Following publication of the original article[1],the authors found that they pasted the same data when drawing XRD for sample NCO-1 and NCO-2 in Fig.2a,however,the XRD of all four samples in the manuscript was tested,...Following publication of the original article[1],the authors found that they pasted the same data when drawing XRD for sample NCO-1 and NCO-2 in Fig.2a,however,the XRD of all four samples in the manuscript was tested,and XRD raw data were kept and can be offered.The correct Fig.2 has been provided in this Correction.展开更多
Cobalt nickel bimetallic oxides(NiCo_(2)O_(4))have received numerous attentions in terms of their controllable morphology,high temperature,corrosion resistance and strong electromagnetic wave(EMW)absorption capability...Cobalt nickel bimetallic oxides(NiCo_(2)O_(4))have received numerous attentions in terms of their controllable morphology,high temperature,corrosion resistance and strong electromagnetic wave(EMW)absorption capability.However,broadening the absorption bandwidth is still a huge challenge for NiCo_(2)O_(4)-based absorbers.Herein,the unique NiCo_(2)O_(4)@C core-shell microcubes with hollow structures were fabricated via a facile sacrificial template strategy.The concentration of oxygen vacancies and morphologies of the three-dimensional(3D)cubic hollow core-shell NiCo_(2)O_(4)@C framework were effectively optimized by adjusting the calcination temperature.The specially designed 3D framework structure facilitated the multiple reflections of incident electromagnetic waves and provided rich interfaces between multiple components,generating significant interfacial polarization losses.Dipole polarizations induced by oxygen vacancies could further enhance the attenuation ability for the incident EM waves.The optimized NiCo_(2)O_(4)@C hollow microcubes exhibit superior EMW absorption capability with minimum RL(RLmin)of-84.45 dB at 8.4 GHz for the thickness of 3.0 mm.Moreover,ultrabroad effective absorption bandwidth(EAB)as large as 12.48 GHz(5.52-18 GHz)is obtained.This work is believed to illuminate the path to synthesis of high-performance cobalt nickel bimetallic oxides for EMW absorbers with excellent EMW absorption capability,especially in broadening effective absorption bandwidth.展开更多
文摘Following publication of the original article[1],the authors found that they pasted the same data when drawing XRD for sample NCO-1 and NCO-2 in Fig.2a,however,the XRD of all four samples in the manuscript was tested,and XRD raw data were kept and can be offered.The correct Fig.2 has been provided in this Correction.
基金This work was supported by Natural Science Foundation of Shandong Province(ZR2022ME089)National Natural Science Foundation of China(52207249)Yantai Basic Research Project(2022JCYJ04).
文摘Cobalt nickel bimetallic oxides(NiCo_(2)O_(4))have received numerous attentions in terms of their controllable morphology,high temperature,corrosion resistance and strong electromagnetic wave(EMW)absorption capability.However,broadening the absorption bandwidth is still a huge challenge for NiCo_(2)O_(4)-based absorbers.Herein,the unique NiCo_(2)O_(4)@C core-shell microcubes with hollow structures were fabricated via a facile sacrificial template strategy.The concentration of oxygen vacancies and morphologies of the three-dimensional(3D)cubic hollow core-shell NiCo_(2)O_(4)@C framework were effectively optimized by adjusting the calcination temperature.The specially designed 3D framework structure facilitated the multiple reflections of incident electromagnetic waves and provided rich interfaces between multiple components,generating significant interfacial polarization losses.Dipole polarizations induced by oxygen vacancies could further enhance the attenuation ability for the incident EM waves.The optimized NiCo_(2)O_(4)@C hollow microcubes exhibit superior EMW absorption capability with minimum RL(RLmin)of-84.45 dB at 8.4 GHz for the thickness of 3.0 mm.Moreover,ultrabroad effective absorption bandwidth(EAB)as large as 12.48 GHz(5.52-18 GHz)is obtained.This work is believed to illuminate the path to synthesis of high-performance cobalt nickel bimetallic oxides for EMW absorbers with excellent EMW absorption capability,especially in broadening effective absorption bandwidth.