Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass r...Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.展开更多
Na2O-Al2O3-SiO2 glass-ceramics doped with Er^3＋ ions were synthesized by the conventional melt quenching technique at a low melting temperature.The samples were characterized by differential scanning calorimetry（DSC...Na2O-Al2O3-SiO2 glass-ceramics doped with Er^3＋ ions were synthesized by the conventional melt quenching technique at a low melting temperature.The samples were characterized by differential scanning calorimetry（DSC）,X-ray diffraction（XRD）,scanning electron microscopy（SEM）,UV-vis-NIR scanning spectrophotometry,and fluorescence spectrometry.The results show that the main crystalline phase of glass-ceramics is nepheline.The best heat-treatment process is at 520 ℃ for 2 h.Because the up-conversion luminescence and near infrared luminescence properties of glass doped with Eu^3＋ are studied in detail.展开更多
Nanostructured γ-Fe2O3/SiO2 complex oxide was prepared by sol-gel method with tetraethoxysilane and iron nitrate as precursors. The particle size distribution, thermal and phase stabilities and gas sensing properties...Nanostructured γ-Fe2O3/SiO2 complex oxide was prepared by sol-gel method with tetraethoxysilane and iron nitrate as precursors. The particle size distribution, thermal and phase stabilities and gas sensing properties were systematically characterized by TEM, granularity distribution, TG-DTA, XRD and gas sensitivity measurements. The particle size is about 10 nm and size distribution is very narrow. The sensitivity of the sensing element to CO, H2, C2H4, C6H6 and the effects of calcination temperature on the sensitivity and conductance of gases were examined. The combination of excellent thermal stability and tunable gas sensing properties through careful control of the preparation and judicious selection of material compositions gives rise to novel nanocomposites, which is attractive for the sensitive and selective detection of reducing gases and some hydrocarbon gases.展开更多
基金Project(51204115)supported by the National Natural Science Foundation of ChinaProject(BK20130308)supported by the Basic Research Program of Jiangsu Province,ChinaProject(2014M561710)supported by China Postdoctoral Science Foundation
文摘Surface tension of calcium aluminate refining slag was measured by the Slide method at 1823 K.Based on different levels of the MgO content and the mass ratio of CaO to Al_2O_3,the effects of MgO content and the mass ratio of CaO to Al_2O_3 on surface tension were investigated.The results indicate that surface tension decreased with increasing MgO content(from 0 to 4.86%),followed by an increase with further increasing MgO content up to 11.33%.The trend that surface tension changed with the mass ratio of CaO to Al_2O_3 was the same as the trend that surface tension changed with the MgO content.The surface tension was varied from 0.617 N/m to 0.710 N/m,for the mass ratio of CaO to Al_2O_3 varying between 0.60 and 1.28.An attempt was made to estimate surface tension of CaO-Al_2O_3-MgO slag and its sub-system,and the application showed that the model worked well.
基金Funded by the National High Technology Research and Development Program of China(No.2011AA030204)Key Research Project of Jilin Provincial Science and Technology Department(No.20150204051GX)
文摘Na2O-Al2O3-SiO2 glass-ceramics doped with Er^3＋ ions were synthesized by the conventional melt quenching technique at a low melting temperature.The samples were characterized by differential scanning calorimetry（DSC）,X-ray diffraction（XRD）,scanning electron microscopy（SEM）,UV-vis-NIR scanning spectrophotometry,and fluorescence spectrometry.The results show that the main crystalline phase of glass-ceramics is nepheline.The best heat-treatment process is at 520 ℃ for 2 h.Because the up-conversion luminescence and near infrared luminescence properties of glass doped with Eu^3＋ are studied in detail.
基金Supported by the National Natural Science Foundation of China (No. 20377004) and Beijing Natural Science Foundation (No. 2032014, No. 8032007).
文摘Nanostructured γ-Fe2O3/SiO2 complex oxide was prepared by sol-gel method with tetraethoxysilane and iron nitrate as precursors. The particle size distribution, thermal and phase stabilities and gas sensing properties were systematically characterized by TEM, granularity distribution, TG-DTA, XRD and gas sensitivity measurements. The particle size is about 10 nm and size distribution is very narrow. The sensitivity of the sensing element to CO, H2, C2H4, C6H6 and the effects of calcination temperature on the sensitivity and conductance of gases were examined. The combination of excellent thermal stability and tunable gas sensing properties through careful control of the preparation and judicious selection of material compositions gives rise to novel nanocomposites, which is attractive for the sensitive and selective detection of reducing gases and some hydrocarbon gases.