Al2O3-Ni interface formed under vacuum condition is non-wetting and weak. Severe instantaneous intedecial reaction (i.e. wetting) at the Al2O3-Ni interface promoted by oxygen can create a strengthened interface. The N...Al2O3-Ni interface formed under vacuum condition is non-wetting and weak. Severe instantaneous intedecial reaction (i.e. wetting) at the Al2O3-Ni interface promoted by oxygen can create a strengthened interface. The NiAl2O4 spinel-Ni intedece is weak and growth of the spinel interphase is detrimental to the Al2O3-Ni intedecial bonding. A proper control of the oxygen partial pressure can achieve wetting while avoiding the existence of spinel at the interface, producing stronger interfaces by both mechanical interlocking and more intimate chemical bonding in an Al2O3-20 vol pct Ni composite.展开更多
文摘Al2O3-Ni interface formed under vacuum condition is non-wetting and weak. Severe instantaneous intedecial reaction (i.e. wetting) at the Al2O3-Ni interface promoted by oxygen can create a strengthened interface. The NiAl2O4 spinel-Ni intedece is weak and growth of the spinel interphase is detrimental to the Al2O3-Ni intedecial bonding. A proper control of the oxygen partial pressure can achieve wetting while avoiding the existence of spinel at the interface, producing stronger interfaces by both mechanical interlocking and more intimate chemical bonding in an Al2O3-20 vol pct Ni composite.