A series of Ce-promoted Mn-Na2WO4/SiO2 catalysts were prepared by incipient wetness impregnation method, and their catalytic performance for oxidative coupling of methane （OCM） was investigated at atmospheric pressu...A series of Ce-promoted Mn-Na2WO4/SiO2 catalysts were prepared by incipient wetness impregnation method, and their catalytic performance for oxidative coupling of methane （OCM） was investigated at atmospheric pressure in a micro-quartz-tube reactor. The catalysts were characterized by X-ray diffraction （XRD）, temperature program reduction （TPR） and BET surface area. Ce promoter increased surface area and Na2WO4 species dispersion, which enriched the amount of the surface species. In addition, Ce promoter increased the Na/W species reduction, but the reduction peak shifted to higher temperature. Stability test of 5wt%Ce catalyst indicated suitable performance and stability. The selectivity and yield of C^2＋ hydrocarbons after 50 h operation reached 65.5% and 19.6%, respectively, at 840 ℃ over 5wt%Ce-2wt%Mn5wt%Na2WO4/SiO2 catalyst.展开更多
The performance of BaC12-TiO2-SnO2 composite catalysts in oxidative coupling of methane reaction has been investigated. A series of BaC12-TiO2, BaC1E-SnO2, TiO2-SnO2, and BaC12-TiO2-SnO2 catalysts were prepared, and c...The performance of BaC12-TiO2-SnO2 composite catalysts in oxidative coupling of methane reaction has been investigated. A series of BaC12-TiO2, BaC1E-SnO2, TiO2-SnO2, and BaC12-TiO2-SnO2 catalysts were prepared, and characterized by BET, XRD, XPS, CO2-TPD and H2-TPR, respectively. The synergistic effect among BaC12, SnO2 and TiO2 compositions enhances the catalytic performance. The best C2 selectivity and ethylene yield are obtained on the catalyst with the equal molar amount of the three compositions （BaC12 ： TiO2 ： SnO2 molar ratio of 1 ： 1 ： 1）. The optimal reaction conditions are as follows： 800 ℃, 44 mL.min-1 for methane, 22 mL.min-1 for oxygen and a space velocity of 5000 mL-h-1 .g-1, and the C2H4 yield over the catalyst is 20.1% with the CH4 conversion of 43.8% and C2 selectivity of 53.3%.展开更多
In this work,the influence of CO2 on the structural variation and catalytic performance of Na2WO4/Mn/Si O2 for oxidative coupling of methane to ethylene was investigated. The catalyst was prepared by impregnation meth...In this work,the influence of CO2 on the structural variation and catalytic performance of Na2WO4/Mn/Si O2 for oxidative coupling of methane to ethylene was investigated. The catalyst was prepared by impregnation method and characterized by XRD,Raman and XPS techniques. Appropriate amount of CO2 in the reactant gases enhanced the formation of surface tetrahedral Na2WO4 species and promoted the migration of O in MOx,Na,W from the catalyst bulk to surface,which were favorable for oxidative coupling of methane. When the molar ratio of CH4/O2/CO2 was 3/1/2,enriched surface tetrahedral Na2WO4 species and high surface concentration of O in MOx,Na,W were detected,and then high CH4 conversion of 33.1% and high C2H4 selectivity of 56.2% were obtained. With further increase of CO2 in the reagent gases,the content of active surface tetrahedral Na2WO4 species and surface concentration of O in MOx,Na,W decreased,while that of inactive species（Mn WO4 and Mn2O3） increased dramatically,leading to low CH4 conversion and low C2H4 selectivity. It could be speculated that Na2WO4 crystal was transformed into Mn WO4 crystal with excessive CO2 added under the reaction conditions. Pretreatment of Na2WO4/Mn/Si O2 catalyst by moderate amount of CO2 before OCM also promoted the formation of Na2WO4 species.展开更多
In order to study the influence of rubidium(Rb)addition on the phase composition,microstructure,mechanical properties and cell response of bioactive glass-ceramics,CaO−SiO2−Na2O−B2O3−MgO−ZnO−P2O5 glass system was desi...In order to study the influence of rubidium(Rb)addition on the phase composition,microstructure,mechanical properties and cell response of bioactive glass-ceramics,CaO−SiO2−Na2O−B2O3−MgO−ZnO−P2O5 glass system was designed with and without addition of Rb.The results show that hydroxyapatite(HA)and Mg−whitelockite(Ca18Mg2H2(PO4)14)crystalline phases are formed in the glass matrix without Rb.After the addition of Rb,only HA phase is detected.The grain size of the crystals in the glass-ceramics is larger with the addition of Rb than that of samples without Rb.Rb addition can improve the bending strength of glass-ceramics.The cultivation of human bone marrow mesenchymal stem cells(hBMSCs)on Rb-containing glass-ceramics demonstrates enhanced cell adhesion,proliferation and ALP activity.In conclusion,Rb-modified glass-ceramics exhibit good mechanical property,excellent bioactivity and biocompatibility,which have potential for bone regeneration application.展开更多
文摘A series of Ce-promoted Mn-Na2WO4/SiO2 catalysts were prepared by incipient wetness impregnation method, and their catalytic performance for oxidative coupling of methane （OCM） was investigated at atmospheric pressure in a micro-quartz-tube reactor. The catalysts were characterized by X-ray diffraction （XRD）, temperature program reduction （TPR） and BET surface area. Ce promoter increased surface area and Na2WO4 species dispersion, which enriched the amount of the surface species. In addition, Ce promoter increased the Na/W species reduction, but the reduction peak shifted to higher temperature. Stability test of 5wt%Ce catalyst indicated suitable performance and stability. The selectivity and yield of C^2＋ hydrocarbons after 50 h operation reached 65.5% and 19.6%, respectively, at 840 ℃ over 5wt%Ce-2wt%Mn5wt%Na2WO4/SiO2 catalyst.
