TiO2 nano powders with Mn concentration of 0 at%-12 at% were synthesized by the sol-gel process, and were annealed at 500 ℃ and 800 ℃ in air for 2 hrs. X-ray diffraction （XRD） measurements indicate that the Mn-TiO...TiO2 nano powders with Mn concentration of 0 at%-12 at% were synthesized by the sol-gel process, and were annealed at 500 ℃ and 800 ℃ in air for 2 hrs. X-ray diffraction （XRD） measurements indicate that the Mn-TiO2 nano powders with Mn concentration of 1 at% and 2 at% annealed at 500 and 800 ℃ are of pure anatase and rutile, respectively. The scanning electron microscope （SEM） observations reveal that the crystal grain size increases with the annealing temperature, and the high resolution transmission electron microscopy （HRTEM） investigations further indicate that the samples are well crystallized, confirming that Mn has doped into the TiO2 crystal lattice effectively. The room temperature ferromagnetism, which could be explained within the scope of the bound magnetic polaron （BMP） theory, is detected in the Mn-TiO2 samples with Mn concentration of 2 at%, and the magnetization of the powders annealed at 500 ℃ is stronger than that of the sample treated at 800 ℃. The UV-VIS diffuse reflectance spectra results demonstrate that the absorption of the TiO2 powders could be enlarged by the enhanced trapped electron absorption caused by Mn doping.展开更多
Electrolytic water splitting,as a promising route to hydrogen(H_(2))production,is still confronted with the sluggish anodic oxygen evolution reaction(OER)and its less value-added O2 production.Herein,we report a bifun...Electrolytic water splitting,as a promising route to hydrogen(H_(2))production,is still confronted with the sluggish anodic oxygen evolution reaction(OER)and its less value-added O2 production.Herein,we report a bifunctional electrode fabricated by in situ growth of Mn-doped CoSe_(2)nanonetworks on carbon fiber cloth(Mn-CoSe_(2)/CFC),which shows attractive electrocatalytic properties toward glycerol oxidation reaction(GOR)in alkali and hydrogen evolution reaction(HER)in acid.A flow alkali/acid hybrid electrolytic cell(fA/A-hEC)was then developed by coupling anodic GOR with cathodic HER with the Mn-CoSe_(2)/CFC bifunctional electrode.Such fA/A-hEC enables a rather low voltage of 0.54 V to achieve 10 mA cm^(-2),and maintain long-term electrolysis stability over 300-h operation at 100 mA cm^(-2)with Faraday efficiencies of over 99%for H_(2)and 90%for formate production.The designed bifunctional electrode in such innovative fA/A-hEC device provides insightful guidance for coupling energy-efficient hydrogen production with biomass upgradation.展开更多
A series of Mn-doped TiO2 nanowires(NWs) were prepared by hydrothermal method at the mole fraction of Mn changing from 0 to 12.0%.X-ray powder diffraction(XRD) analysis shows that all the samples have pure anatase str...A series of Mn-doped TiO2 nanowires(NWs) were prepared by hydrothermal method at the mole fraction of Mn changing from 0 to 12.0%.X-ray powder diffraction(XRD) analysis shows that all the samples have pure anatase structure.SEM and TEM studies show that the diameter and the length of the Mn-doped TiO2 NWs are larger than those of the undoped TiO2 NWs.Energy dispersive X-ray spectroscopy(EDX) reveals that the samples are composed of Ti,Mn and O.According to magnetization measurements,all samples show ferromagnetic behavior,but only the undoped TiO2 NWs are completely ferromagnetic with a saturated magnetization about 1.0 mA·m2/kg.Mn-doped TiO2 samples exhibit antiferromagnetic and ferromagnetic(AF-FM) behaviors simultaneously.Photoluminescence(PL) spectra demonstrate the existence of MnO2 sublattice.These observations indicate that an AF-WF crossover is induced by the coexistence of TiO2 sublattice and MnO2 sublattice.展开更多
Although chemotherapy has been intensively applied in cancer treatments,its inadequate therapeutic efficacy and severe side effects are still under constant concerns.Nanoplatforms used as anti-tumor drug delivery syst...Although chemotherapy has been intensively applied in cancer treatments,its inadequate therapeutic efficacy and severe side effects are still under constant concerns.Nanoplatforms used as anti-tumor drug delivery system(DDS)have attracted tremendous attentions owing to their various intriguing properties.Herein,Mn-doped MoO_(2)nanoparticles coated with ZrO_(2)and capped with Bi_(2)O_(3)have been designed as a DDS,namely MMZB.MMZB possesses good magnetic properties,great photothermal conversion ability,sensitive tumor microenvironment(TME)responsiveness,and good biocompatibility in hemocompatibility in vitro.Thus,MMZB has been utilized to load the chemotherapeutic agent daunomycin(DNM)(MMZB@DNM)for chemo-photothermal combined therapy.MMZB@DNM demonstrates a more impressive anti-cancer effect than the individual photothermal or chemotherapy both in vitro and in vivo.Furthermore,the analysis of tumor specimen sections and serum levels after the treatment indicates negligible side effects for MMZB@DNM in vivo.This contribution provides a valuable concept in designing therapeutic agents for achieving significantly enhanced tumor treatments,which benefits from the synergistic combination of chemotherapy and photothermal therapy in one single nanoagent.展开更多
