material fracture.The dominant mechanism for hot-spot generation under Split Hopkinson Pressure Bar test is the frictional temperature rise at the microcrack after failure.