The leaching kinetics of low grade zinc oxide ore in NH3-NH4Cl-H2O system was studied. The effects of ore particle size, reaction temperature and the sum concentration of ammonium ion and ammonia on the leaching effic...The leaching kinetics of low grade zinc oxide ore in NH3-NH4Cl-H2O system was studied. The effects of ore particle size, reaction temperature and the sum concentration of ammonium ion and ammonia on the leaching efficiency of zinc were examined. The leaching kinetics of low-grade zinc oxide ore in NH3-NH4Cl-H2O system follows the kinetic law of shrinking-core model. The results show that diffusion through the inert particle pores is the leaching kinetics rate controlling step. The calculated apparent activation energy of the process is about 7.057 kJ/mol. The leaching efficiency of zinc is 92.1% under the conditions of ore particle size of 69 μm, holding at 80 ℃ for 60 min, sum ammonia concentration of 7.5 mol/L, the molar ratio of ammonium to ammonia being 2-1, and the ratio (g/mL) of solid to liquid being 1-10.展开更多
The anodic reaction kinetics of zinc electrowinning was investigated on the titanium base RuO2 anode in the system of Zn（Ⅱ）-NH3-NH4Cl-H2O. The effects of stirring speed, ammonium chloride concentration and temperat...The anodic reaction kinetics of zinc electrowinning was investigated on the titanium base RuO2 anode in the system of Zn（Ⅱ）-NH3-NH4Cl-H2O. The effects of stirring speed, ammonium chloride concentration and temperature on anodic reaction rate were studied through the curve measurement of potentiostatic polarization. The results reveal that the electrochemically controlled anodic reaction obeys Tafel equation and the anodic reaction order for ammonium chloride is 1.056, with the apparent activation energy of 40.17 kJ/mol. The general equation of anodic reaction kinetics was obtained.展开更多
基金Project(2007CB613604) supported by the Major State Basic Research Development Program of ChinaProject(50674104) supported by the National Natural Science Foundation of ChinaProject(GJJ08279) supported by the Department of Education of Jiangxi Province
文摘The leaching kinetics of low grade zinc oxide ore in NH3-NH4Cl-H2O system was studied. The effects of ore particle size, reaction temperature and the sum concentration of ammonium ion and ammonia on the leaching efficiency of zinc were examined. The leaching kinetics of low-grade zinc oxide ore in NH3-NH4Cl-H2O system follows the kinetic law of shrinking-core model. The results show that diffusion through the inert particle pores is the leaching kinetics rate controlling step. The calculated apparent activation energy of the process is about 7.057 kJ/mol. The leaching efficiency of zinc is 92.1% under the conditions of ore particle size of 69 μm, holding at 80 ℃ for 60 min, sum ammonia concentration of 7.5 mol/L, the molar ratio of ammonium to ammonia being 2-1, and the ratio (g/mL) of solid to liquid being 1-10.
文摘The anodic reaction kinetics of zinc electrowinning was investigated on the titanium base RuO2 anode in the system of Zn（Ⅱ）-NH3-NH4Cl-H2O. The effects of stirring speed, ammonium chloride concentration and temperature on anodic reaction rate were studied through the curve measurement of potentiostatic polarization. The results reveal that the electrochemically controlled anodic reaction obeys Tafel equation and the anodic reaction order for ammonium chloride is 1.056, with the apparent activation energy of 40.17 kJ/mol. The general equation of anodic reaction kinetics was obtained.
文摘利用NH3-(NH4)2SO4体系,对印刷电路板(printed circuit boards,PCB)生产过程中产生大量的含铜污泥中的铜进行浸析。对PCB污泥中重金属的质量分数进行了测定,其中铜在污泥中的质量分数为33.500%,其余金属质量分数较小。重点探讨了氨-硫酸铵浓度及pH、浸析时间、液固比、温度等条件对浸析率的影响。NH3-(NH4)2SO4体系对PCB污泥中铜浸析的最优条件为氨、硫酸铵浓度分别为3.0mol/L和1.5mol/L,液固比为20mL/g,浸析时间为180min,浸析温度为25℃。在最优条件下进行了浸析应用试验,结果表明铜的浸析率可达到97.5%,此方法的相对标准偏差(relative standard deviation,RSD)为0.63%。