Abstract： Mn/Ba/Al2O3 catalyst for NO oxidation-storage and Pt/Ba/Al2O3 catalyst mixed with Mn/Ba/Al2O3 for NOx storage-reduction by hydrogen were investigated. The results showed that Mn/Ba/Al2O3 had large nitrogen ...Abstract： Mn/Ba/Al2O3 catalyst for NO oxidation-storage and Pt/Ba/Al2O3 catalyst mixed with Mn/Ba/Al2O3 for NOx storage-reduction by hydrogen were investigated. The results showed that Mn/Ba/Al2O3 had large nitrogen oxides storage capacity （397.9 μmolg^-1） under lean burn condition. When Pt/Ba/Al2O3 catalyst was mixed with Mn/Ba/Al2O3 in equal weight proportion, the NOx conversion increased between 250 ℃ and 500 ℃ under the dynamic lean-rich burn conditions, and the maximum NOx conversion increased from 95.4% to 98.2%. Mn/Ba/Al2O3 has promoted NOx storing in the lean stage and improved NOx reduction efficiency in the rich stage, these might result in higher NOx conversion over the low Pt loading content catalyst.展开更多
The ineluctable introduction of lithium salt to polymer solid-state electrolytes incurs a compromise between strength,ionic conductivity,and thickness.Here,we propose Al_(2)O_(3)-coated polyimide(AO/PI)porous film as ...The ineluctable introduction of lithium salt to polymer solid-state electrolytes incurs a compromise between strength,ionic conductivity,and thickness.Here,we propose Al_(2)O_(3)-coated polyimide(AO/PI)porous film as a high-strength substrate to support fast-ion-conducting polymer-in-salt(PIS)solid-state electrolytes,aiming to suppress lithium dendrite growth and improve full-cell performance.The Al_(2)O_(3)coating layer not only refines the wettability of polyimide porous film to PIS,but also performs as a high modulus protective layer to suppress the growth of lithium dendrites.The resulting PI/AO@PIS exhibits a small thickness of only 35μm with an outstanding tensile strength of 11.3 MPa and Young's modulus of 537.6 MPa.In addition,the PI/AO@PIS delivers a high ionic conductivity of 0.1 m S/cm at 25°C.As a result,the PI/AO@PIS enables symmetric Li cells to achieve exceptional cyclability for over 1000 h at 0.1 m A/cm2without noticeable lithium dendrite formation.Moreover,the PI/AO@PIS-based LiFePO4||Li full cells demonstrate outstanding rate performance(125.7 m Ah/g at 5 C)and impressive cycling stability(96.1%capacity retention at 1 C after 200 cycles).This work highlights the efficacy of enhancing the mechanical properties of polymer matrices and extending cell performance through the incorporation of a dense inorganic interface layer.展开更多
Li-rich layered transitional metal oxide Li1.2(Mn0.54Ni0.16Co0.08)O2 was prepared by sol-gel method and further modified by AlF3 coating via a wet process. The bare and AlF3-coated Li1.2(Mn0.54Ni0.16Co0.08)O2 samples ...Li-rich layered transitional metal oxide Li1.2(Mn0.54Ni0.16Co0.08)O2 was prepared by sol-gel method and further modified by AlF3 coating via a wet process. The bare and AlF3-coated Li1.2(Mn0.54Ni0.16Co0.08)O2 samples were characterized by X-ray diffraction(XRD), scanning electron microscope(SEM), and high resolution transmission electron microscope(HRTEM). XRD results show that the bare and AlF3-coated samples have typical hexagonal α-Na Fe O2 structure, and AlF3-coated layer does not affect the crystal structure of the bare Li1.2(Mn0.54Ni0.16Co0.08)O2. Morphology measurements present that the AlF3 layer with a thickness of 5-7 nm is coated on the surface of the Li1.2(Mn0.54Ni0.16Co0.08)O2 particles.Galvanostatic charge-discharge tests at various rates show that the AlF3-coated Li1.2(Mn0.54Ni0.16Co0.08)O2 has an enhanced electrochemical performance compared with the bare sample. At 1C rate, it delivers an initial discharge capacity of 208.2 m A·h/g and a capacity retention of 72.4% after 50 cycles, while those of the bare Li1.2(Mn0.54Ni0.16Co0.08)O2 are 191.7 m A·h/g and 51.6 %, respectively.展开更多
