Er^(3+)-doped BaLaGaO_(4)green phosphors was synthesized through a high-temperature solid-state reaction technique.The phase structure and morphology test results of the phosphor indicate that the BaLaGaO_(4)material ...Er^(3+)-doped BaLaGaO_(4)green phosphors was synthesized through a high-temperature solid-state reaction technique.The phase structure and morphology test results of the phosphor indicate that the BaLaGaO_(4)material was successfully synthesized and Er^(3+)ions were successfully doped into the main lattice.This doping does change the basic structure of the crystal.BaLaGaO_(4):Er^(3+)phosphor exhibits bright green emission centered at 545 nm when excited by 381 nm ultraviolet light or 980 nm near-infrared light.The optimal doping concentration is found to be x=0.04.To quantify the temperature sensitivity of the phosphor,the fluorescence intensity ratio method was used.Within the temperature range of 298-473 K,the maximum relative sensitivities are 1.35%/K(298 K,381 nm)and 1.45%/K(298 K,980 nm),respectively.The maximum absolute sensitivities are 0.67%/K(473 K,381 nm)and 0.69%/K(473 K,980 nm),respectively.Finally,white light-emitting diodes(WLEDs)with a high colour index of Ra=82and a relatively low correlated colour temperature of CCT=5064 K are obtained by integrating the synthesized BaLaGaO_(4):0.04Er^(3+)green phosphor into warm WLEDs devices.These results suggest that Er^(3+)-activated BaLaGaO_(4)multifunctional phosphors hold considerable promise in the areas of optical temperature sensing and WLEDs phosphor conversion.展开更多
基金supported by the National Natural Science Foundation of China(52403403)Guizhou Provincial Basic Research Program(Natural Science)(Qian ke he ji chu-ZK2024 YiBan 095)。
文摘Er^(3+)-doped BaLaGaO_(4)green phosphors was synthesized through a high-temperature solid-state reaction technique.The phase structure and morphology test results of the phosphor indicate that the BaLaGaO_(4)material was successfully synthesized and Er^(3+)ions were successfully doped into the main lattice.This doping does change the basic structure of the crystal.BaLaGaO_(4):Er^(3+)phosphor exhibits bright green emission centered at 545 nm when excited by 381 nm ultraviolet light or 980 nm near-infrared light.The optimal doping concentration is found to be x=0.04.To quantify the temperature sensitivity of the phosphor,the fluorescence intensity ratio method was used.Within the temperature range of 298-473 K,the maximum relative sensitivities are 1.35%/K(298 K,381 nm)and 1.45%/K(298 K,980 nm),respectively.The maximum absolute sensitivities are 0.67%/K(473 K,381 nm)and 0.69%/K(473 K,980 nm),respectively.Finally,white light-emitting diodes(WLEDs)with a high colour index of Ra=82and a relatively low correlated colour temperature of CCT=5064 K are obtained by integrating the synthesized BaLaGaO_(4):0.04Er^(3+)green phosphor into warm WLEDs devices.These results suggest that Er^(3+)-activated BaLaGaO_(4)multifunctional phosphors hold considerable promise in the areas of optical temperature sensing and WLEDs phosphor conversion.