Two-dimensional (2D) ultrathin MoS2-modified black Ti^3+-TiO2 nanotubes were fabricated using an electrospinning-hydrothermal treatment-reduction method.Bare TiO2 nanotubes were fabricated via electrospinning.Then,2D ...Two-dimensional (2D) ultrathin MoS2-modified black Ti^3+-TiO2 nanotubes were fabricated using an electrospinning-hydrothermal treatment-reduction method.Bare TiO2 nanotubes were fabricated via electrospinning.Then,2D MoS2 lamellae were grown on the surface of the nanotubes and Ti^3+/Ov ions were introduced by reduction.The photocatalytic performance of the 2D MoS2/Ti^3+-TiO2 nanotubes was^15 times better than that of TiO2.The HER enhancement of the MoS2/Ti^3+-TiO2 nanotubes can be attributed to the Pt-like behavior of 2D MoS2 and the presence of Ti^3+-ions,which facilitated the quick diffusion of the photogenerated electrons to water,reducing the H2 activation barrier.The presence of Ov ions in the nanotubes and their hollow structure increased their solar utilization.展开更多
TiO2 nanotube precursor was synthesized by the hydrothermal reaction of TiO2 powders with NaOH solution and the properties of the nanotube materials were tuned using different post-treatments. Transmission electron mi...TiO2 nanotube precursor was synthesized by the hydrothermal reaction of TiO2 powders with NaOH solution and the properties of the nanotube materials were tuned using different post-treatments. Transmission electron microscopic （TEM） observation revealed that the nanotube could be obtained by either a direct rinse with acid solution or rinse with distilled water followed by acid solution. The results of X-ray diffraction （XRD） and inductively coupled plasma （ICP） analysis indicated that the nanotube material was composed of H2Ti2O5·H2O. In addition, the photocatalytic activities of the resulting catalysts were found to be strongly dependent on the post-treatment. The results of the photocatalytic reaction showed that the degradation of Acid-red 3B dye fitted pseudo-zero-order kinetics and TiO2 nanotube prepared under direct rinse with acid solution exhibited a higher catalytic efficiency compared to other catalysts.展开更多
In this paper a new solid superacid catalyst SO 2- 4 MoO 3 TiO 2 was prepared.The activity of the catalyst in esterification of acetic acid and iso amyl alcohol was measured and compared with that of SO 2- 4 TiO 2 and...In this paper a new solid superacid catalyst SO 2- 4 MoO 3 TiO 2 was prepared.The activity of the catalyst in esterification of acetic acid and iso amyl alcohol was measured and compared with that of SO 2- 4 TiO 2 and MoO 3 TiO 2.The results showed that SO 2- 4 MoO 3 TiO 2 had better catalytic performance than SO 2- 4 TiO 2 and MoO 3 TiO 2.There was evident coordination between MoO 3 and SO 2- 4 when they coexisted on TiO 2.展开更多
Supported loaded semiconductors （MoO3,ZnO）-TiO2/SiO2 were pre pared by an isovolumetric impregnation method from TiO2/SiO2 pre pared by chemical modification reaction. The chemisorption property and photon a bsorpti...Supported loaded semiconductors （MoO3,ZnO）-TiO2/SiO2 were pre pared by an isovolumetric impregnation method from TiO2/SiO2 pre pared by chemical modification reaction. The chemisorption property and photon a bsorption ability of MoO3-TiO2/SiO2 and ZnO-TiO2/SiO 2 were investigated by BET, UV-Vis DRS, IR and TPD-MS techniques. The gas -phase photocatalytic reaction of CH4 with H2O was performed at 150 ℃ in a fixed-bed annular reactor. The results show that the conversion of met hane and the selectivity of methanol reach to 5.1% and 87.3% respectively over MoO3-TiO2/SiO2, and MoO3-TiO2/SiO2 ex hibits higher photocatalytic acivity than ZnO-TiO2/SiO2.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.51672249,51802282,and 11804301)the Zhejiang Provincial Natural Science Foundation of China(Grant Nos.LQ17F040004 and LY17E020001)Fundamental Research Funds of Zhejiang Sci-Tech University(No.2019Q062)。
文摘Two-dimensional (2D) ultrathin MoS2-modified black Ti^3+-TiO2 nanotubes were fabricated using an electrospinning-hydrothermal treatment-reduction method.Bare TiO2 nanotubes were fabricated via electrospinning.Then,2D MoS2 lamellae were grown on the surface of the nanotubes and Ti^3+/Ov ions were introduced by reduction.The photocatalytic performance of the 2D MoS2/Ti^3+-TiO2 nanotubes was^15 times better than that of TiO2.The HER enhancement of the MoS2/Ti^3+-TiO2 nanotubes can be attributed to the Pt-like behavior of 2D MoS2 and the presence of Ti^3+-ions,which facilitated the quick diffusion of the photogenerated electrons to water,reducing the H2 activation barrier.The presence of Ov ions in the nanotubes and their hollow structure increased their solar utilization.
文摘TiO2 nanotube precursor was synthesized by the hydrothermal reaction of TiO2 powders with NaOH solution and the properties of the nanotube materials were tuned using different post-treatments. Transmission electron microscopic （TEM） observation revealed that the nanotube could be obtained by either a direct rinse with acid solution or rinse with distilled water followed by acid solution. The results of X-ray diffraction （XRD） and inductively coupled plasma （ICP） analysis indicated that the nanotube material was composed of H2Ti2O5·H2O. In addition, the photocatalytic activities of the resulting catalysts were found to be strongly dependent on the post-treatment. The results of the photocatalytic reaction showed that the degradation of Acid-red 3B dye fitted pseudo-zero-order kinetics and TiO2 nanotube prepared under direct rinse with acid solution exhibited a higher catalytic efficiency compared to other catalysts.
文摘In this paper a new solid superacid catalyst SO 2- 4 MoO 3 TiO 2 was prepared.The activity of the catalyst in esterification of acetic acid and iso amyl alcohol was measured and compared with that of SO 2- 4 TiO 2 and MoO 3 TiO 2.The results showed that SO 2- 4 MoO 3 TiO 2 had better catalytic performance than SO 2- 4 TiO 2 and MoO 3 TiO 2.There was evident coordination between MoO 3 and SO 2- 4 when they coexisted on TiO 2.
文摘Supported loaded semiconductors （MoO3,ZnO）-TiO2/SiO2 were pre pared by an isovolumetric impregnation method from TiO2/SiO2 pre pared by chemical modification reaction. The chemisorption property and photon a bsorption ability of MoO3-TiO2/SiO2 and ZnO-TiO2/SiO 2 were investigated by BET, UV-Vis DRS, IR and TPD-MS techniques. The gas -phase photocatalytic reaction of CH4 with H2O was performed at 150 ℃ in a fixed-bed annular reactor. The results show that the conversion of met hane and the selectivity of methanol reach to 5.1% and 87.3% respectively over MoO3-TiO2/SiO2, and MoO3-TiO2/SiO2 ex hibits higher photocatalytic acivity than ZnO-TiO2/SiO2.