Titanium dioxide nano filler(TiO2)with(10 nm)particle size,and(0.5 wt%)was used as a dopant to epoxy type(SR8100),polymer matrix nanocomposite(PMNC)was prepared by hot vibration dispersion,and tested using FTIR,and UV...Titanium dioxide nano filler(TiO2)with(10 nm)particle size,and(0.5 wt%)was used as a dopant to epoxy type(SR8100),polymer matrix nanocomposite(PMNC)was prepared by hot vibration dispersion,and tested using FTIR,and UV spectra.It has been found that transmission of(PMNC)largely enhanced,and absorption of UV radiation reaches up to(52%)at(500 nm),(50%)at(1000 nm),and never drop to zero.展开更多
The effects of 1,2,3,4,and 5wt%of TiO_(2) disperse nanofiller on mechanical properties of polyamide hexaglycol(PAHG)were investigated.Specimen was prepared by the hot vibration dispersion technique to make a PMNC.Hard...The effects of 1,2,3,4,and 5wt%of TiO_(2) disperse nanofiller on mechanical properties of polyamide hexaglycol(PAHG)were investigated.Specimen was prepared by the hot vibration dispersion technique to make a PMNC.Hardness,tensile strength,ultimate tensile strength,young modulus,and impact at room temperature were tested.It has been found that enhancement in these properties starts at extra low weight percent(1wt%)nTiO_(2).The maximum effect of nano TiO_(2) addition was on tensile strength,and the lowest was on young modulus.展开更多
文摘Titanium dioxide nano filler(TiO2)with(10 nm)particle size,and(0.5 wt%)was used as a dopant to epoxy type(SR8100),polymer matrix nanocomposite(PMNC)was prepared by hot vibration dispersion,and tested using FTIR,and UV spectra.It has been found that transmission of(PMNC)largely enhanced,and absorption of UV radiation reaches up to(52%)at(500 nm),(50%)at(1000 nm),and never drop to zero.
文摘The effects of 1,2,3,4,and 5wt%of TiO_(2) disperse nanofiller on mechanical properties of polyamide hexaglycol(PAHG)were investigated.Specimen was prepared by the hot vibration dispersion technique to make a PMNC.Hardness,tensile strength,ultimate tensile strength,young modulus,and impact at room temperature were tested.It has been found that enhancement in these properties starts at extra low weight percent(1wt%)nTiO_(2).The maximum effect of nano TiO_(2) addition was on tensile strength,and the lowest was on young modulus.