Doping in thin-film transistors(TFTs) plays a crucial role in tailoring material properties to enhance device performance, making them essential for advanced electronic applications. This study explores the synthesis ...Doping in thin-film transistors(TFTs) plays a crucial role in tailoring material properties to enhance device performance, making them essential for advanced electronic applications. This study explores the synthesis and characterization of TFTs fabricated using nickel(Ni)-doped indium oxide(In_(2)O_(3)) via a wet-chemical approach. The presented work investigates the effect of "Ni" incorporation in In_(2)O_(3) on the structural and electrical transport properties of In_(2)O_(3), revealing that higher "Ni" content decreases the oxygen vacancies, leading to a reduction in leakage current and a forward shift in threshold potential(V_(th)).Experimental findings reveal that Ni In O-based TFTs(with Ni = 0.5%) showcase enhanced electrical performance, achieving mobility of 7.54 cm^(2)/(V·s), an impressive ON/OFF current ratio of ~10^(7), a V_(th) of 6.26 V, reduced interfacial trap states(D_(it)) of 8.23 ×10^(12) cm^(-2) and enhanced biased stress stability. The efficacy of "Ni" incorporation is attributed to the upgraded Lewis acidity, stable Ni-O bond strength, and small ionic radius of Ni. Negative bias illumination stability(NBIS) measurements further indicate that device stability diminishes with shorter light wavelengths, likely due to the activation of oxygen vacancies. These findings validate the solution-processed techniques' potential for future large-scale, low-cost, energy-efficient, and high-performance electronics.展开更多
利用Illumina Hi Seq高通量测序技术,对我国南方湿热地区某O_3/BAC饮用水处理过程中各工艺出水及滤料中微生物多样性及其变化规律进行研究。结果表明,测序共获得385 499条有效数据(Effective Tags),归类为45个门、86个纲、165个目、308...利用Illumina Hi Seq高通量测序技术,对我国南方湿热地区某O_3/BAC饮用水处理过程中各工艺出水及滤料中微生物多样性及其变化规律进行研究。结果表明,测序共获得385 499条有效数据(Effective Tags),归类为45个门、86个纲、165个目、308个科、567个属。微生物多样性随工艺流程整体呈下降趋势,尤其是消毒工艺能大幅削减水体中的微生物,消毒效果较好,但生物活性炭池出水中微生物多样性较V型滤池出水(FB)不降反增,且滤砂(FS)和活性炭上均有大量微生物附着,其中活性炭上附着的微生物多样性高于原水。此外,所有样品中变形菌门、放线菌门、拟杆菌门、厚壁菌门和浮霉菌门含量较高,分别为68.47%、10.64%、6.15%、4.63%和1.51%;鞘氨醇单胞菌属在FB、FS和BAC样品中大量滋生,且与假单胞菌属在出厂水中均有微量存在,二者可引起管网腐蚀,是饮用水安全的一大隐患,应予以重视。展开更多
Nano-sized reinforcements improved the mechanical characteristics efficiently by promoting more implicit particle hardening mechanisms compared to micron-sized reinforcements.Nano-sized particles lessen the critical p...Nano-sized reinforcements improved the mechanical characteristics efficiently by promoting more implicit particle hardening mechanisms compared to micron-sized reinforcements.Nano-sized particles lessen the critical particle solidification velocity for swamp and thus offers better dispersal.In the present investigation,the friction stir processing(FSP)is utilized to produce AZ31/Al_(2)O_(3)nanocomposites at various tool rotation speeds(i.e.,900,1200,and 1500 rpm)with an optimized 1.5%volume alumina(Al_(2)O_(3))reinforcement ratio.The mechanical and corrosion behavior of AZ31/Al_(2)O_(3)-developed nanocomposites was investigated and compared with that of the AZ31 base alloy.The AZ31 alloy experienced a comprehensive dynamic recrystallization during FSP,causing substantial grain refinement.Grain-size strengthening is the primary factor contributed to the enhancement in the strength of the fabricated nanocomposite.Tensile strength and yield strength values were lower than those for the base metal matrix,although an upward trend in both values has been observed with an increase in tool rotation speed.An 19.72%increase in hardness along with superior corrosion resistance was achieved compared to the base alloy at a tool rotational speed of 1500 rpm.The corrosion currents(Jcorr)of all samples dropped with increase in the rotational speed,in contrast to the corrosion potentials(Ecorr),which increased.The values of Jcorr of AZ31/Al_(2)O_(3)were 42.3%,56.8%,and 65.5%lower than those of AZ31 alloy at the chosen rotating speeds of 900,1200,and 1500 rpm,respectively.The corrosion behavior of friction stir processed nanocomposites have been addressed in this manuscript which has not been given sufficient attention in the existing literature.Further,this work offers an effective choice for the quality assurance of the FSP process of AZ31/Al_(2)O_(3)nanocomposites.The obtained results are relevant to the development of lightweight automobile and aerospace structures and components.展开更多
