A unit cell including the matrix, precipitation free zone(PFZ) and grain boundary was prepared, and the crystal plasticity finite element method(CPFEM) and extended finite element method(XFEM) were used to simulate th...A unit cell including the matrix, precipitation free zone(PFZ) and grain boundary was prepared, and the crystal plasticity finite element method(CPFEM) and extended finite element method(XFEM) were used to simulate the propagation of cracks at grain boundary. Simulation results show that the crystallographic orientation of PFZ has significant influence on crack propagation, which includes the crack growth direction and crack growth velocity. The fracture strain of soft orientation is larger than that of hard orientation due to the role of reducing the stress intensity at grain boundary in intergranular brittle fracture. But in intergranular ductile fracture, the fracture strain of soft orientation may be smaller than that of hard orientation due to the roles of deformation localization.展开更多
This study investigates the corrosion-assisted fatigue crack growth rate(FCGR)of 16 mm thick AA 7075-T651 friction stir welded(FSW)joints.Compact tension(CT)specimens were extracted from both the base material and FSW...This study investigates the corrosion-assisted fatigue crack growth rate(FCGR)of 16 mm thick AA 7075-T651 friction stir welded(FSW)joints.Compact tension(CT)specimens were extracted from both the base material and FSW joints to evaluate FCGR under varying corrosion exposure durations(0,7,30,60,and 90 days)at a constant stress ratio of 0.5.Microstructural analysis of the welds was conducted using optical and transmission electron microscopy(TEM).Results indicate that the critical stress intensity factor range(ΔK_(cr))of FSW joints is lower than that of the base material,primarily due to precipitate dissolution in the weld zone during the FSW process,as confirmed by TEM analysis.The fatigue life of FSW joints was significantly lower than that of the base material,but with prolonged exposure to seawater corrosion,the gap in fatigue life narrowed.Specimens exposed to seawater for more than 60days exhibited minimal differences in fatigue life between the base material and the FSW joints.This was attributed to the higher corrosion rate of the base material compared to the weld nugget,resulting in the formation of deeper pits that facilitated crack initiation and accelerated fatigue failure.The findings conclude that extended corrosion exposure leads to similar fatigue life and crack growth behaviour in both the base material and FSW joints.SEM and EDX analysis of AA7075-T651 revealed corrosion pits and rust products in initiation zones,ductile striations in growth regions,and secondary cracks with micro voids in fracture zones.FSW joints exhibited ultra-fine grains,smooth ductile fracture in initiation and growth regions,and brittle fracture in the fracture zones under both corroded and uncorroded conditions.展开更多
High temperature tensile-creep behavior of Mg-4Y-2.3Nd-IGd-O.6Zr （wt%, WE43（T6）） alloy at 523- 573 K was investigated. The creep stress exponent is equal to 4.6, suggesting the underlying dislocation creep mechani...High temperature tensile-creep behavior of Mg-4Y-2.3Nd-IGd-O.6Zr （wt%, WE43（T6）） alloy at 523- 573 K was investigated. The creep stress exponent is equal to 4.6, suggesting the underlying dislocation creep mechanism. The activation energy is （199 _＋ 23） kJ/mol, which is higher than that for self- diffusion in Mg and is believed to be associated with precipitates coarsening or cross slip. The creep mechanism is further suggested to be dislocation climb at 523 K, while a cross slip at 573 K is possible. The metastable 13＇ and ~]1 phases in the WE43（T6） alloy were relatively thermal stable at 523 K and could be effective to hinder the dislocation climb, which contributed to its excellent creep resistance. However, at 573 K it readily transforms into equilibrium/3e phase and coarsens within two hours, thereby causing a decrease of creep resistance. In addition, precipitate free zones approximately normal to applied stress direction （directional PFZs） developed during the creep deformation, especially at 573 K. Those zones became preferential sites to nucleate, extend and connect microcracks and cavities, which lead to the intergranular creep fracture. Improving the thermal stability of precipitates or introducing thermally stable fine plate-shaped precipitates on the basal planes of Mg matrix could enhance the high temperature creep resistance.展开更多
基金Projects(51475162,51405153)supported by the National Natural Science Foundation of ChinaProject(14JJ5015)supported by the Hunan Provincial Natural Science Foundation,China
文摘A unit cell including the matrix, precipitation free zone(PFZ) and grain boundary was prepared, and the crystal plasticity finite element method(CPFEM) and extended finite element method(XFEM) were used to simulate the propagation of cracks at grain boundary. Simulation results show that the crystallographic orientation of PFZ has significant influence on crack propagation, which includes the crack growth direction and crack growth velocity. The fracture strain of soft orientation is larger than that of hard orientation due to the role of reducing the stress intensity at grain boundary in intergranular brittle fracture. But in intergranular ductile fracture, the fracture strain of soft orientation may be smaller than that of hard orientation due to the roles of deformation localization.
