Fe-loaded activated carbon(AC)has high surface acidity and more active sites,while manganese-loaded AC has high oxygen content.Coconut husk AC modified by Fe-Mn was studied with the aim of revealing the modification m...Fe-loaded activated carbon(AC)has high surface acidity and more active sites,while manganese-loaded AC has high oxygen content.Coconut husk AC modified by Fe-Mn was studied with the aim of revealing the modification mechanism.First,HNO_(3)AC was prepared using the nitric acid immersion method.Second,Fe-Mn/AC was prepared using the Fe(N0_(3))_(3)and Mn(N0_(3))_(2)sequential immersion.The effects of HNO_(3),Fe(N0_(3))_(3),and Mn(N0_(3))_(2)on the pore texture and surface chemical characteristics of carbon materials were examined by scanning electron microscopy,Brunauer-Emmett-Teller(BET)analysis,X-ray diffraction and Fourier-transform infrared spectroscopy.The surface topography,pore structure,active material,and functional groups of AC,HNO_(3)/AC,and Fe-Mn/AC were systematically studied.The following results were obtained.The surface of HNO_(3)AC has more ditches and air voids;the micropores of HNO_(3)AC are deformed and flattened compared to those of AC.The surface of Fe-Mn/AC exhibits an accumulation phenomenon.MnFe_(2)O_(4)and FeMn_(2)O_(4)formed more pore structures.AC and HNO_(3)AC have numerous micropores.The higher loading quantity of Fe-Mn results in bigger specific surface.The active components of Fe-Mn/AC-1,Fe-Mn/AC-2,Fe-Mn/AC-3,and Fe-Mn/AC-4 are MnFe_(2)O_(4),MnO_(0.43)Fe_(2.57)O_(4),Mn_(3)O_(4),and ot-Fe_(2)O_(3)>respectively.The surface functional groups of AC and HNO_(3)AC are oxygen-containing functional groups.The effect of Fe-Mn modifying conditions on functional group species is rare;however,Fe/AC has more oxygen-containing functional groups.These research findings can aid in the desulfurization and denitrification of the Fe-Mn/AC catalyst.展开更多
基金The authors are grateful for Open Fund of Key Laboratory of Ministry of Education for metallurgical emission reduction and comprehensive utilization of resources(JKF19-08),General Project of Science and Technology Plan of Yunnan Science and Technology Department(2019FB077 and 202001AT070029)the Open Fund of Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education(Grant No.FMRUlab-20-4).
文摘Fe-loaded activated carbon(AC)has high surface acidity and more active sites,while manganese-loaded AC has high oxygen content.Coconut husk AC modified by Fe-Mn was studied with the aim of revealing the modification mechanism.First,HNO_(3)AC was prepared using the nitric acid immersion method.Second,Fe-Mn/AC was prepared using the Fe(N0_(3))_(3)and Mn(N0_(3))_(2)sequential immersion.The effects of HNO_(3),Fe(N0_(3))_(3),and Mn(N0_(3))_(2)on the pore texture and surface chemical characteristics of carbon materials were examined by scanning electron microscopy,Brunauer-Emmett-Teller(BET)analysis,X-ray diffraction and Fourier-transform infrared spectroscopy.The surface topography,pore structure,active material,and functional groups of AC,HNO_(3)/AC,and Fe-Mn/AC were systematically studied.The following results were obtained.The surface of HNO_(3)AC has more ditches and air voids;the micropores of HNO_(3)AC are deformed and flattened compared to those of AC.The surface of Fe-Mn/AC exhibits an accumulation phenomenon.MnFe_(2)O_(4)and FeMn_(2)O_(4)formed more pore structures.AC and HNO_(3)AC have numerous micropores.The higher loading quantity of Fe-Mn results in bigger specific surface.The active components of Fe-Mn/AC-1,Fe-Mn/AC-2,Fe-Mn/AC-3,and Fe-Mn/AC-4 are MnFe_(2)O_(4),MnO_(0.43)Fe_(2.57)O_(4),Mn_(3)O_(4),and ot-Fe_(2)O_(3)>respectively.The surface functional groups of AC and HNO_(3)AC are oxygen-containing functional groups.The effect of Fe-Mn modifying conditions on functional group species is rare;however,Fe/AC has more oxygen-containing functional groups.These research findings can aid in the desulfurization and denitrification of the Fe-Mn/AC catalyst.
