Hexagonal MnMX-based(M=Co or Ni,X=Si or Ge)alloys exhibit giant reversible barocaloric effects.However,giant volume expansion would result in the as-cast MnMX ingots fragmenting into powders,and inevitably bring the d...Hexagonal MnMX-based(M=Co or Ni,X=Si or Ge)alloys exhibit giant reversible barocaloric effects.However,giant volume expansion would result in the as-cast MnMX ingots fragmenting into powders,and inevitably bring the deterioration of mechanical properties and formability.Grain fragmentation can bring degradation of structural transformation entropy change during cyclic application and removal of pressure.In this paper,giant reversible barocaloric effects with high thermal cycle stability can be achieved in the epoxy bonded(MnCoGe)0.96(CuCoSn)0.04 composite.Giant reversible isothermal entropy change of 43.0 J·kg^(−1)·K^(−1) and adiabatic temperature change from barocaloric effects(ΔT_(BCE))of 15.6 K can be obtained within a wide temperature span of 30 K at 360 MPa,which is mainly attributed to the integration of the change in the transition temperature driven by pressure of−101 K·GPa^(−1) and suitable thermal hysteresis of 11.1 K.Further,the variation of reversibleΔ_(TBCE) against the applied hydrostatic pressure reaches up to 43 K·GPa^(−1),which is at the highest level among the other reported giant barocaloric compounds.More importantly,after 60 thermal cycles,the composite does not break and the calorimetric curves coincide well,demonstrating good thermal cycle stability.展开更多
磁制冷技术是一种绿色环保,高效节能的制冷技术。固态制冷剂Mn Co Ge合金在相变时的巨大晶格体积变化带来的热效应,使其成为室温磁致冷工质的有力竞争者之一。本文注重对提高Mn Co Ge合金磁性能的方法进行综述,为该合金在实际工业制冷...磁制冷技术是一种绿色环保,高效节能的制冷技术。固态制冷剂Mn Co Ge合金在相变时的巨大晶格体积变化带来的热效应,使其成为室温磁致冷工质的有力竞争者之一。本文注重对提高Mn Co Ge合金磁性能的方法进行综述,为该合金在实际工业制冷应用中提供参考。展开更多
The effects of non-magnetic atom vacancy on structural, martensitic phase transitions and the corresponding magnetocMoric effect in MnCoGel-x alloys are investigated using x-ray diffraction and magnetic measurements. ...The effects of non-magnetic atom vacancy on structural, martensitic phase transitions and the corresponding magnetocMoric effect in MnCoGel-x alloys are investigated using x-ray diffraction and magnetic measurements. The introduction of non-magnetic atom vacancy leads to the decrease of the martensitic transition temperature and realizes a temperature window where magnetic and martensitic phase transitions can be tuned together. Moreover, the giant magnetocaloric effect accompanied with the coupled magnetic-structural transition is ob- tained. It is observed that the peak values of magnetic entropy change of MnCoGeo.97 are about -13.9, -35.1 and -47.4J.kg-1K-1 for △H = 2, 5, 7T, respectively.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.52301248,52271166,52071071,and 52275567)the Foundational Research Project of Shanxi Province,China(Nos.202203021222201 and 202203021212304)+1 种基金PhD Research Startup Foundation of Taiyuan University of Science and Technology(No.20222057)PhD Research Startup Foundation of Shanxi Province,China(No.20232051)。
文摘Hexagonal MnMX-based(M=Co or Ni,X=Si or Ge)alloys exhibit giant reversible barocaloric effects.However,giant volume expansion would result in the as-cast MnMX ingots fragmenting into powders,and inevitably bring the deterioration of mechanical properties and formability.Grain fragmentation can bring degradation of structural transformation entropy change during cyclic application and removal of pressure.In this paper,giant reversible barocaloric effects with high thermal cycle stability can be achieved in the epoxy bonded(MnCoGe)0.96(CuCoSn)0.04 composite.Giant reversible isothermal entropy change of 43.0 J·kg^(−1)·K^(−1) and adiabatic temperature change from barocaloric effects(ΔT_(BCE))of 15.6 K can be obtained within a wide temperature span of 30 K at 360 MPa,which is mainly attributed to the integration of the change in the transition temperature driven by pressure of−101 K·GPa^(−1) and suitable thermal hysteresis of 11.1 K.Further,the variation of reversibleΔ_(TBCE) against the applied hydrostatic pressure reaches up to 43 K·GPa^(−1),which is at the highest level among the other reported giant barocaloric compounds.More importantly,after 60 thermal cycles,the composite does not break and the calorimetric curves coincide well,demonstrating good thermal cycle stability.
基金Supported by the National Natural Science Foundation of China under Grant No 11504222
文摘The effects of non-magnetic atom vacancy on structural, martensitic phase transitions and the corresponding magnetocMoric effect in MnCoGel-x alloys are investigated using x-ray diffraction and magnetic measurements. The introduction of non-magnetic atom vacancy leads to the decrease of the martensitic transition temperature and realizes a temperature window where magnetic and martensitic phase transitions can be tuned together. Moreover, the giant magnetocaloric effect accompanied with the coupled magnetic-structural transition is ob- tained. It is observed that the peak values of magnetic entropy change of MnCoGeo.97 are about -13.9, -35.1 and -47.4J.kg-1K-1 for △H = 2, 5, 7T, respectively.