LiNi1/3Co1/3Mn1/3O2 was coated with uniform nano-sized AlF3 layer by chemical precipitation method to improve its rate capability.The samples were characterized by X-ray diffractometry (XRD),transmission electron micr...LiNi1/3Co1/3Mn1/3O2 was coated with uniform nano-sized AlF3 layer by chemical precipitation method to improve its rate capability.The samples were characterized by X-ray diffractometry (XRD),transmission electron microscopy (TEM),energy dispersive spectroscopy (EDS),charge-discharge cycling,cyclic voltammetry (CV),and electrochemical impedance spectroscopy (EIS).Uniform coated layer with a thickness of about 3 nm was observed on the surface of LiNi1/3Co1/3Mn1/3O2 particle by TEM.At 0.5C and 2C rates,1.5% (mass fraction) AlF3-coated LiNi1/3Co1/3Mn1/3O2/Li in 2.8-4.3 V versus Li/Li+ after 80 cycles showed less than 3% of capacity fading,while those of the bare one were 16.5% and 45.9%,respectively.At 5C rate,the capacity retention of the coated sample after 50 cycles maintained 91.4% of the initial discharge capacity,while that of the bare one decreased to 52.6%.EIS result showed that a little change of charge transfer resistance of the coated sample resulting from uniform thin AlF3 layer was proposed as the main reason why its rate capability was improved obviously.CV result further indicated a greater reversibility for the electrode processes and better electrochemical performance of AlF3-coated layer.展开更多
LiNi1/3Co1/3Mn1/3O2 was synthesized by sol-gel method and effect of calcination temperature on characteristics of LiNi1/3Co1/3Mn1/3O2 cathode was investigated. The structure and characteristics of LiNi1/3Co1/3Mn1/3O2 ...LiNi1/3Co1/3Mn1/3O2 was synthesized by sol-gel method and effect of calcination temperature on characteristics of LiNi1/3Co1/3Mn1/3O2 cathode was investigated. The structure and characteristics of LiNi1/3Co1/3Mn1/3O2 were determined by XRD, SEM and electrochemical measurements. The results show that the compound LiNi1/3Co1/3Mn1/3O2 has layered structure with hexagonal lattice. With the increase of calcination temperature, the basicity of the material decreases, and the size of primary particle rises. The LiNi1/3Co1/3Mn1/3O2 calcined at 900 ℃ for 12 h shows excellent electrochemical performances with large reversible specific capacity of 157.5 mA·h/g in the voltage range of 2.75-4.30 V and good capacity retention of 94.03% after 20 charge/discharge cycles. Capacity of LiNi1/3Co1/3Mn1/3O2 increases with enhancement of charge voltage limit, and specific discharge capacities of 179.4 mA·h/g, 203.1 mA·h/g are observed when the charge voltages limit are fixed at 4.50 V and 4.70 V, respectively.展开更多
A coaxial dielectric barrier discharge (DBD) reactor was used for plasma-catalytic degradation of tetracycline hydrochloride over a series of Mn/γ-Al2O3 catalysts prepared by the incipient wetness impregnation method...A coaxial dielectric barrier discharge (DBD) reactor was used for plasma-catalytic degradation of tetracycline hydrochloride over a series of Mn/γ-Al2O3 catalysts prepared by the incipient wetness impregnation method.The combination of plasma and the Mn/γ-Al2O3 catalysts significantly enhanced the degradation efficiency of tetracycline hydrochloride compared to the plasma process alone,with the 10% Mn/γ-Al2O3 catalyst exhibiting the best tetracycline hydrochloride degradation efficiency.A maximum degradation efficiency of 99.3% can be achieved after 5 min oxidation and a discharge power of 1.3 W,with only 69.7% by a single plasma process.The highest energy yield of the plasma-catalytic process is 91.7 g kWh-1.Probable reaction mechanisms of the plasma-catalytic removal of tetracycline hydrochloride were also proposed.展开更多
To improve the cyclic stability at high temperature and thermal stability, the spherical Al2O3-modified Li（Ni0.5Co0.2Mn0.3）O2 was synthesized by a modified co-precipitation method, and the physical and electrochemic...To improve the cyclic stability at high temperature and thermal stability, the spherical Al2O3-modified Li（Ni0.5Co0.2Mn0.3）O2 was synthesized by a modified co-precipitation method, and the physical and electrochemical properties were studied. The TEM images showed that Li（Ni0.5Co0.2Mn0.3）O2 was modified successfully with nano-Al2O3. The discharge capacity retention of Al2O3-modified Li（Ni0.5Co0.2Mn0.3）O2 maintained about 99% after 200 cycles at high temperature（55 ℃）, while that of the bare one was only 86%. Also, unlike bare Li（Ni0.5Co0.2Mn0.3）O2, the Al2O3-modified material cathode exhibited good thermal stability.展开更多
基金The National Natural Science Foundation of China （No. 20476032）Natural Science Foundation of Guangdong Province （No. 030951） are gratefully acknowledged for financial support for this project.
