The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel...The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel 45 was used as a reference material. Experimentalresults showed that the abrasive wear resistance of Al_2O_3/PA1010 composite coatings has a goodlinear relationship with the volume fraction of Al_2O_3 particles in Al_2O_3/PA1010 compositecoatings, and the linear correlative coefficient is 0.979. Under the experimental conditions, thesize of Al_2O_3 particles (40.5-161.0 μm) has little influence on the abrasive wear resistance ofAl_2O_3/PA1010 composite coatings. By treating the surface of Al_2O_3 particles with a suitablebonding agent, the distribution of Al_2O_3 particles in matrix PA1010 is more homogeneous and thebonding state between Al_2O_3 particles and matrix PA1010 is better. Therefore, the Al_2O_3particles in Al_2O_3/PA1010 composite coatings make the Al_2O_3/PA1010 composite coatings havebetter abrasive wear resistance than PA1010 coatings. The wear resistance of Al_2O_3/PA1010composite coatings is about 45% compared with that of steel 45.展开更多
Many steel components are needed to be reinforced on their surface to have a high abrasive resistance and corrosion resistance. Based on self-propagating hightemperature synthesis, a process to making Al2O3 composite ...Many steel components are needed to be reinforced on their surface to have a high abrasive resistance and corrosion resistance. Based on self-propagating hightemperature synthesis, a process to making Al2O3 composite coatings on mild steel substrate in atmospheric environment with the help of simple auxiliary facilities was developed successfully. A pre-coated bilayer coating was employed. The effects of Fe content in pre-coated transition layer on phase composition, porosity and interfacial bon ding were studied using scanning electron microscopy (SEM), energy-dispersive spectrum (EDS) and X-ray diffraction (XRD). The thermal shock resistance and abrasive resistance were investigated. When Fe content changes from 0 wt% to 50 wt%, the bond quality at first becomes better and then worse gradually. When Fe content is less 20 wt%, there is a small gap between the transition layer and the substrate;when Fe contents are 30 wt% and 40 wt%, working layer, the transition layer and the substrate bond together well. The working layer is mainly composed of Al2O3, Fe-Cr and Al(Cr)2O3 phases and has a dense structure with porosity of less than 1 %. The coating has a good thermal shock resistance and abrasive resistance. The abrasive resistance of the working layer is about ten times that of the substrate.展开更多
The friction and wear behavior of magnesium matrix composites reinforced with particulate Mg2Si was characterized. The influence of Si, applied load and sliding rate on the wear behavior of Mg2Si/AM60 magnesium matrix...The friction and wear behavior of magnesium matrix composites reinforced with particulate Mg2Si was characterized. The influence of Si, applied load and sliding rate on the wear behavior of Mg2Si/AM60 magnesium matrix composites was studied. The results indicate that the particulate Mg2Si can be synthesized by adding Si into magnesium alloy. The wear properties of AM60 magnesium alloy are significantly improved with MgzSi particles. The wear mass losses of AM60 magnesium alloy and MgaSi/AM60 magnesium matrix composites decrease with increase in applied load and sliding rate. The wear feature of the AM60 magnesium alloy is adhesion wear. The wear mechanism of Mg2Si/AM60 magnesium matrix composites transforms from abrasive wear to adhesion wear with the increase of load.展开更多
文摘The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel 45 was used as a reference material. Experimentalresults showed that the abrasive wear resistance of Al_2O_3/PA1010 composite coatings has a goodlinear relationship with the volume fraction of Al_2O_3 particles in Al_2O_3/PA1010 compositecoatings, and the linear correlative coefficient is 0.979. Under the experimental conditions, thesize of Al_2O_3 particles (40.5-161.0 μm) has little influence on the abrasive wear resistance ofAl_2O_3/PA1010 composite coatings. By treating the surface of Al_2O_3 particles with a suitablebonding agent, the distribution of Al_2O_3 particles in matrix PA1010 is more homogeneous and thebonding state between Al_2O_3 particles and matrix PA1010 is better. Therefore, the Al_2O_3particles in Al_2O_3/PA1010 composite coatings make the Al_2O_3/PA1010 composite coatings havebetter abrasive wear resistance than PA1010 coatings. The wear resistance of Al_2O_3/PA1010composite coatings is about 45% compared with that of steel 45.
基金financially supported by the National Natural Science Foundation of China (No.51379070)the Fundamental Research Funds for the Central Universities (No. 2017B40314)
文摘Many steel components are needed to be reinforced on their surface to have a high abrasive resistance and corrosion resistance. Based on self-propagating hightemperature synthesis, a process to making Al2O3 composite coatings on mild steel substrate in atmospheric environment with the help of simple auxiliary facilities was developed successfully. A pre-coated bilayer coating was employed. The effects of Fe content in pre-coated transition layer on phase composition, porosity and interfacial bon ding were studied using scanning electron microscopy (SEM), energy-dispersive spectrum (EDS) and X-ray diffraction (XRD). The thermal shock resistance and abrasive resistance were investigated. When Fe content changes from 0 wt% to 50 wt%, the bond quality at first becomes better and then worse gradually. When Fe content is less 20 wt%, there is a small gap between the transition layer and the substrate;when Fe contents are 30 wt% and 40 wt%, working layer, the transition layer and the substrate bond together well. The working layer is mainly composed of Al2O3, Fe-Cr and Al(Cr)2O3 phases and has a dense structure with porosity of less than 1 %. The coating has a good thermal shock resistance and abrasive resistance. The abrasive resistance of the working layer is about ten times that of the substrate.
基金Project supported by the Key Laboratory of Ministry of Education for Conveyance and Equipment (East China Jiaotong University), ChinaProject (GJJ11094) supported by Science Funds of Jiangxi Provincial Education Project on Department, China
文摘The friction and wear behavior of magnesium matrix composites reinforced with particulate Mg2Si was characterized. The influence of Si, applied load and sliding rate on the wear behavior of Mg2Si/AM60 magnesium matrix composites was studied. The results indicate that the particulate Mg2Si can be synthesized by adding Si into magnesium alloy. The wear properties of AM60 magnesium alloy are significantly improved with MgzSi particles. The wear mass losses of AM60 magnesium alloy and MgaSi/AM60 magnesium matrix composites decrease with increase in applied load and sliding rate. The wear feature of the AM60 magnesium alloy is adhesion wear. The wear mechanism of Mg2Si/AM60 magnesium matrix composites transforms from abrasive wear to adhesion wear with the increase of load.