High-performance pure nickel N6/steel 45#composite plate(N6/45#)was prepared using explosive welding technique.The microstructure of the interface and nearby regions was characterized and analyzed by optical microscop...High-performance pure nickel N6/steel 45#composite plate(N6/45#)was prepared using explosive welding technique.The microstructure of the interface and nearby regions was characterized and analyzed by optical microscope,scanning electron microscope,electron backscatter diffraction,and mechanical property testing,and the microstructural features and mechanical properties of the explosive welding interface were explored.The results show that along the direction of explosive welding,the pure nickel N6/steel 45#composite plate interface gradually evolves from a flat bond to a typical wavy bond.The grains at the crests and troughs exhibit high heterogeneity,and the closer to the interface,the finer the grains.Recrystallization and low-stress deformation bands are formed at the bonding interface.Nanoindentation tests reveal that plastic deformation occurs in the interfacial bonding zone,and the nanohardness values in the crest regions are higher than that in the trough regions.The tensile strength of the N6/45#interface is 599.8 MPa,with an average shear strength of 326.3 MPa.No separation phenomenon is observed between N6 and 45#after the bending test.展开更多
基金Natural Science Foundation of Shanxi Province(202203021221149)Key Research and Development Program of Shanxi Province(202302010101006,202202150401016)+1 种基金Scientific Research Start-up Fund for the Introduction of Talents in Shanxi Institute of Electronic Science and Technology(2023RKJ021)Key R&D Program of Linfen City(2334)。
文摘High-performance pure nickel N6/steel 45#composite plate(N6/45#)was prepared using explosive welding technique.The microstructure of the interface and nearby regions was characterized and analyzed by optical microscope,scanning electron microscope,electron backscatter diffraction,and mechanical property testing,and the microstructural features and mechanical properties of the explosive welding interface were explored.The results show that along the direction of explosive welding,the pure nickel N6/steel 45#composite plate interface gradually evolves from a flat bond to a typical wavy bond.The grains at the crests and troughs exhibit high heterogeneity,and the closer to the interface,the finer the grains.Recrystallization and low-stress deformation bands are formed at the bonding interface.Nanoindentation tests reveal that plastic deformation occurs in the interfacial bonding zone,and the nanohardness values in the crest regions are higher than that in the trough regions.The tensile strength of the N6/45#interface is 599.8 MPa,with an average shear strength of 326.3 MPa.No separation phenomenon is observed between N6 and 45#after the bending test.
基金National Key Research and Development Program(2018YFA0707305)Basic Research Program of Shanxi Province(202203021221149)Major Science and Technology Projects of Shanxi Province(202101120401008)。