Nb/Ta multilayer films deposited on Ti6A14V substrate with Nb and Ta monolayer thicknesses of 30 nm, 120 nm, and 240 nm were irradiated by a high current pulse electron beam （HCPEB） to prepare Nb-Ta alloyed layers. ...Nb/Ta multilayer films deposited on Ti6A14V substrate with Nb and Ta monolayer thicknesses of 30 nm, 120 nm, and 240 nm were irradiated by a high current pulse electron beam （HCPEB） to prepare Nb-Ta alloyed layers. The mi- crostructure and the composition of the outmost surface of melted alloyed layers were investigated using a transmission electron microscope （TEM） equipped with an X-ray energy dispersive spectrometer （EDS） attachment. The Ta content of the alloyed surface layer prepared from the monolayer of thickness 30 nm, 120 nm, and 240 nm was- 27.7 at.%, 6.37 at.%, and 0 at.%, respectively. It was found that the Ta content in the alloyed layer plays a dominant role in the microstructure of the films. The hardness and the wear rate of the alloyed layers decrease with the increasing content of Ta in the surface laver.展开更多
基金Project supported by the National Basic Research Program of China (Grant No. 2013CB632305)the Guangdong Province University-Industry Cooperation Project of the Ministry of Education, China (Grant No. 2010B090400444)+1 种基金the Guangdong International Cooperation Projects, China (Grant No. 2010B050900003)the Guangdong Science and Technology Plan Projects, China (Grant No. 2010A070500002)
文摘Nb/Ta multilayer films deposited on Ti6A14V substrate with Nb and Ta monolayer thicknesses of 30 nm, 120 nm, and 240 nm were irradiated by a high current pulse electron beam （HCPEB） to prepare Nb-Ta alloyed layers. The mi- crostructure and the composition of the outmost surface of melted alloyed layers were investigated using a transmission electron microscope （TEM） equipped with an X-ray energy dispersive spectrometer （EDS） attachment. The Ta content of the alloyed surface layer prepared from the monolayer of thickness 30 nm, 120 nm, and 240 nm was- 27.7 at.%, 6.37 at.%, and 0 at.%, respectively. It was found that the Ta content in the alloyed layer plays a dominant role in the microstructure of the films. The hardness and the wear rate of the alloyed layers decrease with the increasing content of Ta in the surface laver.