Na_(2)SiF_(6) was used as surface activating flux for laser welding of TC4 titanium alloy. The effect of Na_(2)SiF_(6) on TC4 titanium alloy laser welding was determined by observing the weld surface. The morphologica...Na_(2)SiF_(6) was used as surface activating flux for laser welding of TC4 titanium alloy. The effect of Na_(2)SiF_(6) on TC4 titanium alloy laser welding was determined by observing the weld surface. The morphological characteristics of the high temperature plasma above the workpiece was observed and analyzed by using high-speed digital camera system. The variation of weld depth,width and microstructure were analyzed by optical microscope. The experimental results show that laser weld of TC4 titanium alloy has good appearance with activating flux of Na_(2)SiF_(6), weld penetration increases by about 0.8%–12%, while weld surface width decrease by about 10%–29%, the depth to width ratio is effectively improved. The inhomogeneity of weld microstructure was improved, and the crystallization direction of β columnar crystals on the upper part of the weld was changed, the grain size and microstructure of the weld were refined by Na_(2)SiF_(6).展开更多
基金National Natural Science Foundation of China (Grant No. 51165027)Inner Mongolia Natural Science Foundationt(2017MS(LH)0512)。
文摘Na_(2)SiF_(6) was used as surface activating flux for laser welding of TC4 titanium alloy. The effect of Na_(2)SiF_(6) on TC4 titanium alloy laser welding was determined by observing the weld surface. The morphological characteristics of the high temperature plasma above the workpiece was observed and analyzed by using high-speed digital camera system. The variation of weld depth,width and microstructure were analyzed by optical microscope. The experimental results show that laser weld of TC4 titanium alloy has good appearance with activating flux of Na_(2)SiF_(6), weld penetration increases by about 0.8%–12%, while weld surface width decrease by about 10%–29%, the depth to width ratio is effectively improved. The inhomogeneity of weld microstructure was improved, and the crystallization direction of β columnar crystals on the upper part of the weld was changed, the grain size and microstructure of the weld were refined by Na_(2)SiF_(6).