Ni/SiO2-ZrO2 catalysts with Ni loadings of 1 to 13 wt-% were prepared, characterized by elemental analysis, X-ray diffraction, N2 sorption, temperature programmed oxidation, temperature programmed reduc- tion, and tes...Ni/SiO2-ZrO2 catalysts with Ni loadings of 1 to 13 wt-% were prepared, characterized by elemental analysis, X-ray diffraction, N2 sorption, temperature programmed oxidation, temperature programmed reduc- tion, and tested for their activity and stability in the dry reforming of methane with carbon dioxide at 850 ℃, gas hourly space velocity of 6000 and 1800 h^-1 and atmo- spheric pressure. The SiO2-ZrO2 support as obtained through a simple and efficient sol-gel synthesis is highly porous （ABET = 90 m^·g^-1, dp= 4.4 nm） with a homogeneously distributed Si-content of 3 wt-%. No loss of Si or formation ofmonoclinic ZrO2, even after steaming at 850 ℃ for 160 h, was detectable. The catalyst with 5 wt-% Ni loading in its fully reduced state is stable over 15 h on-stream in the dry reforming reaction. If the catalyst was not fully reduced, a reduction during the early stages of dry reforming is accompanied by the deposition of up to 44 mg· g^-1 carbon as shown by experiments in a magnetic suspension balance. Rapid coking occurs for increased residence times and times-on-stream starting at 50 h. The Ni loading of 5 wt-% on SiO2-ZrO2 was shown to provide an optimal balance between activity and coking tendency.展开更多
ZrO2-mullite nano-ceramics were fabricated by in-situ controlled crystallizing from SiO2-Al2O3-ZrO2 amorphous bulk. The thermal transformation sequences of the SiO2-Al2O3-ZrO2 amorphous bulk were investigated by X-ray...ZrO2-mullite nano-ceramics were fabricated by in-situ controlled crystallizing from SiO2-Al2O3-ZrO2 amorphous bulk. The thermal transformation sequences of the SiO2-Al2O3-ZrO2 amorphous bulk were investigated by X-ray diffraction, infrared spectrum, scanning electron microscope and differential scanning calorimetric. And the mechanical properties of the nano-ceramics were studied. The results show that the bulks are still in amorphous state at 900 ℃ and the t-ZrO2 forms at about 950 ℃ with a faint spinel-like phase which changes into mullite on further heating. ZrO2 and mullite become major phases at 1 100 ℃ and an amount of m-ZrO2 occur at the same time. The sample heated at 950 ℃ for 2 h and then at 1 100 ℃ for 1 h shows very dense and homogenous microstructure with ball-like grains in size of 20-50 nm. With the increase of crystallization temperature up to 1 350 ℃, the grains grow quickly and some grow into lath-shaped grains with major diameter of 5 μm. After two-step treatment the highest micro-hardness, flexural strength and fracture toughness of the samples are 13.72 GPa, 520 MPa and 5.13 MPa·m1/2, respectively.展开更多
SiO2-Al2O3-ZrO2 glasses with different nucleating agents were crystallized under special processing schedule. The microstructure and mechanical properties of the glass-ceramics in SiO2-Al2O3-ZrO2 system were investiga...SiO2-Al2O3-ZrO2 glasses with different nucleating agents were crystallized under special processing schedule. The microstructure and mechanical properties of the glass-ceramics in SiO2-Al2O3-ZrO2 system were investigated by differential scanning calorimetry, scanning electron microscopy, X-ray diffraction and three-point bending method. The results show that ZrO2 is not an effective nucleating agent in SiO2-Al2O3-ZrO2 system, while TiO2 is effective for the separation of spinel, and P2O5 facilitates solubility of ZrO2 in glass and crystallization. The main crystalline phases of the glass-ceramics are spinel, anorthite and tetragonal zirconia. With the increase of ZrO2 content in the glass, glass-ceramics show higher bending strength （120MPa） than others.展开更多
文摘Ni/SiO2-ZrO2 catalysts with Ni loadings of 1 to 13 wt-% were prepared, characterized by elemental analysis, X-ray diffraction, N2 sorption, temperature programmed oxidation, temperature programmed reduc- tion, and tested for their activity and stability in the dry reforming of methane with carbon dioxide at 850 ℃, gas hourly space velocity of 6000 and 1800 h^-1 and atmo- spheric pressure. The SiO2-ZrO2 support as obtained through a simple and efficient sol-gel synthesis is highly porous （ABET = 90 m^·g^-1, dp= 4.4 nm） with a homogeneously distributed Si-content of 3 wt-%. No loss of Si or formation ofmonoclinic ZrO2, even after steaming at 850 ℃ for 160 h, was detectable. The catalyst with 5 wt-% Ni loading in its fully reduced state is stable over 15 h on-stream in the dry reforming reaction. If the catalyst was not fully reduced, a reduction during the early stages of dry reforming is accompanied by the deposition of up to 44 mg· g^-1 carbon as shown by experiments in a magnetic suspension balance. Rapid coking occurs for increased residence times and times-on-stream starting at 50 h. The Ni loading of 5 wt-% on SiO2-ZrO2 was shown to provide an optimal balance between activity and coking tendency.
基金Project(2003AA332040) supported by the National High Technology Research and Development Program of China
文摘ZrO2-mullite nano-ceramics were fabricated by in-situ controlled crystallizing from SiO2-Al2O3-ZrO2 amorphous bulk. The thermal transformation sequences of the SiO2-Al2O3-ZrO2 amorphous bulk were investigated by X-ray diffraction, infrared spectrum, scanning electron microscope and differential scanning calorimetric. And the mechanical properties of the nano-ceramics were studied. The results show that the bulks are still in amorphous state at 900 ℃ and the t-ZrO2 forms at about 950 ℃ with a faint spinel-like phase which changes into mullite on further heating. ZrO2 and mullite become major phases at 1 100 ℃ and an amount of m-ZrO2 occur at the same time. The sample heated at 950 ℃ for 2 h and then at 1 100 ℃ for 1 h shows very dense and homogenous microstructure with ball-like grains in size of 20-50 nm. With the increase of crystallization temperature up to 1 350 ℃, the grains grow quickly and some grow into lath-shaped grains with major diameter of 5 μm. After two-step treatment the highest micro-hardness, flexural strength and fracture toughness of the samples are 13.72 GPa, 520 MPa and 5.13 MPa·m1/2, respectively.
文摘SiO2-Al2O3-ZrO2 glasses with different nucleating agents were crystallized under special processing schedule. The microstructure and mechanical properties of the glass-ceramics in SiO2-Al2O3-ZrO2 system were investigated by differential scanning calorimetry, scanning electron microscopy, X-ray diffraction and three-point bending method. The results show that ZrO2 is not an effective nucleating agent in SiO2-Al2O3-ZrO2 system, while TiO2 is effective for the separation of spinel, and P2O5 facilitates solubility of ZrO2 in glass and crystallization. The main crystalline phases of the glass-ceramics are spinel, anorthite and tetragonal zirconia. With the increase of ZrO2 content in the glass, glass-ceramics show higher bending strength （120MPa） than others.
基金supported by the National Natural Science Foundation of China(21703194)the Natural Science Foundation of Jiangsu Province(BK20171168,BK20171169)+2 种基金Natural Science Foundation of Jiangsu Higher Education Institutions of China(17KJB530010,17KJB150038 and18KJA430015)Key Research Project of Social Development of Xuzhou(KC17154)Research Project of Xuzhou University of Technology(XKY2017217)