文摘Abstract： Mn/Ba/Al2O3 catalyst for NO oxidation-storage and Pt/Ba/Al2O3 catalyst mixed with Mn/Ba/Al2O3 for NOx storage-reduction by hydrogen were investigated. The results showed that Mn/Ba/Al2O3 had large nitrogen oxides storage capacity （397.9 μmolg^-1） under lean burn condition. When Pt/Ba/Al2O3 catalyst was mixed with Mn/Ba/Al2O3 in equal weight proportion, the NOx conversion increased between 250 ℃ and 500 ℃ under the dynamic lean-rich burn conditions, and the maximum NOx conversion increased from 95.4% to 98.2%. Mn/Ba/Al2O3 has promoted NOx storing in the lean stage and improved NOx reduction efficiency in the rich stage, these might result in higher NOx conversion over the low Pt loading content catalyst.
基金the financial support from the 261Project of MIIT and Natural Science Foundation of Jiangsu Province(No.BK20240179)。
文摘The ineluctable introduction of lithium salt to polymer solid-state electrolytes incurs a compromise between strength,ionic conductivity,and thickness.Here,we propose Al_(2)O_(3)-coated polyimide(AO/PI)porous film as a high-strength substrate to support fast-ion-conducting polymer-in-salt(PIS)solid-state electrolytes,aiming to suppress lithium dendrite growth and improve full-cell performance.The Al_(2)O_(3)coating layer not only refines the wettability of polyimide porous film to PIS,but also performs as a high modulus protective layer to suppress the growth of lithium dendrites.The resulting PI/AO@PIS exhibits a small thickness of only 35μm with an outstanding tensile strength of 11.3 MPa and Young's modulus of 537.6 MPa.In addition,the PI/AO@PIS delivers a high ionic conductivity of 0.1 m S/cm at 25°C.As a result,the PI/AO@PIS enables symmetric Li cells to achieve exceptional cyclability for over 1000 h at 0.1 m A/cm2without noticeable lithium dendrite formation.Moreover,the PI/AO@PIS-based LiFePO4||Li full cells demonstrate outstanding rate performance(125.7 m Ah/g at 5 C)and impressive cycling stability(96.1%capacity retention at 1 C after 200 cycles).This work highlights the efficacy of enhancing the mechanical properties of polymer matrices and extending cell performance through the incorporation of a dense inorganic interface layer.
基金Project(21071153)supported by the National Natural Science Foundation of China
文摘Li-rich layered transitional metal oxide Li1.2(Mn0.54Ni0.16Co0.08)O2 was prepared by sol-gel method and further modified by AlF3 coating via a wet process. The bare and AlF3-coated Li1.2(Mn0.54Ni0.16Co0.08)O2 samples were characterized by X-ray diffraction(XRD), scanning electron microscope(SEM), and high resolution transmission electron microscope(HRTEM). XRD results show that the bare and AlF3-coated samples have typical hexagonal α-Na Fe O2 structure, and AlF3-coated layer does not affect the crystal structure of the bare Li1.2(Mn0.54Ni0.16Co0.08)O2. Morphology measurements present that the AlF3 layer with a thickness of 5-7 nm is coated on the surface of the Li1.2(Mn0.54Ni0.16Co0.08)O2 particles.Galvanostatic charge-discharge tests at various rates show that the AlF3-coated Li1.2(Mn0.54Ni0.16Co0.08)O2 has an enhanced electrochemical performance compared with the bare sample. At 1C rate, it delivers an initial discharge capacity of 208.2 m A·h/g and a capacity retention of 72.4% after 50 cycles, while those of the bare Li1.2(Mn0.54Ni0.16Co0.08)O2 are 191.7 m A·h/g and 51.6 %, respectively.
