纳米 Ti O2 改性不饱和聚酯树脂 ,其目的是对不饱和聚酯进行同时增韧增强改性。用“反应法”制备的纳米 Ti O2 /UPR,在纳米 Ti O2 与 UPR之间产生的新化学键将纳米 Ti O2 粒子接入 UPR长链上 ,这种新的结构决定了纳米 Ti O2 /UPR的性能...纳米 Ti O2 改性不饱和聚酯树脂 ,其目的是对不饱和聚酯进行同时增韧增强改性。用“反应法”制备的纳米 Ti O2 /UPR,在纳米 Ti O2 与 UPR之间产生的新化学键将纳米 Ti O2 粒子接入 UPR长链上 ,这种新的结构决定了纳米 Ti O2 /UPR的性能。研究结果表明 ,纳米 Ti O2 /UPR的反应活性高于 UPR,纳米 Ti O2 /UPR的冲击韧性和弯曲强度较 UPR分别提高 46%和 5 5 % ,纳米 Ti O2 /UPR的耐热性及介电性与展开更多
Ti6Al4V alloy was subjected to hydrothermal treatment in the concentrated Ca3(PO4)2, Ca HPO4 and Ca(H2PO4)2 solutions for bioactive surface modification. The treated samples are covered by films composed of nano-parti...Ti6Al4V alloy was subjected to hydrothermal treatment in the concentrated Ca3(PO4)2, Ca HPO4 and Ca(H2PO4)2 solutions for bioactive surface modification. The treated samples are covered by films composed of nano-particles with the size of 60-240 nm. Such film can also be grown on the strut surface of a Ti6Al4 V scaffold prepared by electron beam melting(EBM) technology. XPS analysis indicates that Ti element on the surface presents as TiO2, and Ca and P elements are in the form of calcium phosphate. XRD and Raman analyses show that the surface layer is composed of anatase TiO2 and hydroxyapatite. Potentiodynamic polarization test in a Ca-free Hank's balanced solution demonstrates that the treated sample has markedly improved corrosion resistance compared with the polished sample. The present work provides a bioactive surface modification method that is easily-operated, low-temperature, less corrosion, and applicable to porous Ti6Al4 V alloy for biomedical applications.展开更多
文摘纳米 Ti O2 改性不饱和聚酯树脂 ,其目的是对不饱和聚酯进行同时增韧增强改性。用“反应法”制备的纳米 Ti O2 /UPR,在纳米 Ti O2 与 UPR之间产生的新化学键将纳米 Ti O2 粒子接入 UPR长链上 ,这种新的结构决定了纳米 Ti O2 /UPR的性能。研究结果表明 ,纳米 Ti O2 /UPR的反应活性高于 UPR,纳米 Ti O2 /UPR的冲击韧性和弯曲强度较 UPR分别提高 46%和 5 5 % ,纳米 Ti O2 /UPR的耐热性及介电性与
基金Projects(xjj2011096,CHD2011JC001)supported by the Fundamental Research Fund for the Central Universities,ChinaProjects(50901058,51374174)supported by the National Natural Science Foundation of ChinaProject(2013JZ015)supported by the Science and Technology Program of Shaanxi Province,China
文摘Ti6Al4V alloy was subjected to hydrothermal treatment in the concentrated Ca3(PO4)2, Ca HPO4 and Ca(H2PO4)2 solutions for bioactive surface modification. The treated samples are covered by films composed of nano-particles with the size of 60-240 nm. Such film can also be grown on the strut surface of a Ti6Al4 V scaffold prepared by electron beam melting(EBM) technology. XPS analysis indicates that Ti element on the surface presents as TiO2, and Ca and P elements are in the form of calcium phosphate. XRD and Raman analyses show that the surface layer is composed of anatase TiO2 and hydroxyapatite. Potentiodynamic polarization test in a Ca-free Hank's balanced solution demonstrates that the treated sample has markedly improved corrosion resistance compared with the polished sample. The present work provides a bioactive surface modification method that is easily-operated, low-temperature, less corrosion, and applicable to porous Ti6Al4 V alloy for biomedical applications.