Synergistic interplays involving multiple active centers originating from TiO2 nanotube layers(TNT)and ruthenium(Ru)species comprising of both single atoms(SAs)and nanoparticles(NPs)augment the alkaline hydrogen evolu...Synergistic interplays involving multiple active centers originating from TiO2 nanotube layers(TNT)and ruthenium(Ru)species comprising of both single atoms(SAs)and nanoparticles(NPs)augment the alkaline hydrogen evolution reaction(HER)by enhancing Volmer kinetics from rapid water dissociation and improving Tafel kinetics from efficient H*desorption.Atomic layer deposition of Ru with 50 process cycles results in a mixture of Ru SAs and 2.8-0.4 nm NPs present on TNT layers,and it emerges with the highest HER activity among all the electrodes synthesized.A detailed study of the Ti and Ru species using different high-resolution techniques confirmed the presence of Ti^(3+)states and the coexistence of Ru SAs and NPs.With insights from literature,the role of Ti^(3+),appropriate work functions of TNT layers and Ru,and the synergistic effect of Ru SAs and Ru NPs in improving the performance of alkaline HER were elaborated and justified.The aforementioned characteristics led to a remarkable performance by having 9mV onset potentials and 33 mV dec^(-1) of Tafel slopes and a higher turnover frequency of 1.72 H2 s^(-1) at 30 mV.Besides,a notable stability from 28 h staircase chronopotentiometric measurements for TNT@Ru surpasses TNT@Pt in comparison.展开更多
We prepared TiO 2(anatase) and Sn doped TiO 2 nanoparticlate film by Plasma enhanced Chemical Vapor Deposition(PECVD) method. XRD and XPS experiments showed that Sn was doped into the lattice of TiO 2 with a ratio of ...We prepared TiO 2(anatase) and Sn doped TiO 2 nanoparticlate film by Plasma enhanced Chemical Vapor Deposition(PECVD) method. XRD and XPS experiments showed that Sn was doped into the lattice of TiO 2 with a ratio of n (Sn)∶ n (Ti)=1∶10 . Sn doping largely enhanced the photocatalytic activity of TiO 2 film for phenol degradation. The enhancement in photoactivity by doping was discussed, based on the characterization with AFM, FTIR and EFISPS. Sn doping produced localized level of Sn 4+ in the band gap of TiO 2, about 0.4 eV below the conduction band, which could capture photogenerated electrons and reduce O 2 adsorbed on the surface of TiO 2 film, thus accelerated the photocatalytic reaction.展开更多
The transition metal ion doped TiO 2 nanoparticles were prepared with hydrothermal method, and the effects of doping different metal ions on the ability of TiO 2 in photocatalyzing degradation of rhodamine B(RB) were ...The transition metal ion doped TiO 2 nanoparticles were prepared with hydrothermal method, and the effects of doping different metal ions on the ability of TiO 2 in photocatalyzing degradation of rhodamine B(RB) were studied. The results showed that the doping of Fe 3+ , Co 2+ , Ni 2+ and Cr 3+ in TiO 2 nanoparticles made the photocatalytic efficiency of the TiO 2 particles reduce and the higher the initial content of Fe 3+ , the lower the ability of TiO 2 in photocatalyzing the degradation of RB. But the doping of Zn 2+ and Cd 2+ , especially Zn 2+ , made the photocatalytic efficiency of the TiO 2 particles enhance, showing a great increase of the rate constant( k ) and the initial reaction rate( r ini ).展开更多
基金Project supported by the Innovation Foundation of BUAA for PhD Graduates (Grant No. 292122)Equipment Research Foundation of China
文摘TiO2 nano powders with Mn concentration of 0 at%-12 at% were synthesized by the sol-gel process, and were annealed at 500 ℃ and 800 ℃ in air for 2 hrs. X-ray diffraction （XRD） measurements indicate that the Mn-TiO2 nano powders with Mn concentration of 1 at% and 2 at% annealed at 500 and 800 ℃ are of pure anatase and rutile, respectively. The scanning electron microscope （SEM） observations reveal that the crystal grain size increases with the annealing temperature, and the high resolution transmission electron microscopy （HRTEM） investigations further indicate that the samples are well crystallized, confirming that Mn has doped into the TiO2 crystal lattice effectively. The room temperature ferromagnetism, which could be explained within the scope of the bound magnetic polaron （BMP） theory, is detected in the Mn-TiO2 samples with Mn concentration of 2 at%, and the magnetization of the powders annealed at 500 ℃ is stronger than that of the sample treated at 800 ℃. The UV-VIS diffuse reflectance spectra results demonstrate that the absorption of the TiO2 powders could be enlarged by the enhanced trapped electron absorption caused by Mn doping.
