Nickel catalysts supported on CeO2-ZrO2-CeO2,ZrO2-Al2O3 and Al2O3 were prepared and characterized by means of X-ray diffraction（XRD）,BET areas,H2 temperature-programmed reduction（H2-TPR）,and X-ray photoelectron sp...Nickel catalysts supported on CeO2-ZrO2-CeO2,ZrO2-Al2O3 and Al2O3 were prepared and characterized by means of X-ray diffraction（XRD）,BET areas,H2 temperature-programmed reduction（H2-TPR）,and X-ray photoelectron spectroscopy（XPS）.Through the test of catalytic partial oxidation of methane（CPOM）,Ni/CeO2-ZrO2-Al2O3 displayed the highest activity,which resulted from its largest BET area and best NiO dispersion.Furthermore,Ni/CeO2-ZrO2-Al2O3 maintained a long-time stability in CPOM,which was attributed to its best coking resistance among all the prepared catalysts.展开更多
CeO2-ZeO2 solid solutions are extensively used as oxygen storage promoters in the current automotive three-way catalysts. High thermal stability of the textural properties is one of the most important requirements for...CeO2-ZeO2 solid solutions are extensively used as oxygen storage promoters in the current automotive three-way catalysts. High thermal stability of the textural properties is one of the most important requirements for practical application since temperatures up to 1273 K are easily experienced by these materials under real working conditions. In the present paper, we investigated how hydrothermal treatments applied to cakes of doped and undoped ZrO2-rich CeO2-ZrO2 precursors might improve the thermal stability of the final CeO2-ZrO2 solid solution. A rationale was developed that allowed to correlate the morphology of the hydrothermaUy treated cake with the thermal stability at 1273 K of the final product, which did not depend on the composition of the mixed oxides.展开更多
Nickel and sulfate co-modified CeO2-ZrO2 catalysts were prepared by sol-gel method. The catalysts were characterized by XRD, FTIR, XPS, NH3 chemisorption and NH3-SCR activity tests. The results showed that the enhance...Nickel and sulfate co-modified CeO2-ZrO2 catalysts were prepared by sol-gel method. The catalysts were characterized by XRD, FTIR, XPS, NH3 chemisorption and NH3-SCR activity tests. The results showed that the enhanced acidity of CeO2-ZrO2 catalysts by nickel and sulfate co-modification was responsible for the broadened temperature window and improved the selectivity to N2 in NH3-SCR deNOx. The introduction of nickel to CeO2-ZrO2 solid solutions resulted in more Ce3+ on surface of catalyst, leading to an in...展开更多
The influences of CeO2-ZrO2 and γ-Al2O3 mixing methods on the catalytic activity and stability of partial oxidation of methane （POM） were investigated over Ni/Ce0.7Zr0.3O2-Al2O3 catalysts. The catalysts were charac...The influences of CeO2-ZrO2 and γ-Al2O3 mixing methods on the catalytic activity and stability of partial oxidation of methane （POM） were investigated over Ni/Ce0.7Zr0.3O2-Al2O3 catalysts. The catalysts were characterized by XRD, TPR, H2-chemsorption, and TG-DTA. For fresh catalysts, the results showed that the salt precursor mixing catalyst （ATOM） presented better performance than the catalysts prepared by the precipitator mixing method （MOL） and the powder mechanically mixing method （MECH）. The result of XRD suggested that the interaction between CeO2-ZrO2 and Al2O3 in ATOM sample was stronger than the others, which led to more lattice defects and thereby better initial activity. Moreover, the MECH sample had the best stability and the least coke deposition in 24 h stability tests. The results of TPR and H2-chemsorption indicated that the intimate contact of Ni-Al in MECH sample enhanced the ability of resisting coke deposition and metal sintering.展开更多
CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that...CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that three CeO2-based oxygen storage materials are all forming homogeneous solid solution.Among the samples,CeO2-ZrO2-Al2O3(CZA)has the best textural properties and excellent thermal stability.The specific surface area and pore volume of aged CZA are 90 m2/g and 0.29 mL/g.We proposed a viewpoint:Al3+ might insert among the interspace of fluorite structure or highly dispersal in solid solutions.展开更多
基金Project supported by State Key Fundamental Research Project(G1999022400)
文摘Nickel catalysts supported on CeO2-ZrO2-CeO2,ZrO2-Al2O3 and Al2O3 were prepared and characterized by means of X-ray diffraction（XRD）,BET areas,H2 temperature-programmed reduction（H2-TPR）,and X-ray photoelectron spectroscopy（XPS）.Through the test of catalytic partial oxidation of methane（CPOM）,Ni/CeO2-ZrO2-Al2O3 displayed the highest activity,which resulted from its largest BET area and best NiO dispersion.Furthermore,Ni/CeO2-ZrO2-Al2O3 maintained a long-time stability in CPOM,which was attributed to its best coking resistance among all the prepared catalysts.
