NF3 decomposition in the absence of water over Al2O3, Fe2O3, Co3O4 and NiO, and transition metal oxides （Fe203, CO3O4 and NiO） coated Al2O3 reagents was investigated. The results show that Al2O3 is an active reagent...NF3 decomposition in the absence of water over Al2O3, Fe2O3, Co3O4 and NiO, and transition metal oxides （Fe203, CO3O4 and NiO） coated Al2O3 reagents was investigated. The results show that Al2O3 is an active reagent for NF3 decomposition with 100% conversion lasting for 8.5 h at 400 ℃. Fe203, Co3O4 and NiO coated Al2O3 reagents are superior to bare Al2O3, and 5%Co3O4/Al2O3 has a high reactivity with NF3 full conversion maintaining for 10.5 h. It is suggested that the presence of transition metal oxide is beneficial to the reactivity of Al2O3, and results in a significant enhancement in the fluorination of Al2O3.展开更多
Several Al2O3 samples were prepared by a precipitation method coupled with ultrasonic treatment,and NF3 decomposition without water over Al2O3 reagents is carried out.The effect of preparation parameters of Al2O3 reag...Several Al2O3 samples were prepared by a precipitation method coupled with ultrasonic treatment,and NF3 decomposition without water over Al2O3 reagents is carried out.The effect of preparation parameters of Al2O3 reagents,such as precipitating agents,structure directing agents,and calcining temperatures on their reactivity for NF3 decomposition has been investigated.The results show that NF3 can be decomposed completely at 400-C,and full conversion of NF3 maintains 580 min over the best Al2O3 reagent,calcined at 600-C which was prepared using both PEG-2000 and Tween-60 as structure directing agents,ammonia as a precipitating agent.展开更多
NF3 decomposition over transition metal oxides coated MgO reagents in the absence of water is investigated. The results show that NF3 can be decomposed completely over pure MgO but the time of NF3 steady full conversi...NF3 decomposition over transition metal oxides coated MgO reagents in the absence of water is investigated. The results show that NF3 can be decomposed completely over pure MgO but the time of NF3 steady full conversion kept as short as 80 min, while the reactivities of coated MgO reagents were remarkably enhanced by transition metal oxides, for example the time of NF3 complete conversion over 12%Fe/MgO extended to 380 min. It is suggested that not only an increase in surface area but also a significant enhancement in the fluorination of MgO substrate caused by the surface transition metal oxides result in an improved reactivity of coated MgO reagents for NF3 decomposition.展开更多
基金supported by the National Natural Science Foundation of China (No. 20573089, 20976149)
文摘NF3 decomposition in the absence of water over Al2O3, Fe2O3, Co3O4 and NiO, and transition metal oxides （Fe203, CO3O4 and NiO） coated Al2O3 reagents was investigated. The results show that Al2O3 is an active reagent for NF3 decomposition with 100% conversion lasting for 8.5 h at 400 ℃. Fe203, Co3O4 and NiO coated Al2O3 reagents are superior to bare Al2O3, and 5%Co3O4/Al2O3 has a high reactivity with NF3 full conversion maintaining for 10.5 h. It is suggested that the presence of transition metal oxide is beneficial to the reactivity of Al2O3, and results in a significant enhancement in the fluorination of Al2O3.
基金financially supported by the National Natural Science Foundation of China(No.20976149)
文摘Several Al2O3 samples were prepared by a precipitation method coupled with ultrasonic treatment,and NF3 decomposition without water over Al2O3 reagents is carried out.The effect of preparation parameters of Al2O3 reagents,such as precipitating agents,structure directing agents,and calcining temperatures on their reactivity for NF3 decomposition has been investigated.The results show that NF3 can be decomposed completely at 400-C,and full conversion of NF3 maintains 580 min over the best Al2O3 reagent,calcined at 600-C which was prepared using both PEG-2000 and Tween-60 as structure directing agents,ammonia as a precipitating agent.
基金financially supported by the National Natural Science Foundation of China(No.20976149)
文摘NF3 decomposition over transition metal oxides coated MgO reagents in the absence of water is investigated. The results show that NF3 can be decomposed completely over pure MgO but the time of NF3 steady full conversion kept as short as 80 min, while the reactivities of coated MgO reagents were remarkably enhanced by transition metal oxides, for example the time of NF3 complete conversion over 12%Fe/MgO extended to 380 min. It is suggested that not only an increase in surface area but also a significant enhancement in the fluorination of MgO substrate caused by the surface transition metal oxides result in an improved reactivity of coated MgO reagents for NF3 decomposition.