A series of Ca10Na(PO4)7:Ce3+/Tb3+/Mn2+(CNPO:Ce3+/Tb3+/Mn2+) phosphors with high brightness were synthesized by high-temperature solid-state method. X-ray diffraction(XRD), scanning electron microscopy(SEM), diffuse r...A series of Ca10Na(PO4)7:Ce3+/Tb3+/Mn2+(CNPO:Ce3+/Tb3+/Mn2+) phosphors with high brightness were synthesized by high-temperature solid-state method. X-ray diffraction(XRD), scanning electron microscopy(SEM), diffuse reflectance spectra(DRS), photo luminescence(PL) spectra, luminescence decay curves and thermally stability were performed to characterize the as-prepared samples. For Ce3+-doped samples, an intense and broad band emission is present under 265 nm excitation. When Ce3+and Tb3+are codoped, energy transfer(ET) process from Ce3+ to Tb3+ is demonstrated with electric dipole-dipole interaction. The internal and external quantum efficiencies(QEs) of CNPO:0.15 Ce3+, 0.04 Tb3+, 0.005 Mn2+are measured to 76.79% and 54.11% under 265 nm excitation and temperature-dependent PL intensity can remain 51.78% at 150 ℃ of its initial intensity at 25 ℃. It is indicated that single-phased white lightemitting CNPO:Ce3+/Tb3+/Mn2+phosphor can serve as a promising phosphor for illumination devices.展开更多
基金supported by National Natural Science Foundation of China(51302182)Natural Science Foundation of Shanxi Province(201601d011030)
文摘A series of Ca10Na(PO4)7:Ce3+/Tb3+/Mn2+(CNPO:Ce3+/Tb3+/Mn2+) phosphors with high brightness were synthesized by high-temperature solid-state method. X-ray diffraction(XRD), scanning electron microscopy(SEM), diffuse reflectance spectra(DRS), photo luminescence(PL) spectra, luminescence decay curves and thermally stability were performed to characterize the as-prepared samples. For Ce3+-doped samples, an intense and broad band emission is present under 265 nm excitation. When Ce3+and Tb3+are codoped, energy transfer(ET) process from Ce3+ to Tb3+ is demonstrated with electric dipole-dipole interaction. The internal and external quantum efficiencies(QEs) of CNPO:0.15 Ce3+, 0.04 Tb3+, 0.005 Mn2+are measured to 76.79% and 54.11% under 265 nm excitation and temperature-dependent PL intensity can remain 51.78% at 150 ℃ of its initial intensity at 25 ℃. It is indicated that single-phased white lightemitting CNPO:Ce3+/Tb3+/Mn2+phosphor can serve as a promising phosphor for illumination devices.