(γ’+β)two-phase Ni-Al is a promising high-temperature protective coating material used on Ni-base superalloys since it has good interfacial compatibility with superalloys due to the low Al content compared to singl...(γ’+β)two-phase Ni-Al is a promising high-temperature protective coating material used on Ni-base superalloys since it has good interfacial compatibility with superalloys due to the low Al content compared to single-phaseβ-NiA l.In this paper,we aim to improve the oxidation resistance,whereby Ni-34Al-0.1Dy,a(γ’+β)two-phase Ni-Al alloy,was treated by laser shock processing(LSP)and the oxidation behavior at 1150℃ was investigated.The results showed that after oxidation,Al_(2)O_(3)scale formed on the originalβphase of the untreated alloy with a small grain size(200-800 nm),while for the LSP-treated samples,the scale grown on the originalβphase was dominantly composed of larger Al_(2)O_(3)grains with a size of 2-3μm.The distinction was attributed to the promotion ofθ-Al_(2)O_(3)toα-Al_(2)O_(3)transformation induced by the LSP,because the dislocation density,as well as surface roughness,were increased during LSP treatment which can provide heterogeneous nucleation sites forα-Al_(2)O_(3).In addition,the larger-size Al_(2)O_(3)particles,derived from the direct conversion of needle-likeθ-Al_(2)O_(3)in the initial oxidation stage,could rapidly overspread the wholeβphase surface thus reducing the scale growth rate.展开更多
The manufacture process of 8mol% Y-2O-3 stabilized ZrO-2(YSZ) from nano powders, including the forming and sintering stages, was studied. During the forming process of YSZ powders, the relative density of YSZ increase...The manufacture process of 8mol% Y-2O-3 stabilized ZrO-2(YSZ) from nano powders, including the forming and sintering stages, was studied. During the forming process of YSZ powders, the relative density of YSZ increases lineally with the forming press,and the sintering linear shrinkage of YSZ to the forming press compiles to the parabola trend. When the forming press exceeding 500MPa, the samples with lower shrinkage and high density were obtained. The sintering temperature of YSZ decreases greatly because of the small size and high active surface of YSZ powders. As a result, the beginning sintering temperature of YSZ made in the experiment is as low as 825℃, and the end sintering temperature is 1300-1350℃. The relative density of YSZ ceramic by solid sintering at 1300-1350℃ is more than 97%, with little and small pores in the uniform microstructure.展开更多
基金funded by the research startup funding of National Research Foundation (NRF) of Korea through the Ministry of Science and ICT 2022R1G1A1009887Part of this study was supported by research start-up funding of Anhui University (S202418001/078)。
文摘Doping in thin-film transistors(TFTs) plays a crucial role in tailoring material properties to enhance device performance, making them essential for advanced electronic applications. This study explores the synthesis and characterization of TFTs fabricated using nickel(Ni)-doped indium oxide(In_(2)O_(3)) via a wet-chemical approach. The presented work investigates the effect of "Ni" incorporation in In_(2)O_(3) on the structural and electrical transport properties of In_(2)O_(3), revealing that higher "Ni" content decreases the oxygen vacancies, leading to a reduction in leakage current and a forward shift in threshold potential(V_(th)).Experimental findings reveal that Ni In O-based TFTs(with Ni = 0.5%) showcase enhanced electrical performance, achieving mobility of 7.54 cm^(2)/(V·s), an impressive ON/OFF current ratio of ~10^(7), a V_(th) of 6.26 V, reduced interfacial trap states(D_(it)) of 8.23 ×10^(12) cm^(-2) and enhanced biased stress stability. The efficacy of "Ni" incorporation is attributed to the upgraded Lewis acidity, stable Ni-O bond strength, and small ionic radius of Ni. Negative bias illumination stability(NBIS) measurements further indicate that device stability diminishes with shorter light wavelengths, likely due to the activation of oxygen vacancies. These findings validate the solution-processed techniques' potential for future large-scale, low-cost, energy-efficient, and high-performance electronics.
