To obtain the Ti_(p)with different aspect ratios,the Ti_(p)/Mg-5Zn-0.3Ca composite prepared by semi-solid stir casting was subjected to extrusion at 220℃,180℃,and 140℃,respectively.Then,the effect of the Ti_(p)’s ...To obtain the Ti_(p)with different aspect ratios,the Ti_(p)/Mg-5Zn-0.3Ca composite prepared by semi-solid stir casting was subjected to extrusion at 220℃,180℃,and 140℃,respectively.Then,the effect of the Ti_(p)’s aspect ratio on the microstructure,mechanical properties,work hardening and softening behaviors of Ti_(p)/Mg-5Zn-0.3Ca composites was investigated.The results indicated that the Ti_(p)could be elongated obviously after low-temperature extrusion,and the aspect ratio of which would reach to 13.7:1 as the extrusion temperature deceased to 140℃.Then the“Ti/Mg”layer-like structure was formed in the Ti_(p)/Mg-5Zn-0.3Ca composite.Accompanied with the elongation of Ti_(p),the dynamic recrystallized grains and dynamic precipitates were both refined significantly,however,the dynamic recrystallization rate changed a little.The elongated Ti_(p)endowed the Ti_(p)/Mg-5Zn-0.3Ca composites with better matching of strength and toughness without the sacrifice of elongation and bending strain.Both the work hardening rate and softening rate of Ti_(p)/Mg-5Zn-0.3Ca composites increased with the increasing aspect ratio of Ti_(p).The formation of“Ti/Mg”layer-like structure contributed to the redistribution of strain from large aggregations to a network-like distribution,which effectively suppresses the initiation and propagation of micro-cracks,thus enhancing the plasticity of the Ti_(p)/Mg-5Zn-0.3Ca composites.展开更多
基金supported by the“National Natural Science Foundation of China”(Grants.52271109 and 52001223)Support from the“National Key Research and Development Program for Young Scientists”(Grant.2021YFB3703300)+1 种基金the Major Special Plan for Science and Technology in Shanxi Province(202201050201012)the Special Fund Project for Guiding Local Science and Technology Development by the Central Government(Grant.YDZJSX2021B019)。
文摘To obtain the Ti_(p)with different aspect ratios,the Ti_(p)/Mg-5Zn-0.3Ca composite prepared by semi-solid stir casting was subjected to extrusion at 220℃,180℃,and 140℃,respectively.Then,the effect of the Ti_(p)’s aspect ratio on the microstructure,mechanical properties,work hardening and softening behaviors of Ti_(p)/Mg-5Zn-0.3Ca composites was investigated.The results indicated that the Ti_(p)could be elongated obviously after low-temperature extrusion,and the aspect ratio of which would reach to 13.7:1 as the extrusion temperature deceased to 140℃.Then the“Ti/Mg”layer-like structure was formed in the Ti_(p)/Mg-5Zn-0.3Ca composite.Accompanied with the elongation of Ti_(p),the dynamic recrystallized grains and dynamic precipitates were both refined significantly,however,the dynamic recrystallization rate changed a little.The elongated Ti_(p)endowed the Ti_(p)/Mg-5Zn-0.3Ca composites with better matching of strength and toughness without the sacrifice of elongation and bending strain.Both the work hardening rate and softening rate of Ti_(p)/Mg-5Zn-0.3Ca composites increased with the increasing aspect ratio of Ti_(p).The formation of“Ti/Mg”layer-like structure contributed to the redistribution of strain from large aggregations to a network-like distribution,which effectively suppresses the initiation and propagation of micro-cracks,thus enhancing the plasticity of the Ti_(p)/Mg-5Zn-0.3Ca composites.