基金Project(50542004) supported by the National Natural Science Foundation of ChinaProject(1960-71131100017) supported by Graduate Degree Thesis Innovation Foundation of Central South University,China
文摘LiNi1/3Co1/3Mn1/3O2 was coated with uniform nano-sized AlF3 layer by chemical precipitation method to improve its rate capability.The samples were characterized by X-ray diffractometry (XRD),transmission electron microscopy (TEM),energy dispersive spectroscopy (EDS),charge-discharge cycling,cyclic voltammetry (CV),and electrochemical impedance spectroscopy (EIS).Uniform coated layer with a thickness of about 3 nm was observed on the surface of LiNi1/3Co1/3Mn1/3O2 particle by TEM.At 0.5C and 2C rates,1.5% (mass fraction) AlF3-coated LiNi1/3Co1/3Mn1/3O2/Li in 2.8-4.3 V versus Li/Li+ after 80 cycles showed less than 3% of capacity fading,while those of the bare one were 16.5% and 45.9%,respectively.At 5C rate,the capacity retention of the coated sample after 50 cycles maintained 91.4% of the initial discharge capacity,while that of the bare one decreased to 52.6%.EIS result showed that a little change of charge transfer resistance of the coated sample resulting from uniform thin AlF3 layer was proposed as the main reason why its rate capability was improved obviously.CV result further indicated a greater reversibility for the electrode processes and better electrochemical performance of AlF3-coated layer.
基金Project (2007CB613607) supported by the National Basic Research Program of ChinaProject (2005037698) supported by the Postdoctoral Science Foundation of China
文摘LiNi1/3Co1/3Mn1/3O2 was synthesized by sol-gel method and effect of calcination temperature on characteristics of LiNi1/3Co1/3Mn1/3O2 cathode was investigated. The structure and characteristics of LiNi1/3Co1/3Mn1/3O2 were determined by XRD, SEM and electrochemical measurements. The results show that the compound LiNi1/3Co1/3Mn1/3O2 has layered structure with hexagonal lattice. With the increase of calcination temperature, the basicity of the material decreases, and the size of primary particle rises. The LiNi1/3Co1/3Mn1/3O2 calcined at 900 ℃ for 12 h shows excellent electrochemical performances with large reversible specific capacity of 157.5 mA·h/g in the voltage range of 2.75-4.30 V and good capacity retention of 94.03% after 20 charge/discharge cycles. Capacity of LiNi1/3Co1/3Mn1/3O2 increases with enhancement of charge voltage limit, and specific discharge capacities of 179.4 mA·h/g, 203.1 mA·h/g are observed when the charge voltages limit are fixed at 4.50 V and 4.70 V, respectively.
文摘A coaxial dielectric barrier discharge (DBD) reactor was used for plasma-catalytic degradation of tetracycline hydrochloride over a series of Mn/γ-Al2O3 catalysts prepared by the incipient wetness impregnation method.The combination of plasma and the Mn/γ-Al2O3 catalysts significantly enhanced the degradation efficiency of tetracycline hydrochloride compared to the plasma process alone,with the 10% Mn/γ-Al2O3 catalyst exhibiting the best tetracycline hydrochloride degradation efficiency.A maximum degradation efficiency of 99.3% can be achieved after 5 min oxidation and a discharge power of 1.3 W,with only 69.7% by a single plasma process.The highest energy yield of the plasma-catalytic process is 91.7 g kWh-1.Probable reaction mechanisms of the plasma-catalytic removal of tetracycline hydrochloride were also proposed.
基金Funded by the National High Technology Research and Development Program of China(863 Program)(No.2015AA034600)Province Science and Technology in Anhui(No.1301021011)
文摘To improve the cyclic stability at high temperature and thermal stability, the spherical Al2O3-modified Li（Ni0.5Co0.2Mn0.3）O2 was synthesized by a modified co-precipitation method, and the physical and electrochemical properties were studied. The TEM images showed that Li（Ni0.5Co0.2Mn0.3）O2 was modified successfully with nano-Al2O3. The discharge capacity retention of Al2O3-modified Li（Ni0.5Co0.2Mn0.3）O2 maintained about 99% after 200 cycles at high temperature（55 ℃）, while that of the bare one was only 86%. Also, unlike bare Li（Ni0.5Co0.2Mn0.3）O2, the Al2O3-modified material cathode exhibited good thermal stability.