The development of magnetic heterostructures with strong perpendicular magnetic anisotropy(PMA),strong spin-orbit torques(SOTs),low impedance,and good integration compatibility at the same time is central for high-per...The development of magnetic heterostructures with strong perpendicular magnetic anisotropy(PMA),strong spin-orbit torques(SOTs),low impedance,and good integration compatibility at the same time is central for high-performance spintronic memory and computing applications.Here,we report the development of the PMA superlattice[Pt/Co/W]_(n)that can be sputtered-deposited on commercial oxidized silicon substrates and has giant SOTs,strong uniaxial PMA of≈9.2 Merg/cm^(3),and rigid macrospin performance.The damping-like and field-like SOTs of the[Pt/Co/W]_(n)superlattices exhibit a linear increase with the repeat number n and reach the giant values of 225%and-33%(two orders of magnitude greater than that in clean-limit Pt)at n=12,respectively.The damping-like SOT is also of the opposite sign and much greater in magnitude than the field-like SOT,regardless of the number n.These results clarify that the spin current that generates SOTs in the[Pt/Co/W]_(n)superlattices arises predominantly from the spin Hall effect rather than bulk Rashba spin splitting,providing a unified understanding of the SOTs in these superlattices.We also demonstrate deterministic switching in thickerthan-50-nm PMA[Pt/Co/W]_(12)superlattices at a low current density.This work establishes the[Pt/Co/W]_(n)superlattice as a compelling material candidate for ultra-fast,low-power,long-retention nonvolatile spintronic memory and computing technologies.展开更多
Pd/Co_(2)MnSi(CMS)/Co/Pd multilayer films were designed based on the idea of combining highly spin-polarized materials with strong perpendicular magnetic anisotropy(PMA)films.The PMA of Pd/CMS/Co/Pd multilayer films w...Pd/Co_(2)MnSi(CMS)/Co/Pd multilayer films were designed based on the idea of combining highly spin-polarized materials with strong perpendicular magnetic anisotropy(PMA)films.The PMA of Pd/CMS/Co/Pd multilayer films was studied by optimizing the growth conditions and thickness of each film layer.The optimal structure of the multilayer films was Pd(6 nm)/CMS(5 nm)/Co(2 nm)/Pd(1 nm).Its abnormal Hall resistance(R_(Hall)),coercivity(H_(c))and effective magnetic anisotropy constant(Keff)are 0.08Ω,284 Oe and 1.36 Merg/cm^(3),respectively,which are 100%,492%,and 183%higher than the corresponding values(0.04Ω,48 Oe,and 0.48 Merg/cm^(3))of the Pd(6 nm)/Co(1 nm)/Pd(3 nm)trilayer films.The analysis shows that the increases of the above values are the result of the Pd/CMS interface effect and CMS/Co interface ferromagnetic(FM)coupling,and that it is closely related to the thickness of each film layer in the multilayer films and the growth conditions of the multilayer films.展开更多
在9%(w/v)NaCl条件下,通过温度、pH两种因素诱导一株单增李斯特菌进入"活的非可培养"(viable but non-cuturable,VBNC)状态。通过LIVE/DEAD Baclight活菌检测试剂盒检测细菌总数与活菌数,比较单增李斯特菌状态及数量的差异与...在9%(w/v)NaCl条件下,通过温度、pH两种因素诱导一株单增李斯特菌进入"活的非可培养"(viable but non-cuturable,VBNC)状态。通过LIVE/DEAD Baclight活菌检测试剂盒检测细菌总数与活菌数,比较单增李斯特菌状态及数量的差异与变化。结果显示,在2℃、pH6.0条件下单增李斯特菌活菌全部进入VBNC状态。用PMA-qPCR对经诱导的四份菌液进行检测,结果表明该方法能快速、准确地测出死菌背景下的活的单增李斯特菌。展开更多
基金supported by the National Key Research and Development Program of China(Grant No.2022YFA1204000)the Beijing National Natural Science Foundation(Grant No.Z230006)the National Natural Science Foundation of China(Grant Nos.12304155 and 12274405).
文摘The development of magnetic heterostructures with strong perpendicular magnetic anisotropy(PMA),strong spin-orbit torques(SOTs),low impedance,and good integration compatibility at the same time is central for high-performance spintronic memory and computing applications.Here,we report the development of the PMA superlattice[Pt/Co/W]_(n)that can be sputtered-deposited on commercial oxidized silicon substrates and has giant SOTs,strong uniaxial PMA of≈9.2 Merg/cm^(3),and rigid macrospin performance.The damping-like and field-like SOTs of the[Pt/Co/W]_(n)superlattices exhibit a linear increase with the repeat number n and reach the giant values of 225%and-33%(two orders of magnitude greater than that in clean-limit Pt)at n=12,respectively.The damping-like SOT is also of the opposite sign and much greater in magnitude than the field-like SOT,regardless of the number n.These results clarify that the spin current that generates SOTs in the[Pt/Co/W]_(n)superlattices arises predominantly from the spin Hall effect rather than bulk Rashba spin splitting,providing a unified understanding of the SOTs in these superlattices.We also demonstrate deterministic switching in thickerthan-50-nm PMA[Pt/Co/W]_(12)superlattices at a low current density.This work establishes the[Pt/Co/W]_(n)superlattice as a compelling material candidate for ultra-fast,low-power,long-retention nonvolatile spintronic memory and computing technologies.
基金Project supported by Shandong Provincial Natural Science Foundation,China(Grant No.ZR2022ME059)。
文摘Pd/Co_(2)MnSi(CMS)/Co/Pd multilayer films were designed based on the idea of combining highly spin-polarized materials with strong perpendicular magnetic anisotropy(PMA)films.The PMA of Pd/CMS/Co/Pd multilayer films was studied by optimizing the growth conditions and thickness of each film layer.The optimal structure of the multilayer films was Pd(6 nm)/CMS(5 nm)/Co(2 nm)/Pd(1 nm).Its abnormal Hall resistance(R_(Hall)),coercivity(H_(c))and effective magnetic anisotropy constant(Keff)are 0.08Ω,284 Oe and 1.36 Merg/cm^(3),respectively,which are 100%,492%,and 183%higher than the corresponding values(0.04Ω,48 Oe,and 0.48 Merg/cm^(3))of the Pd(6 nm)/Co(1 nm)/Pd(3 nm)trilayer films.The analysis shows that the increases of the above values are the result of the Pd/CMS interface effect and CMS/Co interface ferromagnetic(FM)coupling,and that it is closely related to the thickness of each film layer in the multilayer films and the growth conditions of the multilayer films.
文摘在9%(w/v)NaCl条件下,通过温度、pH两种因素诱导一株单增李斯特菌进入"活的非可培养"(viable but non-cuturable,VBNC)状态。通过LIVE/DEAD Baclight活菌检测试剂盒检测细菌总数与活菌数,比较单增李斯特菌状态及数量的差异与变化。结果显示,在2℃、pH6.0条件下单增李斯特菌活菌全部进入VBNC状态。用PMA-qPCR对经诱导的四份菌液进行检测,结果表明该方法能快速、准确地测出死菌背景下的活的单增李斯特菌。