文摘利用Illumina Hi Seq高通量测序技术,对我国南方湿热地区某O_3/BAC饮用水处理过程中各工艺出水及滤料中微生物多样性及其变化规律进行研究。结果表明,测序共获得385 499条有效数据(Effective Tags),归类为45个门、86个纲、165个目、308个科、567个属。微生物多样性随工艺流程整体呈下降趋势,尤其是消毒工艺能大幅削减水体中的微生物,消毒效果较好,但生物活性炭池出水中微生物多样性较V型滤池出水(FB)不降反增,且滤砂(FS)和活性炭上均有大量微生物附着,其中活性炭上附着的微生物多样性高于原水。此外,所有样品中变形菌门、放线菌门、拟杆菌门、厚壁菌门和浮霉菌门含量较高,分别为68.47%、10.64%、6.15%、4.63%和1.51%;鞘氨醇单胞菌属在FB、FS和BAC样品中大量滋生,且与假单胞菌属在出厂水中均有微量存在,二者可引起管网腐蚀,是饮用水安全的一大隐患,应予以重视。
文摘Nano-sized reinforcements improved the mechanical characteristics efficiently by promoting more implicit particle hardening mechanisms compared to micron-sized reinforcements.Nano-sized particles lessen the critical particle solidification velocity for swamp and thus offers better dispersal.In the present investigation,the friction stir processing(FSP)is utilized to produce AZ31/Al_(2)O_(3)nanocomposites at various tool rotation speeds(i.e.,900,1200,and 1500 rpm)with an optimized 1.5%volume alumina(Al_(2)O_(3))reinforcement ratio.The mechanical and corrosion behavior of AZ31/Al_(2)O_(3)-developed nanocomposites was investigated and compared with that of the AZ31 base alloy.The AZ31 alloy experienced a comprehensive dynamic recrystallization during FSP,causing substantial grain refinement.Grain-size strengthening is the primary factor contributed to the enhancement in the strength of the fabricated nanocomposite.Tensile strength and yield strength values were lower than those for the base metal matrix,although an upward trend in both values has been observed with an increase in tool rotation speed.An 19.72%increase in hardness along with superior corrosion resistance was achieved compared to the base alloy at a tool rotational speed of 1500 rpm.The corrosion currents(Jcorr)of all samples dropped with increase in the rotational speed,in contrast to the corrosion potentials(Ecorr),which increased.The values of Jcorr of AZ31/Al_(2)O_(3)were 42.3%,56.8%,and 65.5%lower than those of AZ31 alloy at the chosen rotating speeds of 900,1200,and 1500 rpm,respectively.The corrosion behavior of friction stir processed nanocomposites have been addressed in this manuscript which has not been given sufficient attention in the existing literature.Further,this work offers an effective choice for the quality assurance of the FSP process of AZ31/Al_(2)O_(3)nanocomposites.The obtained results are relevant to the development of lightweight automobile and aerospace structures and components.
基金financially supported by the National Natural Science Foundation of China(Grant No.51901011)the National Science and Technology Major Project(Grant Nos.2017-Ⅵ-0002-0072 and 2017-VII-0007-0100)+1 种基金the Fundamental Research Funds for Central Universities(Grant No.YWF-21-BJ-J-1034)the support from Youth Talent Support Program of Beihang University。
文摘(γ’+β)two-phase Ni-Al is a promising high-temperature protective coating material used on Ni-base superalloys since it has good interfacial compatibility with superalloys due to the low Al content compared to single-phaseβ-NiA l.In this paper,we aim to improve the oxidation resistance,whereby Ni-34Al-0.1Dy,a(γ’+β)two-phase Ni-Al alloy,was treated by laser shock processing(LSP)and the oxidation behavior at 1150℃ was investigated.The results showed that after oxidation,Al_(2)O_(3)scale formed on the originalβphase of the untreated alloy with a small grain size(200-800 nm),while for the LSP-treated samples,the scale grown on the originalβphase was dominantly composed of larger Al_(2)O_(3)grains with a size of 2-3μm.The distinction was attributed to the promotion ofθ-Al_(2)O_(3)toα-Al_(2)O_(3)transformation induced by the LSP,because the dislocation density,as well as surface roughness,were increased during LSP treatment which can provide heterogeneous nucleation sites forα-Al_(2)O_(3).In addition,the larger-size Al_(2)O_(3)particles,derived from the direct conversion of needle-likeθ-Al_(2)O_(3)in the initial oxidation stage,could rapidly overspread the wholeβphase surface thus reducing the scale growth rate.
文摘The manufacture process of 8mol% Y-2O-3 stabilized ZrO-2(YSZ) from nano powders, including the forming and sintering stages, was studied. During the forming process of YSZ powders, the relative density of YSZ increases lineally with the forming press,and the sintering linear shrinkage of YSZ to the forming press compiles to the parabola trend. When the forming press exceeding 500MPa, the samples with lower shrinkage and high density were obtained. The sintering temperature of YSZ decreases greatly because of the small size and high active surface of YSZ powders. As a result, the beginning sintering temperature of YSZ made in the experiment is as low as 825℃, and the end sintering temperature is 1300-1350℃. The relative density of YSZ ceramic by solid sintering at 1300-1350℃ is more than 97%, with little and small pores in the uniform microstructure.