文摘This study investigates the corrosion-assisted fatigue crack growth rate(FCGR)of 16 mm thick AA 7075-T651 friction stir welded(FSW)joints.Compact tension(CT)specimens were extracted from both the base material and FSW joints to evaluate FCGR under varying corrosion exposure durations(0,7,30,60,and 90 days)at a constant stress ratio of 0.5.Microstructural analysis of the welds was conducted using optical and transmission electron microscopy(TEM).Results indicate that the critical stress intensity factor range(ΔK_(cr))of FSW joints is lower than that of the base material,primarily due to precipitate dissolution in the weld zone during the FSW process,as confirmed by TEM analysis.The fatigue life of FSW joints was significantly lower than that of the base material,but with prolonged exposure to seawater corrosion,the gap in fatigue life narrowed.Specimens exposed to seawater for more than 60days exhibited minimal differences in fatigue life between the base material and the FSW joints.This was attributed to the higher corrosion rate of the base material compared to the weld nugget,resulting in the formation of deeper pits that facilitated crack initiation and accelerated fatigue failure.The findings conclude that extended corrosion exposure leads to similar fatigue life and crack growth behaviour in both the base material and FSW joints.SEM and EDX analysis of AA7075-T651 revealed corrosion pits and rust products in initiation zones,ductile striations in growth regions,and secondary cracks with micro voids in fracture zones.FSW joints exhibited ultra-fine grains,smooth ductile fracture in initiation and growth regions,and brittle fracture in the fracture zones under both corroded and uncorroded conditions.
基金funded by the National Basic Research Program of China(No.2013CB632202 and No.51531002)the National Natural Science Foundation of China(No.51301173)
文摘High temperature tensile-creep behavior of Mg-4Y-2.3Nd-IGd-O.6Zr （wt%, WE43（T6）） alloy at 523- 573 K was investigated. The creep stress exponent is equal to 4.6, suggesting the underlying dislocation creep mechanism. The activation energy is （199 _＋ 23） kJ/mol, which is higher than that for self- diffusion in Mg and is believed to be associated with precipitates coarsening or cross slip. The creep mechanism is further suggested to be dislocation climb at 523 K, while a cross slip at 573 K is possible. The metastable 13＇ and ~]1 phases in the WE43（T6） alloy were relatively thermal stable at 523 K and could be effective to hinder the dislocation climb, which contributed to its excellent creep resistance. However, at 573 K it readily transforms into equilibrium/3e phase and coarsens within two hours, thereby causing a decrease of creep resistance. In addition, precipitate free zones approximately normal to applied stress direction （directional PFZs） developed during the creep deformation, especially at 573 K. Those zones became preferential sites to nucleate, extend and connect microcracks and cavities, which lead to the intergranular creep fracture. Improving the thermal stability of precipitates or introducing thermally stable fine plate-shaped precipitates on the basal planes of Mg matrix could enhance the high temperature creep resistance.