The phase transformation behavior and micro structure of Nb-Ru alloys have been studied by DSC, X-ray diffraction, optical microscopy, transmission electron microscopy (TEM) and high-resolution electron microscopy (HR...The phase transformation behavior and micro structure of Nb-Ru alloys have been studied by DSC, X-ray diffraction, optical microscopy, transmission electron microscopy (TEM) and high-resolution electron microscopy (HREM). Two-step phase transformation of CsCl (β) →face-centered tetragonal (β)→ monoclinic (β') occurs during cooling from high temperature to room temperature. The lattice parameters of marten-sites of Nb-Ru alloys were found to increase with the increase of Nb content. The martensite variants exhibit triangular self-accommodating morphology, with alternating regular bands inside. The twinning relationship between the sub structural bands was found to be (101) type I mode, and this kind of twinning interface was straight, well-defined and coherent.展开更多
The microstructure,phase transformation,compression property and strain recovery characteristics of equiatomic Ru-Nb high temperature shape memory alloy were investigated by means of optical microscope,X-ray diffracti...The microstructure,phase transformation,compression property and strain recovery characteristics of equiatomic Ru-Nb high temperature shape memory alloy were investigated by means of optical microscope,X-ray diffraction(XRD),differential scanning calorimetry(DSC),compression tests and transmission electron microscopy(TEM).When cooling the alloy specimen from high temperature to room temperature,β(parent phase)→β’(interphase)→β″(martensite) two step phase transformation occurs.The microstructure at room temperature shows regularly arranged band morphology with the monoclinic crystal structure.The twinning relationship between the martensite bands was determined to be(101) Type I.Reorientation and of the martensite bands inside the variant and dislocation were found during compression at room temperature.The maximum complete recovery strain is about 1.5%.展开更多
基金The authors would like to thank financial support of National Natural Science Foundation of China(Project No.59901004).
文摘The phase transformation behavior and micro structure of Nb-Ru alloys have been studied by DSC, X-ray diffraction, optical microscopy, transmission electron microscopy (TEM) and high-resolution electron microscopy (HREM). Two-step phase transformation of CsCl (β) →face-centered tetragonal (β)→ monoclinic (β') occurs during cooling from high temperature to room temperature. The lattice parameters of marten-sites of Nb-Ru alloys were found to increase with the increase of Nb content. The martensite variants exhibit triangular self-accommodating morphology, with alternating regular bands inside. The twinning relationship between the sub structural bands was found to be (101) type I mode, and this kind of twinning interface was straight, well-defined and coherent.
基金The project is financially supported by the National Natural Science Foundation of China ( No 50531020)
文摘The microstructure,phase transformation,compression property and strain recovery characteristics of equiatomic Ru-Nb high temperature shape memory alloy were investigated by means of optical microscope,X-ray diffraction(XRD),differential scanning calorimetry(DSC),compression tests and transmission electron microscopy(TEM).When cooling the alloy specimen from high temperature to room temperature,β(parent phase)→β’(interphase)→β″(martensite) two step phase transformation occurs.The microstructure at room temperature shows regularly arranged band morphology with the monoclinic crystal structure.The twinning relationship between the martensite bands was determined to be(101) Type I.Reorientation and of the martensite bands inside the variant and dislocation were found during compression at room temperature.The maximum complete recovery strain is about 1.5%.