Dense Nb/Nb5Si3 composites were fabricated via spark plasma sintering technology using Nb, Si, and Al elemental powders as raw materials. The microstructttres of the synthesised composites were analyzed through scanni...Dense Nb/Nb5Si3 composites were fabricated via spark plasma sintering technology using Nb, Si, and Al elemental powders as raw materials. The microstructttres of the synthesised composites were analyzed through scanning electron microscopy, X-ray diffraction, and electron probe microanalysis. The results show that the composites consisted of residual Nb particle phase and Nb5Si3 phase. The microstructure of the Nb/ Nb5Si3 in situ composites was evidently affected by Al addition, which prompted the formation of the Al3Nb10Si3 phase. In addition, the Rockwell hardness of the composites decreased with the increase in AI additions. The Rockwell hardness of Nb-20Si is 60HRC, which decreased to approximately 52.7 HRC when the Al content increased to 15 at%. The oxidation resistance of the Nb/NbsSi3 in situ composites significantly improved with the increase in Al addition.展开更多
The Nb 10Si (mole fraction, %) alloy was fabricated using the vacuum arc melting method and heat treated at 1850?℃ and 1?550?℃ for 2～100?h in Ar atmosphere. The microstructure of the alloy has been investigated usi...The Nb 10Si (mole fraction, %) alloy was fabricated using the vacuum arc melting method and heat treated at 1850?℃ and 1?550?℃ for 2～100?h in Ar atmosphere. The microstructure of the alloy has been investigated using X ray diffractometry(XRD), scanning electron microscopy (SEM) equipped with X ray energy dispersive spectrometry (EDS) and transmission electron microscopy (TEM). The results show that 1?550?℃, 100?h is an optimum heat treatment condition to acquire the equilibrium Nb+Nb 5Si 3 two phase microstructure. The microstructure of Nb 10Si alloy in the as cast condition consists of continuous Nb 3Si matrix and dispersed Nb particles, which implies that the alloy is in the metastable equilibrium state. In the case of 1?850?℃, 2?h heat treatment the Nb particles are coarsened evidently. However, in the heat treatment condition of 1?550?℃ for 25～100?h the growth of Nb particles is unconspicuous. After heat treated at 1?550?℃, Nb 3Si phase transforms into the equilibrium Nb 5Si 3 and Nb phase with the increase of heat treatment time gradually. TEM observations reveal that the interface of Nb phase and Nb 5Si 3 phase is clean and some twins with about 10?nm in width are found.展开更多
基金Funded by National Natural Science Foundation of China(No.51271091)Science Project of Jiangxi Ministry of Education of China(No.GJJ12420)
文摘Dense Nb/Nb5Si3 composites were fabricated via spark plasma sintering technology using Nb, Si, and Al elemental powders as raw materials. The microstructttres of the synthesised composites were analyzed through scanning electron microscopy, X-ray diffraction, and electron probe microanalysis. The results show that the composites consisted of residual Nb particle phase and Nb5Si3 phase. The microstructure of the Nb/ Nb5Si3 in situ composites was evidently affected by Al addition, which prompted the formation of the Al3Nb10Si3 phase. In addition, the Rockwell hardness of the composites decreased with the increase in AI additions. The Rockwell hardness of Nb-20Si is 60HRC, which decreased to approximately 52.7 HRC when the Al content increased to 15 at%. The oxidation resistance of the Nb/NbsSi3 in situ composites significantly improved with the increase in Al addition.
文摘The Nb 10Si (mole fraction, %) alloy was fabricated using the vacuum arc melting method and heat treated at 1850?℃ and 1?550?℃ for 2～100?h in Ar atmosphere. The microstructure of the alloy has been investigated using X ray diffractometry(XRD), scanning electron microscopy (SEM) equipped with X ray energy dispersive spectrometry (EDS) and transmission electron microscopy (TEM). The results show that 1?550?℃, 100?h is an optimum heat treatment condition to acquire the equilibrium Nb+Nb 5Si 3 two phase microstructure. The microstructure of Nb 10Si alloy in the as cast condition consists of continuous Nb 3Si matrix and dispersed Nb particles, which implies that the alloy is in the metastable equilibrium state. In the case of 1?850?℃, 2?h heat treatment the Nb particles are coarsened evidently. However, in the heat treatment condition of 1?550?℃ for 25～100?h the growth of Nb particles is unconspicuous. After heat treated at 1?550?℃, Nb 3Si phase transforms into the equilibrium Nb 5Si 3 and Nb phase with the increase of heat treatment time gradually. TEM observations reveal that the interface of Nb phase and Nb 5Si 3 phase is clean and some twins with about 10?nm in width are found.