Hierarchical mesoporous MoO2/Mo2C/C microspheres,which are composed of primary nanoparticles with a size of about 30 nm,have been designed and synthesized through polymer regulation and subsequent carbonization proces...Hierarchical mesoporous MoO2/Mo2C/C microspheres,which are composed of primary nanoparticles with a size of about 30 nm,have been designed and synthesized through polymer regulation and subsequent carbonization processes.The as-synthesized microspheres were characterized by XRD,Raman,SEM,TEM,XPS measurements and so on.It was found that polyethylene glycol acted as a structure-directing agent,mild reducing agent and carbon source in the formation of these hierarchical mesoporous Mo O2/Mo2C/C microspheres.Moreover,the electrochemical property of the microspheres was also investigated in this work.Evaluated as an anode material for lithium ion batteries,the hierarchical mesoporous Mo O2/Mo2C/C electrode delivered the discharge specific capacities of 665 and 588 m Ah/g after 100 cycles at current densities of 100 and 200 m A/g,respectively.The satisfactory cycling performance and controllable process facilitate the practical applications of the hierarchical mesoporous Mo O2/Mo2C/C as a potential anode material in high-energy density lithium-ion batteries.展开更多
以三聚氰胺苯甲酸盐为碳源和氮源、以三聚氰胺磷钼酸盐为钼源、磷源和氮源,采用程序升温的方法制备了系列N,P掺杂型C@Mo_2C催化剂。采用XRD、SEM、TEM和XPS等对催化剂的结构、形貌和表面特性进行了表征,研究了三聚氰胺苯甲酸盐中n(三聚...以三聚氰胺苯甲酸盐为碳源和氮源、以三聚氰胺磷钼酸盐为钼源、磷源和氮源,采用程序升温的方法制备了系列N,P掺杂型C@Mo_2C催化剂。采用XRD、SEM、TEM和XPS等对催化剂的结构、形貌和表面特性进行了表征,研究了三聚氰胺苯甲酸盐中n(三聚氰胺)/n(苯甲酸)、前驱体中n(C)/n(Mo)等因素对所制备催化剂的结构及其在二氧化碳加氢反应中催化性能的影响。在反应温度为220℃、反应压力为3.0 MPa、空速为3 600 m L/(g·h)的条件下,在N,P掺杂型C@Mo_2C的催化作用下,CO_2转化率可以达到12.2%,此时产物中CH_3OH的选择性达到52.2%。展开更多
Hierarchical hollow structure has demonstrated potential for enhancing electromagnetic(EM)attenuation and improving impedance matching,garnering significant attention for researching.Herein,we have successfully implem...Hierarchical hollow structure has demonstrated potential for enhancing electromagnetic(EM)attenuation and improving impedance matching,garnering significant attention for researching.Herein,we have successfully implemented compositional and structural engineering to fabricate hollow Mo2C/C microspheres with controllable composition by coupling interaction between dopamine hydrochloride and ammonium molybdate.With the synergistic effect of composition and hollow structure,the strongest reflection loss intensity and broadest effective absorption of the optimized sample reach-70.2 dB and 6.2 GHz,respectively.The formation of hollow heterogeneous structures not only favors impedance matching feature,but also generates considerable contribution to EM attenuation capacity.Furthermore,radar cross-section simulation data indicate that hollow Mo2C/C microspheres with compositional optimization and heterogeneous structures have broad prospects for practical applications.展开更多
基金supported by the National Natural Science Foundation of China(No.21376251 and 21406233)the National Basic Research Development Program of China(2013CB632600)
文摘Hierarchical mesoporous MoO2/Mo2C/C microspheres,which are composed of primary nanoparticles with a size of about 30 nm,have been designed and synthesized through polymer regulation and subsequent carbonization processes.The as-synthesized microspheres were characterized by XRD,Raman,SEM,TEM,XPS measurements and so on.It was found that polyethylene glycol acted as a structure-directing agent,mild reducing agent and carbon source in the formation of these hierarchical mesoporous Mo O2/Mo2C/C microspheres.Moreover,the electrochemical property of the microspheres was also investigated in this work.Evaluated as an anode material for lithium ion batteries,the hierarchical mesoporous Mo O2/Mo2C/C electrode delivered the discharge specific capacities of 665 and 588 m Ah/g after 100 cycles at current densities of 100 and 200 m A/g,respectively.The satisfactory cycling performance and controllable process facilitate the practical applications of the hierarchical mesoporous Mo O2/Mo2C/C as a potential anode material in high-energy density lithium-ion batteries.
文摘以三聚氰胺苯甲酸盐为碳源和氮源、以三聚氰胺磷钼酸盐为钼源、磷源和氮源,采用程序升温的方法制备了系列N,P掺杂型C@Mo_2C催化剂。采用XRD、SEM、TEM和XPS等对催化剂的结构、形貌和表面特性进行了表征,研究了三聚氰胺苯甲酸盐中n(三聚氰胺)/n(苯甲酸)、前驱体中n(C)/n(Mo)等因素对所制备催化剂的结构及其在二氧化碳加氢反应中催化性能的影响。在反应温度为220℃、反应压力为3.0 MPa、空速为3 600 m L/(g·h)的条件下,在N,P掺杂型C@Mo_2C的催化作用下,CO_2转化率可以达到12.2%,此时产物中CH_3OH的选择性达到52.2%。
基金supported by the National University of Defense Technology Independent Innovation Science Fund(No.24-ZZCXJDZ-42)the Postdoctoral Fellowship Program of CPSF(No.GZC20241747).
文摘Hierarchical hollow structure has demonstrated potential for enhancing electromagnetic(EM)attenuation and improving impedance matching,garnering significant attention for researching.Herein,we have successfully implemented compositional and structural engineering to fabricate hollow Mo2C/C microspheres with controllable composition by coupling interaction between dopamine hydrochloride and ammonium molybdate.With the synergistic effect of composition and hollow structure,the strongest reflection loss intensity and broadest effective absorption of the optimized sample reach-70.2 dB and 6.2 GHz,respectively.The formation of hollow heterogeneous structures not only favors impedance matching feature,but also generates considerable contribution to EM attenuation capacity.Furthermore,radar cross-section simulation data indicate that hollow Mo2C/C microspheres with compositional optimization and heterogeneous structures have broad prospects for practical applications.