基金PRIN 2006, "Caratterizzazione spettroscopica e morfologica di Me-POSS eterogeneizzati", MEL Chemicals
文摘CeO2-ZeO2 solid solutions are extensively used as oxygen storage promoters in the current automotive three-way catalysts. High thermal stability of the textural properties is one of the most important requirements for practical application since temperatures up to 1273 K are easily experienced by these materials under real working conditions. In the present paper, we investigated how hydrothermal treatments applied to cakes of doped and undoped ZrO2-rich CeO2-ZrO2 precursors might improve the thermal stability of the final CeO2-ZrO2 solid solution. A rationale was developed that allowed to correlate the morphology of the hydrothermaUy treated cake with the thermal stability at 1273 K of the final product, which did not depend on the composition of the mixed oxides.
基金Project supported by the "863 Project" (2009AA06Z304 and 2009AA064801)
文摘Nickel and sulfate co-modified CeO2-ZrO2 catalysts were prepared by sol-gel method. The catalysts were characterized by XRD, FTIR, XPS, NH3 chemisorption and NH3-SCR activity tests. The results showed that the enhanced acidity of CeO2-ZrO2 catalysts by nickel and sulfate co-modification was responsible for the broadened temperature window and improved the selectivity to N2 in NH3-SCR deNOx. The introduction of nickel to CeO2-ZrO2 solid solutions resulted in more Ce3+ on surface of catalyst, leading to an in...
基金973 Program (2004CB719503)Key Program of Natural Science Foundation of Tianjin (07JCZDJC01600)Program for New Century Excellent Talents in University (NCET-06-0243)
文摘The influences of CeO2-ZrO2 and γ-Al2O3 mixing methods on the catalytic activity and stability of partial oxidation of methane （POM） were investigated over Ni/Ce0.7Zr0.3O2-Al2O3 catalysts. The catalysts were characterized by XRD, TPR, H2-chemsorption, and TG-DTA. For fresh catalysts, the results showed that the salt precursor mixing catalyst （ATOM） presented better performance than the catalysts prepared by the precipitator mixing method （MOL） and the powder mechanically mixing method （MECH）. The result of XRD suggested that the interaction between CeO2-ZrO2 and Al2O3 in ATOM sample was stronger than the others, which led to more lattice defects and thereby better initial activity. Moreover, the MECH sample had the best stability and the least coke deposition in 24 h stability tests. The results of TPR and H2-chemsorption indicated that the intimate contact of Ni-Al in MECH sample enhanced the ability of resisting coke deposition and metal sintering.
文摘CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that three CeO2-based oxygen storage materials are all forming homogeneous solid solution.Among the samples,CeO2-ZrO2-Al2O3(CZA)has the best textural properties and excellent thermal stability.The specific surface area and pore volume of aged CZA are 90 m2/g and 0.29 mL/g.We proposed a viewpoint:Al3+ might insert among the interspace of fluorite structure or highly dispersal in solid solutions.