借助扫描电镜、X- ray及吸氢性能测试装置研究了镁含量对机械合金化制备的 Mm Ni5- x ( Co Al Mn) x/Mg纳米晶复合储氢材料的性能的影响。结果表明 ,随着镁含量的增加 ,合金的活化性能表现出差 -好 -差的变化趋势。当镁含量达到50 wt%...借助扫描电镜、X- ray及吸氢性能测试装置研究了镁含量对机械合金化制备的 Mm Ni5- x ( Co Al Mn) x/Mg纳米晶复合储氢材料的性能的影响。结果表明 ,随着镁含量的增加 ,合金的活化性能表现出差 -好 -差的变化趋势。当镁含量达到50 wt%时 ,材料无法被活化。镁含量对吸氢量也有影响 ,具体表现为 ,随着镁含量的增加 ,材料的吸氢量增加。展开更多
Negative electrodes of the Ni-metal hydride battery were made from hydrogen storage alloy Mm0.9Ti0. 1Ni3. 9Mn0.4Co0.4Al0.3 mod fied by coating with Ni or mixing with Co powder. The cell volume expansion of hexagonal s...Negative electrodes of the Ni-metal hydride battery were made from hydrogen storage alloy Mm0.9Ti0. 1Ni3. 9Mn0.4Co0.4Al0.3 mod fied by coating with Ni or mixing with Co powder. The cell volume expansion of hexagonal structure was about 12 % after coating with 11 % Ni on the alloy Surface,When this alloy was mixed with Co powder. the discharge capacity and the utilization efficiency of the hydrogen storage alloy increased. When the alloy was coated with 11 wt-% Ni and also mixed with 10 wt-% Co powder. the capacity decay for a small sealed cylindrical cell (AA size. 1 Ah) was only about 4 % after 200 cycles展开更多
The degradation of La 0.8 Pr 0.2 Ni 3.55 Co 0.75 Mn 0.4 Al 0.3 alloy electrode during charge discharge cycles was studied with analytical electron microscope (AEM) and scanning electron micro...The degradation of La 0.8 Pr 0.2 Ni 3.55 Co 0.75 Mn 0.4 Al 0.3 alloy electrode during charge discharge cycles was studied with analytical electron microscope (AEM) and scanning electron microscope (SEM). During the cycles, the alloy particles of the negative electrode were pulverized gradually. After 200 cycles, the pulverizing process basically ended and the larger particles were pulverized to below 10 μm. The particles were oxided at the rate of about 0.1 μm/100 times cycles. The oxide layer was porous and consisted of the La(OH) 3 and oxides of Pr, Co and Ni. Most of Pr, Mn and almost all of Al in the oxide layer were dissolved into the electrolyte. The oxidation of the alloy particles was one of the main factors of the decay of the discharge capacity of the negative electrode during the cycles.展开更多
文摘借助扫描电镜、X- ray及吸氢性能测试装置研究了镁含量对机械合金化制备的 Mm Ni5- x ( Co Al Mn) x/Mg纳米晶复合储氢材料的性能的影响。结果表明 ,随着镁含量的增加 ,合金的活化性能表现出差 -好 -差的变化趋势。当镁含量达到50 wt%时 ,材料无法被活化。镁含量对吸氢量也有影响 ,具体表现为 ,随着镁含量的增加 ,材料的吸氢量增加。
文摘Negative electrodes of the Ni-metal hydride battery were made from hydrogen storage alloy Mm0.9Ti0. 1Ni3. 9Mn0.4Co0.4Al0.3 mod fied by coating with Ni or mixing with Co powder. The cell volume expansion of hexagonal structure was about 12 % after coating with 11 % Ni on the alloy Surface,When this alloy was mixed with Co powder. the discharge capacity and the utilization efficiency of the hydrogen storage alloy increased. When the alloy was coated with 11 wt-% Ni and also mixed with 10 wt-% Co powder. the capacity decay for a small sealed cylindrical cell (AA size. 1 Ah) was only about 4 % after 200 cycles
文摘The degradation of La 0.8 Pr 0.2 Ni 3.55 Co 0.75 Mn 0.4 Al 0.3 alloy electrode during charge discharge cycles was studied with analytical electron microscope (AEM) and scanning electron microscope (SEM). During the cycles, the alloy particles of the negative electrode were pulverized gradually. After 200 cycles, the pulverizing process basically ended and the larger particles were pulverized to below 10 μm. The particles were oxided at the rate of about 0.1 μm/100 times cycles. The oxide layer was porous and consisted of the La(OH) 3 and oxides of Pr, Co and Ni. Most of Pr, Mn and almost all of Al in the oxide layer were dissolved into the electrolyte. The oxidation of the alloy particles was one of the main factors of the decay of the discharge capacity of the negative electrode during the cycles.
