采用铜模吸铸制备了厚度为0.8 mm,成分为Nd9Fe81-x-yTi4C2BxNby(x=11,13,15;y=0,4)的Nd2Fe14B/Fe3B型纳米复合永磁合金块体样品,研究了添加Nb对合金铸态组织及其晶化行为的影响,并测试了其磁性能。结果表明:在合金中添加4%(原子分数)Nb...采用铜模吸铸制备了厚度为0.8 mm,成分为Nd9Fe81-x-yTi4C2BxNby(x=11,13,15;y=0,4)的Nd2Fe14B/Fe3B型纳米复合永磁合金块体样品,研究了添加Nb对合金铸态组织及其晶化行为的影响,并测试了其磁性能。结果表明:在合金中添加4%(原子分数)Nb元素,不仅能抑制吸铸样品表面Nd2Fe23B3软磁性相、Nd1.1Fe4B4非磁性相和未知相的形成,导致Nd2Fe14B,Fe3B和α-Fe相的相对量增加,而且促使样品内部在非晶基体上形成了少量的Nd2Fe14B和α-Fe,Fe3B纳米晶。添加了Nb的合金吸铸样品表现出一定的硬磁性,其中Nd9Fe66Ti4C2B15Nb4吸铸样品具有最高的矫顽力(Hci=116.66 k A·m-1);添加4%(原子分数)Nb使得合金在晶化过程中由原来的异相同温一步晶化转变为两步晶化,且初始晶化温度Tx均明显降低,两个放热峰的ΔTpx均增大。展开更多
A systematic study of syntheses and magnetic properties of the Nd_3Fe_(29-x)Cr_x (x=4.5, 4.7, 5.0, and 5.5) compounds has been performed. The single-phase compounds of Nd_3Fe_(29-x)Cr_x can be formed in the range 4.5...A systematic study of syntheses and magnetic properties of the Nd_3Fe_(29-x)Cr_x (x=4.5, 4.7, 5.0, and 5.5) compounds has been performed. The single-phase compounds of Nd_3Fe_(29-x)Cr_x can be formed in the range 4.5≤ x ≤ 5.5. The Curie temperature T_C, the saturation magnetization M_s at 4.2 K, the anisotropy field H_A at 4.2 K and room temperature. and the intra-sublattice exchange coupling parameter j_(FeFe) at 4.2 K for the Nd_3Fe_(29-x)Cr_x compounds decrease with increasing Cr composition from x=4.5 to 5.5, respectively. Nitrogenation and carbonation, unlike hydrogenation. result mainly in improvements of the Curie temperature, the saturation magnetization and the anisotropy field at 4.2 K and room temperature for the Nd_3Fe_(29-x)Cr_x compounds compared with their parent compounds.展开更多
The compound effect of Nd2Fe14B/Fe3B-Ferrite bonded magnets was studied.The result shows that the value ofβjHC obviously decreases with the ferrite content increasing.In addition, a functional relation between magnet...The compound effect of Nd2Fe14B/Fe3B-Ferrite bonded magnets was studied.The result shows that the value ofβjHC obviously decreases with the ferrite content increasing.In addition, a functional relation between magnetic properties and ferrite content was clearly revealed by the physical relation in the magnetic powders.展开更多
文摘采用铜模吸铸制备了厚度为0.8 mm,成分为Nd9Fe81-x-yTi4C2BxNby(x=11,13,15;y=0,4)的Nd2Fe14B/Fe3B型纳米复合永磁合金块体样品,研究了添加Nb对合金铸态组织及其晶化行为的影响,并测试了其磁性能。结果表明:在合金中添加4%(原子分数)Nb元素,不仅能抑制吸铸样品表面Nd2Fe23B3软磁性相、Nd1.1Fe4B4非磁性相和未知相的形成,导致Nd2Fe14B,Fe3B和α-Fe相的相对量增加,而且促使样品内部在非晶基体上形成了少量的Nd2Fe14B和α-Fe,Fe3B纳米晶。添加了Nb的合金吸铸样品表现出一定的硬磁性,其中Nd9Fe66Ti4C2B15Nb4吸铸样品具有最高的矫顽力(Hci=116.66 k A·m-1);添加4%(原子分数)Nb使得合金在晶化过程中由原来的异相同温一步晶化转变为两步晶化,且初始晶化温度Tx均明显降低,两个放热峰的ΔTpx均增大。
文摘A systematic study of syntheses and magnetic properties of the Nd_3Fe_(29-x)Cr_x (x=4.5, 4.7, 5.0, and 5.5) compounds has been performed. The single-phase compounds of Nd_3Fe_(29-x)Cr_x can be formed in the range 4.5≤ x ≤ 5.5. The Curie temperature T_C, the saturation magnetization M_s at 4.2 K, the anisotropy field H_A at 4.2 K and room temperature. and the intra-sublattice exchange coupling parameter j_(FeFe) at 4.2 K for the Nd_3Fe_(29-x)Cr_x compounds decrease with increasing Cr composition from x=4.5 to 5.5, respectively. Nitrogenation and carbonation, unlike hydrogenation. result mainly in improvements of the Curie temperature, the saturation magnetization and the anisotropy field at 4.2 K and room temperature for the Nd_3Fe_(29-x)Cr_x compounds compared with their parent compounds.
文摘The compound effect of Nd2Fe14B/Fe3B-Ferrite bonded magnets was studied.The result shows that the value ofβjHC obviously decreases with the ferrite content increasing.In addition, a functional relation between magnetic properties and ferrite content was clearly revealed by the physical relation in the magnetic powders.