基金supported by the National Natural Science Foundation of China(Project No.21875253)the CAS Commonwealth Scientific and Industrial Research Organization(CSIRO)Joint Research Projects(121835KYSB20200039)+3 种基金the Scientific Research and Equipment Development Project of CAS(YJKYYQ20190007)Fujian Natural Science Foundation(2021J01210293)the Fujian Science and Technology Pilot Project(Project No.2020H0039)the Joint Fund of the Yulin University and the Dalian National Laboratory for Clean Energy(Grant.YLUDNL Fund 2021011)。
文摘Electrolytic water splitting,as a promising route to hydrogen(H_(2))production,is still confronted with the sluggish anodic oxygen evolution reaction(OER)and its less value-added O2 production.Herein,we report a bifunctional electrode fabricated by in situ growth of Mn-doped CoSe_(2)nanonetworks on carbon fiber cloth(Mn-CoSe_(2)/CFC),which shows attractive electrocatalytic properties toward glycerol oxidation reaction(GOR)in alkali and hydrogen evolution reaction(HER)in acid.A flow alkali/acid hybrid electrolytic cell(fA/A-hEC)was then developed by coupling anodic GOR with cathodic HER with the Mn-CoSe_(2)/CFC bifunctional electrode.Such fA/A-hEC enables a rather low voltage of 0.54 V to achieve 10 mA cm^(-2),and maintain long-term electrolysis stability over 300-h operation at 100 mA cm^(-2)with Faraday efficiencies of over 99%for H_(2)and 90%for formate production.The designed bifunctional electrode in such innovative fA/A-hEC device provides insightful guidance for coupling energy-efficient hydrogen production with biomass upgradation.
基金Project(06JJ2031) supported by Natrual Science Foundation of Hunan Province, ChinaProject(06A065) supported by Education Department of Hunan Province, China
文摘A series of Mn-doped TiO2 nanowires(NWs) were prepared by hydrothermal method at the mole fraction of Mn changing from 0 to 12.0%.X-ray powder diffraction(XRD) analysis shows that all the samples have pure anatase structure.SEM and TEM studies show that the diameter and the length of the Mn-doped TiO2 NWs are larger than those of the undoped TiO2 NWs.Energy dispersive X-ray spectroscopy(EDX) reveals that the samples are composed of Ti,Mn and O.According to magnetization measurements,all samples show ferromagnetic behavior,but only the undoped TiO2 NWs are completely ferromagnetic with a saturated magnetization about 1.0 mA·m2/kg.Mn-doped TiO2 samples exhibit antiferromagnetic and ferromagnetic(AF-FM) behaviors simultaneously.Photoluminescence(PL) spectra demonstrate the existence of MnO2 sublattice.These observations indicate that an AF-WF crossover is induced by the coexistence of TiO2 sublattice and MnO2 sublattice.
