A method of electroless plating is utilized to deposit Co-Fe alloy on the surface of multi-walled carbon nanotubes （MWCNTs）,and electromagnetic parameters of MWCNTs with and without electroless plating are discussed...A method of electroless plating is utilized to deposit Co-Fe alloy on the surface of multi-walled carbon nanotubes （MWCNTs）,and electromagnetic parameters of MWCNTs with and without electroless plating are discussed. The MWCNTs covered by Co-Fe is a desirable light absorbent in wide wave band by utilizing electroless plating process in experiments. Field-emission scanning electron microscope （FESEM） and field-emission transmission electron microscope （FETEM） images as well as energy dispersive spectroscopy （EDS） results are presented to show the morphology,components and electromagnetic parameters of MWCNTs. Electromagnetic properties of MWCNTs are enhanced after electroless plating observed from contrast of results be-tween MWCNTs with and without plating. In conclusion,the covering Co-Fe on the surface of MWCNTs in 2-18 GHz frequency range has better electromagnetic properties. When the material is in the 6.5 GHz electromagnetic waves,the reflection loss is up to -10 dB,and the bandwidth more than -4 dB is 5 GHz. The excellent electromagnetic properties make it probable for MWCNTs to be utilized as absorbent in electromagnetic shielding materials.展开更多
Catalytic hydrogenation of CO_(2) using renewable hydrogen not only reduces greenhouse gas emissions,but also provides industrial chemicals.Herein,a Co-Fe bimetallic catalyst was developed by a facile reactive ball-mi...Catalytic hydrogenation of CO_(2) using renewable hydrogen not only reduces greenhouse gas emissions,but also provides industrial chemicals.Herein,a Co-Fe bimetallic catalyst was developed by a facile reactive ball-milling method for highly active and selective hydrogenation of CO_(2) to value-added hydrocarbons.When reacted at 320℃,1.0 MPa and 9600 mL h^(-1) g_(cat)^(-1),the selectivity to light olefin(C_(2)^(=)-C_(4)^(=)) and C_(5)+ species achieves 57.3% and 22.3%,respectively,at a CO_(2) co nversion of 31.4%,which is superior to previous Fe-based catalysts.The CO_(2) activation can be promoted by the CoFe phase formed by reactive ball milling of the Fe-Co_(3)O_(4) mixture,and the in-situ Co_(2)C and Fe_(5)C_(2) formed during hydrogenation are beneficial for the C-C coupling reaction.The initial C-C coupling is related to the combination of CO species with the surface carbon of Fe/Co carbides,and the sustained C-C coupling is maintained by self-recovery of defective carbides.This new strategy contributes to the development of efficient catalysts for the hydrogenation of CO_(2) to value-added hydrocarbons.展开更多
文摘A method of electroless plating is utilized to deposit Co-Fe alloy on the surface of multi-walled carbon nanotubes （MWCNTs）,and electromagnetic parameters of MWCNTs with and without electroless plating are discussed. The MWCNTs covered by Co-Fe is a desirable light absorbent in wide wave band by utilizing electroless plating process in experiments. Field-emission scanning electron microscope （FESEM） and field-emission transmission electron microscope （FETEM） images as well as energy dispersive spectroscopy （EDS） results are presented to show the morphology,components and electromagnetic parameters of MWCNTs. Electromagnetic properties of MWCNTs are enhanced after electroless plating observed from contrast of results be-tween MWCNTs with and without plating. In conclusion,the covering Co-Fe on the surface of MWCNTs in 2-18 GHz frequency range has better electromagnetic properties. When the material is in the 6.5 GHz electromagnetic waves,the reflection loss is up to -10 dB,and the bandwidth more than -4 dB is 5 GHz. The excellent electromagnetic properties make it probable for MWCNTs to be utilized as absorbent in electromagnetic shielding materials.
基金supported by the National Natural Science Foundation of China (22008098, 21978156, 42002040)the Program for Innovative Research Team (in Science and Technology) in University of Henan Province (21IRTSTHN004)+1 种基金the Program for Science & Technology Innovation Talents in Universities of Henan Province (22HASTIT008)the Foundation of State Key Laboratory of High-efficiency Utilization of Coal and Green Chemical Engineering (2022-K34)。
文摘Catalytic hydrogenation of CO_(2) using renewable hydrogen not only reduces greenhouse gas emissions,but also provides industrial chemicals.Herein,a Co-Fe bimetallic catalyst was developed by a facile reactive ball-milling method for highly active and selective hydrogenation of CO_(2) to value-added hydrocarbons.When reacted at 320℃,1.0 MPa and 9600 mL h^(-1) g_(cat)^(-1),the selectivity to light olefin(C_(2)^(=)-C_(4)^(=)) and C_(5)+ species achieves 57.3% and 22.3%,respectively,at a CO_(2) co nversion of 31.4%,which is superior to previous Fe-based catalysts.The CO_(2) activation can be promoted by the CoFe phase formed by reactive ball milling of the Fe-Co_(3)O_(4) mixture,and the in-situ Co_(2)C and Fe_(5)C_(2) formed during hydrogenation are beneficial for the C-C coupling reaction.The initial C-C coupling is related to the combination of CO species with the surface carbon of Fe/Co carbides,and the sustained C-C coupling is maintained by self-recovery of defective carbides.This new strategy contributes to the development of efficient catalysts for the hydrogenation of CO_(2) to value-added hydrocarbons.