Blends of PC and PPSQ (A) with high M-w and good ladderlike regularity or PPSQ(B) with low M-w and more defective Si-atoms in its structure have been prepared by solution casting. The dispersed spheres (PPSQ(A)-rich) ...Blends of PC and PPSQ (A) with high M-w and good ladderlike regularity or PPSQ(B) with low M-w and more defective Si-atoms in its structure have been prepared by solution casting. The dispersed spheres (PPSQ(A)-rich) are unevenly dispersed in the continuous PC-rich phase and there is no phase-inversion as PPSQ(A) content increases when the percentage of PPSQ(A) is not more than 70%. PPSQ(B)-rich spheres are evenly dispersed in the continuous phase (PC-rich) and phase-inversion occurs when PPSQ(B) percentage is up to 70%. T-g of PPSQ(A)/PC or PPSQ(B)/PC at some compositions are lower than that of pure PC due to the enlarged free-volume of PC-rich phase because some spheres of rigid PPSQ chains are included in the PC-rich phase. PC and PPSQ(A) or PPSQ(B) are partially compatible. The compatibility of PC and PPSQ(B) is better than that of PC and PPSQ(A) with high M-w and good ladderlike regularity. Heat history has some influence on the T(g)s and compatibility of PPSQ(A)/PC and PPSQ(B)/PC blends.展开更多
基金This work was supported by Fund of Head of College of Chemistry,Shandong University.
文摘Blends of PC and PPSQ (A) with high M-w and good ladderlike regularity or PPSQ(B) with low M-w and more defective Si-atoms in its structure have been prepared by solution casting. The dispersed spheres (PPSQ(A)-rich) are unevenly dispersed in the continuous PC-rich phase and there is no phase-inversion as PPSQ(A) content increases when the percentage of PPSQ(A) is not more than 70%. PPSQ(B)-rich spheres are evenly dispersed in the continuous phase (PC-rich) and phase-inversion occurs when PPSQ(B) percentage is up to 70%. T-g of PPSQ(A)/PC or PPSQ(B)/PC at some compositions are lower than that of pure PC due to the enlarged free-volume of PC-rich phase because some spheres of rigid PPSQ chains are included in the PC-rich phase. PC and PPSQ(A) or PPSQ(B) are partially compatible. The compatibility of PC and PPSQ(B) is better than that of PC and PPSQ(A) with high M-w and good ladderlike regularity. Heat history has some influence on the T(g)s and compatibility of PPSQ(A)/PC and PPSQ(B)/PC blends.