Nano-Y2O3 and nano-CeO2 of different weight ratio mixed with deionizing water were doped into MoO2 powder by liquid-solid doping method. The diameter 1.80 and 0.18 mm alloy wires of Mo-0.3Y, Mo-0.3Ce, and Mo-0.15Y-0.1...Nano-Y2O3 and nano-CeO2 of different weight ratio mixed with deionizing water were doped into MoO2 powder by liquid-solid doping method. The diameter 1.80 and 0.18 mm alloy wires of Mo-0.3Y, Mo-0.3Ce, and Mo-0.15Y-0.15Ce were prepared through reduction, iso- static pressing, sintering, and drawing. Tensile properties, second phase microstructure and fracture surface appear- ance of wires were analyzed. The better refining effect for Mo alloy powder can be gotten after two kinds of nano- particle oxide doped into MoO2 than only one doped. Nano-Y2O3 and nano-CeO2 have different influences on sintering process. For nano-CeO2, the constraining effect of grain growth focuses on the initial sintering stage, nano- Y2O3 plays refining grains roles in the later densification stage. Nano-Y2O3 is undistorted and keeps intact in the process of drawing; and nano-CeO2 is elongated and bro- ken into parts in the drawing direction. The strengthening effect of nano-Y2O3 and nano-CeO2 keeps the finer grains and superior tensile properties for Mo-0.15Y-0.15Ce wire.展开更多
A solid ternary mixture consisting of NaF,silicon and one metal oxide such as La2O3,CeO2,Pr6O11,Nd2O3,and Y2O3 was prepared and usedas de-fluorinated reagent for CF4 decomposition.The results show that 90% conversion ...A solid ternary mixture consisting of NaF,silicon and one metal oxide such as La2O3,CeO2,Pr6O11,Nd2O3,and Y2O3 was prepared and usedas de-fluorinated reagent for CF4 decomposition.The results show that 90% conversion of CF4 can be reached initially over NaF-Si-La2O3,NaF-Si-CeO2,NaF-Si-Nd2O3,and NaF-Si-Y2O3 at 850 C.The fresh and used reagents were characterized using XRD and XPS techniques.It was found that the active components of NaF and metal oxides in NaF-Si-CeO2,NaF-Si-Pr6O11,NaF-Si-Nd2O3,and NaF-Si-Y2O3 weretransformed into inert phases of mixed metal fluorides and silicates,respectively,resulting in an ineffective utilization of these de-fluorinatedreagents,whereas no inert phases from NaF and La2O3 can be observed in the used NaF-Si-La2O3,indicating the NaF-Si-La2O3 reagent couldbe utilized more efficiently than the other reagents in CF4 decomposition.展开更多
基金financially supported by the National Tungsten and Molybdenum Value-added Utilization Tech-nology Industry Development(No.2012BAE06B02)Shanxi Province Science and Technology Innovation Plan(No.2012KTCQ01-08)
文摘Nano-Y2O3 and nano-CeO2 of different weight ratio mixed with deionizing water were doped into MoO2 powder by liquid-solid doping method. The diameter 1.80 and 0.18 mm alloy wires of Mo-0.3Y, Mo-0.3Ce, and Mo-0.15Y-0.15Ce were prepared through reduction, iso- static pressing, sintering, and drawing. Tensile properties, second phase microstructure and fracture surface appear- ance of wires were analyzed. The better refining effect for Mo alloy powder can be gotten after two kinds of nano- particle oxide doped into MoO2 than only one doped. Nano-Y2O3 and nano-CeO2 have different influences on sintering process. For nano-CeO2, the constraining effect of grain growth focuses on the initial sintering stage, nano- Y2O3 plays refining grains roles in the later densification stage. Nano-Y2O3 is undistorted and keeps intact in the process of drawing; and nano-CeO2 is elongated and bro- ken into parts in the drawing direction. The strengthening effect of nano-Y2O3 and nano-CeO2 keeps the finer grains and superior tensile properties for Mo-0.15Y-0.15Ce wire.
基金supported by the National Natural Science Foundation of China (No. 20976149)
文摘A solid ternary mixture consisting of NaF,silicon and one metal oxide such as La2O3,CeO2,Pr6O11,Nd2O3,and Y2O3 was prepared and usedas de-fluorinated reagent for CF4 decomposition.The results show that 90% conversion of CF4 can be reached initially over NaF-Si-La2O3,NaF-Si-CeO2,NaF-Si-Nd2O3,and NaF-Si-Y2O3 at 850 C.The fresh and used reagents were characterized using XRD and XPS techniques.It was found that the active components of NaF and metal oxides in NaF-Si-CeO2,NaF-Si-Pr6O11,NaF-Si-Nd2O3,and NaF-Si-Y2O3 weretransformed into inert phases of mixed metal fluorides and silicates,respectively,resulting in an ineffective utilization of these de-fluorinatedreagents,whereas no inert phases from NaF and La2O3 can be observed in the used NaF-Si-La2O3,indicating the NaF-Si-La2O3 reagent couldbe utilized more efficiently than the other reagents in CF4 decomposition.