基金supported by the National Natural Science Foundation of China(Nos.22271178 and 22001156)Project of Special Key Fields in Guangdong Province(No.2021ZDZX4019)+1 种基金the Science and technology innovation strategy of Guangdong province(No.51361212)Guangdong Provincial Science and Technology Innovation Strategy Special Fund Approval Project(No.pdjh2021b0266)。
文摘Although chemotherapy has been intensively applied in cancer treatments,its inadequate therapeutic efficacy and severe side effects are still under constant concerns.Nanoplatforms used as anti-tumor drug delivery system(DDS)have attracted tremendous attentions owing to their various intriguing properties.Herein,Mn-doped MoO_(2)nanoparticles coated with ZrO_(2)and capped with Bi_(2)O_(3)have been designed as a DDS,namely MMZB.MMZB possesses good magnetic properties,great photothermal conversion ability,sensitive tumor microenvironment(TME)responsiveness,and good biocompatibility in hemocompatibility in vitro.Thus,MMZB has been utilized to load the chemotherapeutic agent daunomycin(DNM)(MMZB@DNM)for chemo-photothermal combined therapy.MMZB@DNM demonstrates a more impressive anti-cancer effect than the individual photothermal or chemotherapy both in vitro and in vivo.Furthermore,the analysis of tumor specimen sections and serum levels after the treatment indicates negligible side effects for MMZB@DNM in vivo.This contribution provides a valuable concept in designing therapeutic agents for achieving significantly enhanced tumor treatments,which benefits from the synergistic combination of chemotherapy and photothermal therapy in one single nanoagent.
基金support from the European Union Horizon 2020 program(project HERMES,nr.952184)the Ministry of Education,Youth and Sports of the Czech Republic for supporting CEMNAT(LM2023037)+1 种基金Czech-NanoLab(LM2023051)infrastructures for providing ALD,SEM,EDX,XPS,TEM,and XRDCzech Science Foundation(project 23-08019X,EXPRO).
文摘Synergistic interplays involving multiple active centers originating from TiO2 nanotube layers(TNT)and ruthenium(Ru)species comprising of both single atoms(SAs)and nanoparticles(NPs)augment the alkaline hydrogen evolution reaction(HER)by enhancing Volmer kinetics from rapid water dissociation and improving Tafel kinetics from efficient H*desorption.Atomic layer deposition of Ru with 50 process cycles results in a mixture of Ru SAs and 2.8-0.4 nm NPs present on TNT layers,and it emerges with the highest HER activity among all the electrodes synthesized.A detailed study of the Ti and Ru species using different high-resolution techniques confirmed the presence of Ti^(3+)states and the coexistence of Ru SAs and NPs.With insights from literature,the role of Ti^(3+),appropriate work functions of TNT layers and Ru,and the synergistic effect of Ru SAs and Ru NPs in improving the performance of alkaline HER were elaborated and justified.The aforementioned characteristics led to a remarkable performance by having 9mV onset potentials and 33 mV dec^(-1) of Tafel slopes and a higher turnover frequency of 1.72 H2 s^(-1) at 30 mV.Besides,a notable stability from 28 h staircase chronopotentiometric measurements for TNT@Ru surpasses TNT@Pt in comparison.
文摘We prepared TiO 2(anatase) and Sn doped TiO 2 nanoparticlate film by Plasma enhanced Chemical Vapor Deposition(PECVD) method. XRD and XPS experiments showed that Sn was doped into the lattice of TiO 2 with a ratio of n (Sn)∶ n (Ti)=1∶10 . Sn doping largely enhanced the photocatalytic activity of TiO 2 film for phenol degradation. The enhancement in photoactivity by doping was discussed, based on the characterization with AFM, FTIR and EFISPS. Sn doping produced localized level of Sn 4+ in the band gap of TiO 2, about 0.4 eV below the conduction band, which could capture photogenerated electrons and reduce O 2 adsorbed on the surface of TiO 2 film, thus accelerated the photocatalytic reaction.
文摘The transition metal ion doped TiO 2 nanoparticles were prepared with hydrothermal method, and the effects of doping different metal ions on the ability of TiO 2 in photocatalyzing degradation of rhodamine B(RB) were studied. The results showed that the doping of Fe 3+ , Co 2+ , Ni 2+ and Cr 3+ in TiO 2 nanoparticles made the photocatalytic efficiency of the TiO 2 particles reduce and the higher the initial content of Fe 3+ , the lower the ability of TiO 2 in photocatalyzing the degradation of RB. But the doping of Zn 2+ and Cd 2+ , especially Zn 2+ , made the photocatalytic efficiency of the TiO 2 particles enhance, showing a great increase of the rate constant( k ) and the initial reaction rate( r ini ).