文摘The performance of BaC12-TiO2-SnO2 composite catalysts in oxidative coupling of methane reaction has been investigated. A series of BaC12-TiO2, BaC1E-SnO2, TiO2-SnO2, and BaC12-TiO2-SnO2 catalysts were prepared, and characterized by BET, XRD, XPS, CO2-TPD and H2-TPR, respectively. The synergistic effect among BaC12, SnO2 and TiO2 compositions enhances the catalytic performance. The best C2 selectivity and ethylene yield are obtained on the catalyst with the equal molar amount of the three compositions （BaC12 ： TiO2 ： SnO2 molar ratio of 1 ： 1 ： 1）. The optimal reaction conditions are as follows： 800 ℃, 44 mL.min-1 for methane, 22 mL.min-1 for oxygen and a space velocity of 5000 mL-h-1 .g-1, and the C2H4 yield over the catalyst is 20.1% with the CH4 conversion of 43.8% and C2 selectivity of 53.3%.
基金support from the Ministry of Science and Technology (Nos.2012BAC20B10)the National Natural Science Foundation of China (Nos. 21321061 and 20976109)
文摘In this work,the influence of CO2 on the structural variation and catalytic performance of Na2WO4/Mn/Si O2 for oxidative coupling of methane to ethylene was investigated. The catalyst was prepared by impregnation method and characterized by XRD,Raman and XPS techniques. Appropriate amount of CO2 in the reactant gases enhanced the formation of surface tetrahedral Na2WO4 species and promoted the migration of O in MOx,Na,W from the catalyst bulk to surface,which were favorable for oxidative coupling of methane. When the molar ratio of CH4/O2/CO2 was 3/1/2,enriched surface tetrahedral Na2WO4 species and high surface concentration of O in MOx,Na,W were detected,and then high CH4 conversion of 33.1% and high C2H4 selectivity of 56.2% were obtained. With further increase of CO2 in the reagent gases,the content of active surface tetrahedral Na2WO4 species and surface concentration of O in MOx,Na,W decreased,while that of inactive species（Mn WO4 and Mn2O3） increased dramatically,leading to low CH4 conversion and low C2H4 selectivity. It could be speculated that Na2WO4 crystal was transformed into Mn WO4 crystal with excessive CO2 added under the reaction conditions. Pretreatment of Na2WO4/Mn/Si O2 catalyst by moderate amount of CO2 before OCM also promoted the formation of Na2WO4 species.
基金The authors are grateful for the financial supports from the Natural Science Foundation of Hunan Province,China(2019JJ50797)the Postdoctoral Science Foundation of China(2019T120711).
文摘In order to study the influence of rubidium(Rb)addition on the phase composition,microstructure,mechanical properties and cell response of bioactive glass-ceramics,CaO−SiO2−Na2O−B2O3−MgO−ZnO−P2O5 glass system was designed with and without addition of Rb.The results show that hydroxyapatite(HA)and Mg−whitelockite(Ca18Mg2H2(PO4)14)crystalline phases are formed in the glass matrix without Rb.After the addition of Rb,only HA phase is detected.The grain size of the crystals in the glass-ceramics is larger with the addition of Rb than that of samples without Rb.Rb addition can improve the bending strength of glass-ceramics.The cultivation of human bone marrow mesenchymal stem cells(hBMSCs)on Rb-containing glass-ceramics demonstrates enhanced cell adhesion,proliferation and ALP activity.In conclusion,Rb-modified glass-ceramics exhibit good mechanical property,excellent bioactivity and biocompatibility,which have potential for bone regeneration application.